Special Metals INCONEL® Alloy C-276
| Category | Metal , Nonferrous Metal , Nickel Alloy , Superalloy |
| Manufacturer | Special Metals (includes the former Inco Alloys International Inc.) |
| Trade Name | INCONEL® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Special Metals INCONEL® Alloy C-276.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A nickel-molybdenum-chromium alloy with an addition of tungsten having excellent corrosion resistance in a wide range of severe environments. The high molybdenum content makes the alloy especially resistant to pitting and crevice corrosion. The low carbon content minimizes carbide precipitation during welding to maintain corrosion resistance in as-welded structures. Used in pollution control, chemical processing, pulp and paper production, and waste treatment. Standard product forms are round, forging stock, tube, pipe, plate, sheet, strip, and wire.Data provided by the manufacturer, Special Metals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.89 g/cc | 0.321 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 790 MPa | 115000 psi | Annealed |
| 620 MPa @Temperature 550 °C |
89900 psi @Temperature 1020 °F |
Annealed prior to test | |
| Tensile Strength, Yield | 415 MPa | 60200 psi | Annealed |
| 230 MPa @Temperature 550 °C |
33400 psi @Temperature 1020 °F |
Annealed prior to test | |
| Elongation at Break | 62 % | 62 % | Annealed prior to test. |
| 60 % @Temperature 550 °C |
60 % @Temperature 1020 °F |
Annealed prior to test. |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 100 °C |
6.78 µin/in-°F @Temperature 68.0 - 212 °F |
|
| Specific Heat Capacity | 0.427 J/g-°C | 0.102 BTU/lb-°F | |
| Thermal Conductivity | 9.80 W/m-K | 68.0 BTU-in/hr-ft²-°F | |
| Melting Point | 1325 - 1370 °C | 2417 - 2500 °F | |
| Solidus | 1325 °C | 2417 °F | |
| Liquidus | 1370 °C | 2500 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | <= 0.010 % | <= 0.010 % | |
| Chromium, Cr | 14.5 - 16.5 % | 14.5 - 16.5 % | |
| Cobalt, Co | <= 2.5 % | <= 2.5 % | |
| Iron, Fe | 4.0 - 7.0 % | 4.0 - 7.0 % | |
| Manganese, Mn | <= 1.0 % | <= 1.0 % | |
| Molybdenum, Mo | 15 - 17 % | 15 - 17 % | |
| Nickel, Ni | 55 % | 55 % | As remainder |
| Phosphorous, P | <= 0.040 % | <= 0.040 % | |
| Silicon, Si | <= 0.080 % | <= 0.080 % | |
| Sulfur, S | <= 0.030 % | <= 0.030 % | |
| Tungsten, W | 3.0 - 4.5 % | 3.0 - 4.5 % | |
| Vanadium, V | <= 0.35 % | <= 0.35 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.0001229 ohm-cm | 0.0001229 ohm-cm | |
| Magnetic Permeability | 1.0002 | 1.0002 | at 200 oersted (15.9 kA/m) |
Users viewing this material also viewed the following:
- Polykemi AB POLYelast TPE E706 Thermoplastic Elastomer, EPDM-based
- DuPont Performance Polymers Hypalon® HPG-6525 Chlorosulfonated Polyethylene Rubber, Carbon Black Filled Compound &n
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 30 PHR N550 (FEF) Filler
- Haynes 282® Nickel Alloy Sheet, Solution Annealed and Age-hardened
- Solvay Specialty Polymers Aquivion® D79-20BS Tetrafluoroethylene + SFVE (TFE+SFVE)
- Goodfellow Nichrome®, Tophet A® Nickel 80 Chromium 20 Alloy
- ExxonMobil Bicor® 70 HSH OPP Film
- Fainplast Compounds HGKA 78 Flexible PVC, Sheathing for High Temperatures Lead Free
- Fainplast Compounds FRT 82 Flexible PVC, Insulation
- Braskem LF 118/21 LLDPE Blown Film Extrusion Polyethylene Copolymer
Copyright © lookpolymers.com All Rights Reserved