Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 793 MPa | 115000 psi | |
Kennametal Stellite Nistelle® C-4C Nickel Alloy Comparable to Tribaloy Alloy 745. Data provided by the manufacturer, Deloro Stellite Inc.Product of former Deloro Stellite Inc. |
|||
Tensile Strength, Ultimate | 793 MPa @Temperature 677 °C |
115000 psi @Temperature 1250 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, 12.7 mm (1/2 in.) thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
Tensile Strength, Ultimate | 790 MPa @Temperature 650 °C |
115000 psi @Temperature 1200 °F |
|
Haynes 214® alloy, hot rolled solution annealed plate 12.7 mm (1/2 in.) thick Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Tensile Strength, Ultimate | 793 MPa | 115000 psi | |
Haynes HR-160® alloy, plate, aged 1000 hours at 760°C (1400°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Tensile Strength, Ultimate | 793 MPa @Temperature 538 °C |
115000 psi @Temperature 1000 °F |
|
Haynes Ultimet® alloy, 12.7-50.8 mm bar Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Tensile Strength, Ultimate | 790 - 930 MPa | 115000 - 135000 psi | |
Materion Brush 60™ 3/4 HT Information supplied by Brush Wellman Engineered Materials.Treatment required for max strength: Mill HardenedStress Relaxation-% Stress Remaining after 1000 hrs @ 100°C: 96%Stress Relaxation afte.. |
|||
Tensile Strength, Ultimate | >= 790 MPa | >= 115000 psi | |
MetalTek IN® 100 UNS N13100 Centri-Vac Nickel Based Alloy Information provided by MetalTek |
|||
Tensile Strength, Ultimate | 790 MPa | 115000 psi | |
Haynes 556® alloy, 0% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Tensile Strength, Ultimate | 795 MPa @Temperature 205 °C |
115000 psi @Temperature 401 °F |
|
Haynes Hastelloy® B-3® alloy, 6.3 mm plate The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
Tensile Strength, Ultimate | 790 MPa | 115000 psi | Annealed |
Special Metals INCONEL® Alloy C-276 A nickel-molybdenum-chromium alloy with an addition of tungsten having excellent corrosion resistance in a wide range of severe environments. The high molybdenum content makes the alloy especially .. |
|||
Tensile Strength, Ultimate | 793 MPa | 115000 psi | Sheet |
Special Metals INCONEL® HX Nickel Superalloy Data provided by the manufacturer, Special Metals. |
|||
Tensile Strength, Ultimate | 793 MPa | 115000 psi | |
Universal Wire Works 312 Stainless Steel Electrode Universal 312 electrodes were originally designed for the welding of high tensile alloys to high temperature heat resisting alloys on turbine engines. However, based upon performance these electrode.. |
|||
Tensile Strength, Ultimate | 793 MPa | 115000 psi | |
Universal Wire Works 622 Nickel Alloy Welding Wire Alloy 622 is an alloy of nickel with chromium, molybdenum, tungsten as principal alloying elements. It is used to weld alloys of similar composition as well as dissimilar joints between nickel-chrom.. |
|||
Tensile Strength, Ultimate | 793 MPa | 115000 psi | Annealed and Aged |
Universal Wire Works Inconel 92 (AMS 5675) Nickel Alloy Filler Metal Inconel Filler Metal 92 is a nickel base alloy designed especially for gas tungsten arc and gas metal arc welding of dissimilar combinations of high nickel alloys and austenitic and ferritic steels... |
|||
Tensile Strength, Ultimate | 793 MPa | 115000 psi | |
Universal Wire Works No. 6 Cobalt Alloy Welding Wire Universal No. 6 is a cobalt-chromium-tungsten alloy suited for applications requiring extreme impact resistance at elevated temperatures, exhaust valve contact surfaces, hot and cold trimmer dies an.. |
|||
Tensile Strength, Ultimate | 793 MPa @Temperature 399 °C |
115000 psi @Temperature 750 °F |
(hardened to 310 HB) |
Bohler-Uddeholm HOLDER Pre-hardened Holder Tool Steel Chromium-molybdenum alloyed steelA pre-hardened steel with very good machinability supplied at ~300 HB for clamping and holding plates and blocks.Holder is characterized by: Excellent machinability.. |
|||
Tensile Strength, Ultimate | 792 - 930 MPa | 115000 - 135000 psi | |
Ametek AM 388™ Alloy (UNS C72650) TM02 Information supplied by Ametek Specialty Metal Products Division.Copper base Spinodal alloy with high conductivity and high strength. Outstanding performance for contacts in connectors, sockets and.. |
|||
Tensile Strength, Ultimate | 793 MPa | 115000 psi | |
ATI Allvac® Nickelvac® C-276 UNS N10276 Nickel Superalloy Uses: Pressure vessels, pumps, valves, HX tubing and piping for the CPI and HPI. Trays, flanges, fasteners, wire, screens.Property values are for samples in the metallurgical condition: 2050°F anne.. |
|||
Tensile Strength, Ultimate | 793 MPa | 115000 psi | |
ATI Allvac® Nickelvac® HC-276 Nickel Superalloy, Heat Treatment: 1121°C (2050°F) Anneal Data provided by Allvac.Applications: High temperature applications also requiring good resistance to corrosive fluids, such as liquids and combustion products. |
|||
Tensile Strength, Ultimate | 793 MPa @Temperature 538 °C |
115000 psi @Temperature 1000 °F |
|
Carpenter Custom 630 (17-Cr-4Ni) Precipitation Hardening Stainless Steel, Condition H 900 (Age-Hardened 482°C/1hr/AC) Data provided by Carpenter Technology Corporation.Custom 630 (17Cr-4Ni) is a martensitic precipitation/age-hardening stainless steel offering high strength and hardness along with excellent corrosio.. |
|||
Tensile Strength, Ultimate | 792 MPa | 115000 psi | |
Carpenter Hiperco® 50 Fe-Co-V Soft Magnetic Alloy, 0.15 mm Strip Heat Treated 843°C Hiperco® alloy 50 is an iron-cobalt-vanadium soft magnetic alloy which exhibits high magnetic saturation (24 kilogauss), high D.C. maximum permeability, low D.C. coercive force, and low A.C. core l.. |
|||
Tensile Strength, Ultimate | 790 MPa | 115000 psi | Typical |
ATI Allegheny Ludlum AL 601™ Nickel-Base Alloy, Annealed at 982°C (1800°F), UNS N06601 Allegheny Ludlum's AL 601 alloy is an austenitic nickel-chromium-iron alloy designed for both heat and corrosion resistance. As compared to AL 600 alloy, the AL 601 alloy has, in addition to increa.. |
|||
Tensile Strength, Ultimate | 793 MPa | 115000 psi | |
ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 304, 20% Cold Rolled (UNS S30400) This alloy is one of the most familiar and most frequently used alloy in the stainless steel family. It may be best used in applications where the following properties are important: resistance to .. |
|||
Tensile Strength, Ultimate | 796 MPa | 115000 psi | |
Haynes Hastelloy® N, 1.6 mm sheet, aged 128 hours at 815°C (1500°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
Tensile Strength, Ultimate | 794 MPa | 115000 psi | |
Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, rapid air cooled Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
Tensile Strength, Ultimate | 793 MPa | 115000 psi | |
Materion PROtherm® Beryllium Copper Alloy Description: moldMAX® and PROtherm® are Brush Wellman's copper beryllium alloys specifically designed for the plastic processing industry. These alloys provide a combination of thermal conduct.. |
|||
Tensile Strength, Ultimate | 793 MPa | 115000 psi | |
Haynes Hastelloy® C-22® alloy, GTAW weld, 316L base metal, C-22 weld metal HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
Tensile Strength, Ultimate | 793 MPa | 115000 psi | |
Schmolz + Bickenbach MoldMAX XL® Copper Alloy Description: Brush Wellman’s MoldMAX XL® is a high strength copper mold alloy with good thermal conductivity. The alloy contains no beryllium and is available in sections as large as 12” thick. .. |