Polymer Property : Tensile Strength, Ultimate = 1310 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	9.00 MPa	1310 psi	ASTM D412
Multibase Multi-Flex® TPE A 9103 BLK Multi-Flex TPE contains Kraton™ G.Data provided by Multibase.
Tensile Strength, Ultimate	9.00 MPa	1310 psi	ASTM D638
Multibase Multi-Flex® TPE G 7821 Multi-Flex® high heat compounds are a new generations elastomers exhibiting improved compression set at elevated temperature. Multi-Flex® TPE compounds are based on Kraton G technology and featur..
Tensile Strength, Ultimate	9.00 MPa	1310 psi	ASTM D638-95
Multibase Multi-Flex® TPO D-6509 Multi-Flex® A-6509 thermoplastic elastomer blend is designed to provide processors with cost effective compounds with excellent tear strength, tensile strength and high elongation. Multi-Flex® A-..
Tensile Strength, Ultimate	9.00 MPa	1310 psi
Reliance Industries METABOLIX PHO Information provided by Reliance Industries
Tensile Strength, Ultimate	9.00 MPa	1310 psi	500 mm/min (20 in./min.); ASTM D638, Type IV Specimen
Eastman 1390P Polyethylene (discontinued **) Low-density polyethylene 1390P is used primarily in extrusion-coating applications that require fast line speeds and relatively low coating weights. When compared with other low-density polyethylen..
Tensile Strength, Ultimate	9.00 MPa	1310 psi	500 mm/min (20 in./min.); ASTM D638, Type IV Specimen
Eastman 811E Polyethylene (discontinued **) Extrusion grade; no additives. 811E as supplied by Eastman Chemical may lawfully be used in food contact (noncooking) subject to FDA 21 CFR 177.1520(c)(2.1).Information from manufacturer data sheet..
Tensile Strength, Ultimate	9.00 MPa	1310 psi	500 mm/min (20 in./min.); Type IV Specimen; ASTM D638
Eastman 811P Polyethylene (discontinued **) Injection grade. With its high melt index, the material flows well in molding machines and fills large molds with ease. It is used for molding housewares and other items where a flexible, easy mol..
Tensile Strength, Ultimate	9.00 MPa	1310 psi	ASTM D638
ExxonMobil Escorene® LD-402 LDPE Electrical Jacketing Resin (discontinued **) Data provided by the manufacturer, Exxon Chemical.A low density polyethylene homopolymer resin designed for high speed extrusions.
Tensile Strength, Ultimate	9.00 - 161.337 MPa @Temperature -40.0 - 120 °C	1310 - 23400.0 psi @Temperature -40.0 - 248 °F	Average value: 69.4 MPa Grade Count:3
Overview of materials for High Density Polyethylene (HDPE), Glass fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Glass fiber Filled". Each property range of values reported is minimum..
Tensile Strength, Ultimate	9.00 MPa	1310 psi	ASTM D412
DuPont Performance Polymers Kalrez® 1058 FFKM Perfluoroelastomer (discontinued **) A carbon black-filled compound that has been plasticized with perfluorinated oil. It is the softest, lowest modulus compound in the Kalrez line. Generally it is similar in resistance to Compound 1..
Tensile Strength, Ultimate	9.00 MPa @Temperature 49.0 °C	1310 psi @Temperature 120 °F	Type IV, crosshead speed 2 in/min; ASTM D638
DuPont Elvax® 750 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with..
Tensile Strength, Ultimate	9.00 - 18.0 MPa	1310 - 2610 psi
ATG s.r.l. EACM Ethylene-Acrylic Rubber
Tensile Strength, Ultimate	9.03 MPa	1310 psi	ASTM D412; ISO 37
Advanced Polymer Alloys Alcryn® 4670 BK Melt Processable Rubber Alcryn melt-processable rubber (MPR) is a true rubber, based on a partially cross-linked, chlorinated olefin interpolymer alloy. Alcryn is designed for the manufacture of rubber parts with high prod..
Tensile Strength, Ultimate	9.03 MPa	1310 psi	silicone property; ASTM D412
Arlon 49283R040 Silicone Rubber/Fiberglass Laminate Interleave: 3 mil polyethylene; Side 1: cured silicone rubber; Substrate: 1681 Fiberglass; Side 2: cured silicone rubber
Tensile Strength, Ultimate	9.00 MPa	1310 psi	ASTM D638
Huntsman PE2035 Injection Molding Polyethylene (discontinued **) Homopolymer and FDA compliant.Features: Medium flow resin with good stiffness.Applications: Injection molding: color concentrates.FDA Notes: Conforms to FDA regulation 21 CFR 177.1520 (c)2.2 under c..
Tensile Strength, Ultimate	9.00 MPa	1310 psi	ASTM D638
Huntsman PE2051 Injection Molding Polyethylene (discontinued **) Homopolymer and FDA compliant.Features: Very good molding processability, produces parts with good stiffness, and shows excellent flatness in large projected areas. Also recommended for multi-cavit..
Tensile Strength, Ultimate	9.00 MPa	1310 psi	ASTM D638
Huntsman PE2060 Injection Molding Polyethylene (discontinued **) Homopolymer and FDA compliant.Features: High flow characteristics, good processability.Applications: Injection molding: general purpose molding, large moldings including housewares and toys.FDA Note..
Tensile Strength, Ultimate	9.00 MPa	1310 psi	ASTM D638
Huntsman PE2072 Injection Molding Polyethylene (discontinued **) Homopolymer and FDA compliant.Features: Very high flow rapid set-up characteristics, excellent clarity, gloss, and stiffness.Applications: Injection molding: lids and difficult to fill applications...
Tensile Strength, Ultimate	9.00 MPa	1310 psi	ASTM D638
Huntsman PE2075 Injection Molding Polyethylene (discontinued **) Homopolymer and FDA compliant.Features: Very high flow rapid set-up characteristics, excellent clarity, and gloss.Applications: Injection molding: lids and difficult to fill applications.FDA Notes: ..
Tensile Strength, Ultimate	9.00 - 18.0 MPa	1310 - 2610 psi	Average value: 11.4 MPa Grade Count:28
Overview of materials for Low Density Polyethylene (LDPE), Extrusion Grade This property data is a summary of similar materials in the MatWeb database for the category "Low Density Polyethylene (LDPE), Extrusion Grade". Each property range of values reported is minimum and..
Tensile Strength, Ultimate	9.00 - 15.0 MPa	1310 - 2180 psi	Average value: 12.3 MPa Grade Count:3
Overview of materials for Very Low Density Polyethylene (VLDPE) This property data is a summary of similar materials in the MatWeb database for the category "Very Low Density Polyethylene (VLDPE)". Each property range of values reported is minimum and maximum va..
Tensile Strength, Ultimate	9.00 - 62.0 MPa	1310 - 8990 psi	Average value: 41.4 MPa Grade Count:56
Overview of materials for Polyether Block Amide (PEBA) This property data is a summary of similar materials in the MatWeb database for the category "Polyether Block Amide (PEBA)". Each property range of values reported is minimum and maximum values of a..
Tensile Strength, Ultimate	9.00 - 50.9 MPa	1310 - 7380 psi	Average value: 34.0 MPa Grade Count:3
Overview of materials for ABS/PVC Alloy This property data is a summary of similar materials in the MatWeb database for the category "ABS/PVC Alloy". Each property range of values reported is minimum and maximum values of appropriate MatW..
Tensile Strength, Ultimate	9.00 MPa	1310 psi	Type IV, crosshead speed 2 in/min; ASTM D638
DuPont Elvax® 250 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with..
Tensile Strength, Ultimate	9.00 - 60.0 MPa @Temperature 60.0 - 120 °C	1310 - 8700 psi @Temperature 140 - 248 °F	Average value: 36.3 MPa Grade Count:4
Overview of materials for Polypropylene with 20% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 20% Glass Fiber Filler". Specific grades with glass content between 15% and 24% are i..
Tensile Strength, Ultimate	9.00 - 80.0 MPa @Temperature 60.0 - 120 °C	1310 - 11600 psi @Temperature 140 - 248 °F	Average value: 31.0 MPa Grade Count:2
Overview of materials for Polypropylene, Glass/Mineral Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Glass/Mineral Reinforced". Each property range of values reported is minimum and maximum ..
Tensile Strength, Ultimate	9.00 - 15.0 MPa @Temperature 60.0 - 90.0 °C	1310 - 2180 psi @Temperature 140 - 194 °F	Average value: 12.0 MPa Grade Count:1
Overview of materials for Polypropylene Copolymer This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene Copolymer". Each property range of values reported is minimum and maximum values of approp..