- Polymer Property : Tensile Strength, Ultimate = 1100 psi
Polymer Property : Tensile Strength, Ultimate = 1100 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 7.60 MPa | 1100 psi | ASTM D412 |
| Multibase Multi-Flex® TPE A 7204 LC BLK Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
| Tensile Strength, Ultimate | 7.60 MPa | 1100 psi | ASTM D412 |
| Multibase Multi-Flex® TPE A 7318 BLK The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
| Tensile Strength, Ultimate | 7.58 MPa | 1100 psi | post cured- 2 hours at 177°C |
| Multibase SILASTIC® C7-4565 CADOX TS-50S Dow-Corning Biomedical Grade ETR Elastomer Information provided by Multibase |
|||
| Tensile Strength, Ultimate | 7.60 - 31.0 MPa | 1100 - 4500 psi | Average value: 17.1 MPa Grade Count:30 |
| Overview of materials for Methacrylate Adhesive This property data is a summary of similar materials in the MatWeb database for the category "Methacrylate Adhesive". Each property range of values reported is minimum and maximum values of appropri.. |
|||
| Tensile Strength, Ultimate | 7.58 - 96.5 MPa | 1100 - 14000 psi | Average value: 48.2 MPa Grade Count:56 |
| Overview of materials for Epoxy, Cast, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Epoxy, Cast, Unreinforced". Each property range of values reported is minimum and maximum values of appr.. |
|||
| Tensile Strength, Ultimate | 7.60 MPa | 1100 psi | |
| Freudenberg Simrit F40 Fluorosilicone Elastomer Combines excellent low-temperature performance of silicone with improved chemical resistance. Very good resistance to military and aerospace fuels. Excellent performance in oxygen plasma environment.. |
|||
| Tensile Strength, Ultimate | 7.60 MPa | 1100 psi | ASTM D3574E |
| Mearthane Durethaneâ„¢ M DM-715A Foam Polyurethane MDI backbone: ether.Shore 00 Hardness: 60Summary: Durethane M is a flexible, microcellular, open cell and closed cell urethane foam. Because it is mechanically mixed, the cell size is uniform. Dur.. |
|||
| Tensile Strength, Ultimate | 7.60 MPa | 1100 psi | Bond Strength Tensile Shear, to ABS or polycarbonate; ASTM D1002 |
| ITW Plexus Plexusâ„¢ MA200 Methacrylate Adhesive Two component adhesive that expands to twice original volume without toxic blowing agents. Used where weight, gap-filling, or increased toughness (vibration damping) is requires for the bonded join.. |
|||
| Tensile Strength, Ultimate | 7.58 MPa | 1100 psi | molded-without post cure; ASTM D412 |
| Multibase C6-235 DI-CUP R Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
| Tensile Strength, Ultimate | 7.58 MPa | 1100 psi | post cured- 2 hours at 177°C; ASTM D412 |
| Multibase C6-235 DI-CUP R Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
| Tensile Strength, Ultimate | 7.58 MPa | 1100 psi | post cured- 4 hours at 177°C; ASTM D412 |
| Multibase C6-235 DI-CUP R Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
| Tensile Strength, Ultimate | 7.58 MPa | 1100 psi | post cured- 8 hours at 177°C; ASTM D412 |
| Multibase C6-235 PERKADOX PD-50S Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
| Tensile Strength, Ultimate | 7.58 MPa | 1100 psi | post cured- 2 hours at 177°C; ASTM D412 |
| Multibase C6-235 VAROX DBPH Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
| Tensile Strength, Ultimate | 7.58 MPa | 1100 psi | post cured- 4 hours at 177°C; ASTM D412 |
| Multibase C6-235 VAROX DBPH Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
| Tensile Strength, Ultimate | 7.58 MPa | 1100 psi | post cured- 8 hours at 177°C; ASTM D412 |
| Multibase C6-235 VAROX DBPH Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
| Tensile Strength, Ultimate | 7.58 MPa | 1100 psi | molded-without post cure; ASTM D412 |
| Multibase C6-265 DI-CUP R Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
| Tensile Strength, Ultimate | 7.58 MPa | 1100 psi | post cured- 2 hours at 177°C; ASTM D412 |
| Multibase C6-265 DI-CUP R Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
| Tensile Strength, Ultimate | 7.58 MPa | 1100 psi | post cured- 4 hours at 177°C; ASTM D412 |
| Multibase C6-265 DI-CUP R Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
| Tensile Strength, Ultimate | 7.58 MPa | 1100 psi | post cured- 4 hours at 177°C; ASTM D412 |
| Multibase C6-265 PERKADOX PD-50S Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
| Tensile Strength, Ultimate | 7.58 MPa | 1100 psi | post cured- 8 hours at 177°C; ASTM D412 |
| Multibase C6-265 PERKADOX PD-50S Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
| Tensile Strength, Ultimate | 7.58 MPa | 1100 psi | molded-without post cure; ASTM D412 |
| Multibase C6-265 PERKADOX PD-50S Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
| Tensile Strength, Ultimate | 7.58 MPa | 1100 psi | molded-without post cure; ASTM D412 |
| Multibase C6-265 VAROX DBPH Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
| Tensile Strength, Ultimate | 7.58 MPa | 1100 psi | post cured- 2 hours at 177°C; ASTM D412 |
| Multibase C6-265 VAROX DBPH Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
| Tensile Strength, Ultimate | 7.58 MPa | 1100 psi | post cured- 8 hours at 177°C; ASTM D412 |
| Multibase C6-265 VAROX DBPH Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
| Tensile Strength, Ultimate | 7.58 MPa | 1100 psi | |
| Sylvin Technologies 8999-70 Natural PVC Extrusion Compound Information provided by Sylvin Technologies Inc. |
|||
| Tensile Strength, Ultimate | 7.58 MPa | 1100 psi | |
| Sylvin Technologies 9960-60 Natural PVC Molding Compound Information provided by Sylvin Technologies Inc. |
|||
| Tensile Strength, Ultimate | 7.58 MPa | 1100 psi | |
| Sylvin Technologies 9980-65 Natural PVC Molding Compound Information provided by Sylvin Technologies Inc. |
|||
| Tensile Strength, Ultimate | 7.58 MPa | 1100 psi | |
| Sylvin Technologies 9999-70 Natural PVC Molding Compound Information provided by Sylvin Technologies Inc. |
|||
| Tensile Strength, Ultimate | 7.61 - 8.99 MPa | 1100 - 1300 psi | |
| Arlon Flexible Silicon Insulation with Fiberglass Substrate (56493F031) Side one - cured silicone rubber ,0.007 in. (0.18 mm) minimum: Substrate - Prime Coated 1564 Fiberglass, 0.017 in. (0.43 mm) nominal; Side two- cured silicone rubber, 0.007 in. (0.18 mm) minimum; 0... |
|||
| Tensile Strength, Ultimate | 7.58 MPa | 1100 psi | silicone property; ASTM D412 |
| Arlon R37908R015L Silicone Rubber/Fiberglass/Acrylic/Polyester Laminated film: aluminized PEN; Side 1: cured silicone rubber; Substrate: 7628 fiberglass; Side 2, layer 1: acrylic PSA; Side 2, layer 2: polyester substrate; Side 2, layer 3: acrylic PSA; Interleav.. |
|||