Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 128 MPa | 18600 psi | ASTM D638 |
Owens Corning Glass Fiber Reinforced Acetal, 25 wt.% glass Data provided by the manufacturer, Owens Corning. |
|||
Tensile Strength, Ultimate | 128 MPa | 18600 psi | ASTM D638 |
Solvay Specialty Polymers Amodel® A-1115 HS Polyphthalamide (PPA) Resin, 15% Glass Reinforced, Dry As Molded
AMODEL A-1115 HS resin is a 15% glass reinforced, heat stabilized polyphthalamide (PPA) which exhibits a high deflection temperature, high flexural modulus, and high tensile strength. Excellent cre.. |
|||
Tensile Strength, Ultimate | 128 MPa | 18600 psi | |
Haysite 54500 Polyester SMC, 35% Glass Reinforced A high strength fiberglass reinforced thermoset polyester compound formulated for injection, compression, or transfer molding. This material exhibits excellent electrical and mechanical properties, .. |
|||
Tensile Strength, Ultimate | 128 MPa | 18600 psi | ASMT D638 |
Toyobo TS101 PPS, Glass Fiber/Mineral Reinforced Key Feature: High dimensional stabilityHigh performance injection-molding resin created from crystalline polyphenylene sulfide, using a special formulation technology developed by Toyobo. Excellent.. |
|||
Tensile Strength, Ultimate | 128 MPa | 18600 psi | 5 mm/min |
Arkema Group Rilsan® ASR 20 Nylon 12, 20% Carbon Fiber Filled (Conditioned) Designation ISO 1874-PA12,M,16-090,CF20Rigid grade with carbon fiber filler (20%) for injection molding. Available color: black. High strength-to-weight ratio. Very low shrinkage: include 0,5% on av.. |
|||
Tensile Strength, Ultimate | 128 MPa | 18600 psi | ASTM D638 |
Chem Polymer Chemlon 225-15 MG Nylon 6, 25% Mineral/15% Glass Fiber Reinforced A 25% mineral reinforced, 15% glass fiber reinforced nylon 6 offering excellent rigidity, dimensional stability and warpage control in large area parts.Data provided by the manufacturer, Chem Polyme.. |
|||
Tensile Strength, Ultimate | 128 MPa | 18600 psi | ASTM D638 |
A. Schulman ComAlloy Hiloy® 612 Nylon 6, Glass Reinforced, UL Data provided by the manufacturer, ComAlloy International Company.20% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 128 MPa | 18600 psi | ASTM D638 |
A. Schulman ComAlloy Hiloy® 757 Carbon Fiber Reinforced, Flow Enhanced, PPS Alloy Data provided by the manufacturer, ComAlloy International Company.30% Carbon Fiber Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 128 MPa | 18600 psi | ASTM D638 |
A. Schulman ComAlloy Lubrilon® 610 Nylon 6, Carbon Fiber/PTFE Reinforced Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulma.. |
|||
Tensile Strength, Ultimate | 128 MPa @Temperature 60.0 °C |
18600 psi @Temperature 140 °F |
ISO 527 |
LATI LARTON G/40 40% Glass Fiber Filled Polyphenylene sulfide (PPS)
(Unverified Data**) Description: Larton thermoplastics are polyphenylene sulfide (PPS) products. They are distinguished by a group of very interesting properties combined with easy moldability. Larton parts feature: ex.. |