- Daelim H&L Plavis MS Aromatic Polyimide, 15% MoS2 Filled, Machined Parts
Daelim H&L Plavis MS Aromatic Polyimide, 15% MoS2 Filled, Machined Parts
| Category | Polymer , Thermoset , Polyimide, TS |
| Manufacturer | Daelim H&L Super Engineering Plastics |
| Trade Name | Plavis |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Daelim H&L Plavis MS Aromatic Polyimide, 15% MoS2 Filled, Machined Parts.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Available in vacuum or non-lubrication condition, very high abrasion resistance and low friction coefficient propertyInformation provided by Daelim H&L
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.60 g/cc | 1.60 g/cc | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.90 % | 0.90 % | 50% RH; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 70 - 75 | 70 - 75 | ASTM D785 |
| Tensile Strength, Ultimate | 78.5 MPa @Temperature 23.0 °C |
11400 psi @Temperature 73.4 °F |
ASTM D1708 |
| Tensile Strength, Yield | 29.4 MPa @Strain 1.00 % |
4270 psi @Strain 1.00 % |
ASTM D95 |
| 103 MPa @Strain 10.0 % |
14900 psi @Strain 10.0 % |
ASTM D95 | |
| Elongation at Break | 6.3 % @Temperature 23.0 °C |
6.3 % @Temperature 73.4 °F |
ASTM D1708 |
| Flexural Strength | 51.0 MPa @Temperature 260 °C |
7400 psi @Temperature 500 °F |
ASTM D790 |
| 85.8 MPa @Temperature 23.0 °C |
12400 psi @Temperature 73.4 °F |
ASTM D790 | |
| Flexural Modulus | 2.35 GPa @Temperature 260 °C |
341 ksi @Temperature 500 °F |
ASTM D790 |
| 2.94 GPa @Temperature 23.0 °C |
427 ksi @Temperature 73.4 °F |
ASTM D790 | |
| Compressive Modulus | 2.4525 GPa @Temperature 23.0 °C |
355.71 ksi @Temperature 73.4 °F |
ASTM D695 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 5.10 µm/m-°C @Temperature 23.0 - 260 °C |
2.83 µin/in-°F @Temperature 73.4 - 500 °F |
ASTM D696 |
| Decomposition Temperature | 623 °C | 1150 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| 50% Weight Reduction Time (Minutes) | 250 |
Users viewing this material also viewed the following:
- Rogers Corporation Poron® ThinStik™ 92-09020 Self-Adhesive Urethane Foam
- Plenco 304 Black Impact Grade Woodflour/Cellulose Filled Phenolic Molding Compound (discontinued **)
- Kolon KOPA® KN333HRBL Heat Resistant Nylon 66
- Latrobe Lescalloy® 9310 VAC-ARC Premium Carburizing Steel
- Sylvin Technologies 9915-65 Natural PVC Molding Compound
- Formosa Plastics Formolene® 6144O Impact Copolymer Polypropylene
- A. Schulman FORMION™ FI 393 Ionomer
- Elektro-Isola Etronit IIQ R Phenolic, Paper Reinforcement, Yellow, Sheets
- Arkema Group Orgalloy® RS 6015 ES T6L Polyamide Alloy
- Lehmann & Voss LUVOCOM® 1105-7825 PEEK, with PTFE
Copyright © lookpolymers.com All Rights Reserved