Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 78.6 MPa | 11400 psi | ASTM D638 |
Nylene® 4114-14 GL (HS) , 14% Glass Fiber Reinforced, Impact Modified Nylon 6/6 Description: Nylene® 4114-14 GL (HS) is a 14% glass reinforced, high impact nylon 6/6. 4114-14 GL is automotive approved. Information provided by Custom Resins. ALM, Nylene Canada, and Custom Resin.. |
|||
Tensile Strength, Ultimate | 78.5 MPa | 11400 psi | ISO 527 |
Polikim KESTLUB® Polyamide 6 + Lubricant Kestlub® is a special type of cast polyamide ideal for bearings. It is produced by adding lubricants to cast polyamide through special processes. It performs extremely well in bearing applications .. |
|||
Tensile Strength, Ultimate | 78.5 MPa | 11400 psi | DIN 53455; ASTM D638 |
Kolon KOPA® KN178MT40 M/F Reinforced Nylon 6 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubr.. |
|||
Tensile Strength, Ultimate | 78.5 MPa @Temperature 23.0 °C |
11400 psi @Temperature 73.4 °F |
ASTM D1708 |
Daelim H&L Plavis MS Aromatic Polyimide, 15% MoS2 Filled, Machined Parts Available in vacuum or non-lubrication condition, very high abrasion resistance and low friction coefficient propertyInformation provided by Daelim H&L |
|||
Tensile Strength, Ultimate | 78.6 MPa | 11400 psi | |
Abatron AboCast 50-3/AboCure 50-12 Epoxy Data provided by the manufacturer, Abatron, Inc. Light motor oil viscosity, almost colorless. Shelf life is 12+ months. |
|||
Tensile Strength, Ultimate | 78.5 MPa | 11400 psi | 5mm/min; ASTM D638 |
Asia International Enterprise (Hong Kong) 60T6 Nylon 66, 30% Filled Information provided by Asia International Enterprise (Hong Kong) Ltd. |
|||
Tensile Strength, Ultimate | 78.5 MPa | 11400 psi | ISO 527 |
Polikim KESTAMID® HS Polyamide 6, Heat Resistant Kestamid-HS® is Polikim’s cast polyamide with increased heat resistance. Thermal stabilizer additives increase thermal aging significantly. In operating temperatures over 80°C, it performs with .. |
|||
Tensile Strength, Ultimate | 78.5 MPa | 11400 psi | 5mm/min; ASTM D638 |
Asia International Enterprise (Hong Kong) 6010FEN Nylon 66 Information provided by Asia International Enterprise (Hong Kong) Ltd. |
|||
Tensile Strength, Ultimate | 78.5 MPa | 11400 psi | 5mm/min; ASTM D638 |
Asia International Enterprise (Hong Kong) ST6010 Nylon 66 Information provided by Asia International Enterprise (Hong Kong) Ltd. |