ExxonMobil Escorene® LD-402 LDPE Electrical Jacketing Resin (discontinued **)
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Wire/Cable Grade |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Escorene® LD-402 LDPE Electrical Jacketing Resin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer, Exxon Chemical.A low density polyethylene homopolymer resin designed for high speed extrusions.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | Exxon Method |
| Environmental Stress Crack Resistance | <= 5.0 hour | <= 5.0 hour | F50, Condition A; ASTM D-1693 |
| Melt Flow | 12 g/10 min | 12 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 48 | 48 | ASTM D2240 |
| Tensile Strength, Ultimate | 9.00 MPa | 1310 psi | ASTM D638 |
| Elongation at Break | 760 % | 760 % | ASTM D638 |
| Flexural Modulus | 0.165 GPa | 23.9 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 104 °C | 219 °F | Exxon Method |
| Brittleness Temperature | <= -67.0 °C | <= -88.6 °F | ASTM D746 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.03 @Frequency 1e+6 Hz |
2.03 @Frequency 1e+6 Hz |
ASTM D150 |
| Dielectric Strength | 14.2 kV/mm @Thickness 3.17 mm |
361 kV/in @Thickness 0.125 in |
ASTM D149 |
| Dissipation Factor | 0.00010 @Frequency 1e+6 Hz |
0.00010 @Frequency 1e+6 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- MV Labs NA870 Na2CO4 Sodium oxalate
- Omnia Plastica Rilsan® PA6 GF - Akulon GF - at 50% RH
- SABIC Innovative Plastics Extem UH1016M TPI Blend (Europe-Africa-Middle East)
- Plastcom SLOVAMID 6 GF 5 PA6, 5% glass fibre
- Formosa Plastics Formolene® HL3712 Sheet and Thermoforming HDPE (discontinued **)
- Stir SpA FB 70 E (PVC)
- Teknor Apex Sinvicomp SBB 3700 Polyvinyl Chloride, Rigid
- Williams Advanced Alloys C106 Solder
- Arkema Group Appryl® CZN 0525 Polypropylene, 25% Talc Filled
- CeramTec B 40 Alumina, 99.1%
Copyright © lookpolymers.com All Rights Reserved