North Wood Plastics Polypropylene with 40% Wood Fiber, Extrusion Grade
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Wood Filled |
| Manufacturer | North Wood Plastics |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | North Wood Plastics Polypropylene with 40% Wood Fiber, Extrusion Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by North Wood Plastics, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in³ | ASTM D792 |
| Melt Flow | <= 0.50 g/10 min @Temperature 190 °C |
<= 0.50 g/10 min @Temperature 374 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 27.0 MPa | 3920 psi | ASTM D638 |
| Tensile Strength, Yield | 31.0 MPa | 4500 psi | ASTM D638 |
| Elongation at Break | 6.2 % | 6.2 % | ASTM D638 |
| Tensile Modulus | 3.90 GPa | 566 ksi | ASTM D638 |
| Flexural Yield Strength | 54.0 MPa | 7830 psi | ASTM D790 |
| Flexural Modulus | 3.90 GPa | 566 ksi | ASTM D790 |
| Izod Impact, Notched | 0.250 J/cm | 0.468 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 1.00 J/cm | 1.87 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 50.0 µm/m-°C @Temperature 20.0 °C |
27.8 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | <= 200 °C | <= 392 °F | To prevent fiber degradation. |
Users viewing this material also viewed the following:
- Precision Polymer Engineering E70I Ethylene Propylene Rubber
- NOVA Chemicals Dytherm® 250R Expandable Polystyrene
- Samsung Cheil Industries Starex® HF-0690M ABS, Unreinforced
- A. Schulman COMTUF® 5011 10% Glass Fiber Reinforced Polycarbonate
- Formosa Plastics Formolon® 608 PVC
- CP-Polymer-Technik Wellamid® 6600 GV 10 HWCP 10% Glass Fiber Nylon 66, Heat Stabilized, Dry
- BASF Ultramid® S3K Balance PA 610 (Dry)
- Momentive Performance Materials TSE 2287 Heat Cured Rubber - High Duro Translucent
Copyright © lookpolymers.com All Rights Reserved