Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 115 MPa | 16700 psi | ISO value at 5mm/min. |
BASF Capron® HPN 9233G 33% Glass-Filled Nylon 6 (Conditioned)
(discontinued **) Capron HPN 9233G is a 33% glass reinforced polyamide 6 injection molding compound combining exceptional strength, stiffness and high temperature performance with excellent surface aesthetics. It is.. |
|||
Tensile Strength, Ultimate | 115 - 385 MPa | 16700 - 55800 psi | Average value: 232 MPa Grade Count:51 |
Overview of materials for Polyphthalamide (PPA), Carbon Fiber This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, Carbon Fiber". Each property range of values reported is minimum and maximum values of .. |
|||
Tensile Strength, Ultimate | 115 - 115 MPa @Temperature 125 - 125 °C |
16700 - 16700 psi @Temperature 257 - 257 °F |
Average value: 115 MPa Grade Count:1 |
Overview of materials for Polyetheretherketone, PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetheretherketone, PTFE Filled". Each property range of values reported is minimum and maximum values.. |
|||
Tensile Strength, Ultimate | 115 MPa | 16700 psi | ISO 527 |
LATI LAPEX A G/20 20% Glass Fiber Reinforced Polyethersulfone (PES) (UL94 V-0)
(Unverified Data**) Description: Lapex A compounds are polyethersulfone (PES) products. They are high temperature compounds offering an interesting combination of properties. Lapex A provides outstanding thermal resist.. |
|||
Tensile Strength, Ultimate | 115 - 180 MPa @Temperature 70.0 - 175 °C |
16700 - 26100 psi @Temperature 158 - 347 °F |
Average value: 139 MPa Grade Count:4 |
Overview of materials for Nylon 6, 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 50% Glass Fiber Filled". Specific grades with glass content between 45% and 54% are included. E.. |
|||
Tensile Strength, Ultimate | 115 MPa | 16700 psi | ASTM D638 |
Chevron Phillips Ryton® R10-110BL Polyphenylene Sulfide Compound
(discontinued **) Black Polyphenylene Sulfide CompoundRyton® R10-110BL is a glass and mineral filled polyphenylene sulfide compound which provides a good combination of mechanical and electrical properties.Applicati.. |
|||
Tensile Strength, Ultimate | 115 MPa @Temperature 980 °C |
16700 psi @Temperature 1800 °F |
|
Haynes 214® alloy, hot rolled solution annealed plate 12.7 mm (1/2 in.) thick Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Tensile Strength, Ultimate | 115 MPa | 16700 psi | ASTM D638 |
Tipco Tipcolite® VASW 200 Phenolic Compound, Long Glass Fiber, in fluffy form, Medium -Soft Flow & Very High Strength |
|||
Tensile Strength, Ultimate | 115 MPa | 16700 psi | ISO 527-93 |
Wellman Wellpet® MRGF102-BK1 PET, 35% Mineral/Glass Fiber Reinforced Typical data obtained from injection molded test bars, tested dry as molded at 73°F (23°C). Information provided by Wellman, Inc. Engineering Resins Division. |
|||
Tensile Strength, Ultimate | 115 MPa | 16700 psi | ISO 527-1/-2 |
DSM Arnite® B427 SE/R PBT-GF35 FR(17) 35% Glass Reinforced, Flame Retardant |
|||
Tensile Strength, Ultimate | 115 MPa | 16700 psi | cond; ISO 527-1/-2 |
DSM EcoPaXX® Q-KG6 PA410-GF30 % Glass Reinforced, Heat Stabilized, for E&E applications |
|||
Tensile Strength, Ultimate | 115 MPa | 16700 psi | cond; ISO 527-1/-2 |
DSM Stanyl® 46HF4530 PA46-GF30 30% Glass Reinforced, Heat Stabilized, High Flow, for E&E applications |
|||
Tensile Strength, Ultimate | 115 MPa @Temperature 160 °C |
16700 psi @Temperature 320 °F |
ISO 527-1/-2 |
DSM Stanyl® TE200F8 PA46-GF40 40% Glass Reinforced, Heat Stabilized, for E&E applications |
|||
Tensile Strength, Ultimate | 115 MPa | 16700 psi | dry; ISO 527-1/-2 |
DSM Stanyl® TQ261F2 PA46-GF10 10% Glass Reinforced, Heat Stabilized |
|||
Tensile Strength, Ultimate | 115 MPa @Temperature 160 °C |
16700 psi @Temperature 320 °F |
ISO 527-1/-2 |
DSM Stanyl® TW271B6 (PA46+PTFE)-CF30 30% Carbon Reinforced, Heat Stabilized, Wear and Friction Modified |
|||
Tensile Strength, Ultimate | 115 MPa | 16700 psi | cond; ISO 527-1/-2 |
DSM EcoPaXX® Q-HG6 PA410-GF30 30% Glass Reinforced, Heat Stabilized |
|||
Tensile Strength, Ultimate | 115 MPa | 16700 psi | 5 mm/min |
Arkema Group Rilsan® BZM 30 TL Nylon 11, 30% Glass Fiber Filled (Dry) Designation ISO 1874-PA11,MHL,18-050,GF30Rigid grade with glass fiber (30%) filler for injection molding. Available colors: black and natural. Light and heat stabilized.Rigidity. High compressive st.. |
|||
Tensile Strength, Ultimate | 115 MPa | 16700 psi | 5mm/min; ISO 527 |
BASF Ultramid® 8267G HS BK-106 15/25% Glass/Mineral Filled PA6 (Dry) Ultramid 8267G HS BK-106 is a heat stabilized, weather resistant, 40% mineral and glass fiber reinforced PA6 injection molding compound with improved UV resistance and sink mark resistance. The com.. |
|||
Tensile Strength, Ultimate | 115 MPa | 16700 psi | 5 mm/min |
Arkema Group Rilsan® AZM 30 O TLD Nylon 12, 30% Glass Fiber Filled (Conditioned) Designation ISO 1874-PA12,MHLR,16-050,GF30Rigid grade with glass fiber (30%) for injection molding. Available color: natural. Light and heat stabilizing agent. Mold-release agent.High rigidity. High.. |
|||
Tensile Strength, Ultimate | 115 MPa | 16700 psi | 5mm/min; ISO 527 |
BASF Ultradur B 4300 G4 LS High Speed BK15045 20% Glass Filled PBT |
|||
Tensile Strength, Ultimate | 115 - 115 MPa @Temperature -40.0 - -40.0 °C |
16700 - 16700 psi @Temperature -40.0 - -40.0 °F |
Average value: 115 MPa Grade Count:1 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend, Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend, Glass Reinforced". Each property range of values repo.. |
|||
Tensile Strength, Ultimate | 115 MPa | 16700 psi | ASTM data at 5 mm/min. |
BASF Capron® GR30 20% Glass-Filled Nylon 6 (Conditioned)
(discontinued **) Capron GR30 is a 30% glass reinforced polyamide 6 injection molding compound. IT is also available in heat stabilized (Capron GR30 HS) and/or pigmented versions. The glass fiber reinforcement enhanc.. |
|||
Tensile Strength, Ultimate | 115 MPa | 16700 psi | ASTM data at 5 mm/min. |
BASF Capron® GR30 HS 30% Glass-Filled Nylon 6 (Conditioned)
(discontinued **) Capron GR30 HS is a heat stabilized 30% glass reinforced polyamide 6 injection molding compound possessing a balance of engineering properties combined with excellent processability and surface aest.. |
|||
Tensile Strength, Ultimate | 115 MPa | 16700 psi | ISO 527 |
LATI LAESTRA G/40-V0CT1 40% Glass Fiber Reinforced, Elastomer Modified, Flame Retardant Syndiotactic Polystyrene (SPS) Description: Laestra compounds are syndiotactic polystyrene (SPS) products. SPS is a polymer offering a combination of properties unavailable with other materials. It exhibits a melting point of 270.. |
|||
Tensile Strength, Ultimate | 115 MPa @Temperature 90.0 °C |
16700 psi @Temperature 194 °F |
ISO 527 |
LATI LARTON G/30 30% Glass Fiber Filled Polyphenylene sulfide (PPS)
(discontinued **) Description: Larton thermoplastics are polyphenylene sulfide (PPS) products. They are distinguished by a group of very interesting properties combined with easy moldability. Larton parts feature: ex.. |
|||
Tensile Strength, Ultimate | 115 MPa | 16700 psi | 5mm/min; ISO 527 |
BASF Petra® 230 BK-112 22/13% Glass/Mineral Filled PET Petra 230 BK-112 is a 35% mineral and glass fiber reinforced, black pigmented, polyethylene terephthalate injection molding compound. It exhibits a very good combination of performance properties in.. |
|||
Tensile Strength, Ultimate | 115 MPa | 16700 psi | cond; ISO 527-1/-2 |
DSM Stanyl® TS200F6 PA46-GF30 30% Glass Reinforced |