Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | |
Cookson Group Plaskon® 3300SGH Mineral Filled Epoxy Molding Compound
(discontinued **) Test specimens were transfer molded and post cured 4 hours at 175°C.Exhibits exceptional reliability, excellent moldability, good release characteristics, low flash and rapid cure. This compound i.. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ASTM D638 |
Firestone CL200-001 Nylon 6 Natural color. Not heat stabilized or modified. Lubricated. Chip size is 2 x 3.5 mm.Information provided by Firestone |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ASTM D638 |
IDI Composites C-108 Thermoset Polyester, Molding Vinylester compounds in a range of strengths with superior corrosion resistance.Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | DIN 53455; ASTM D638 |
Kolon Kopa® KN1331 Nylon 6 Resin KOPA is widely used in the automobile and industrial parts.General KOPA N-6 Features: Good mechanical properties, Extreme toughness, Outstanding self-lubrication and abrasion resistance, Excellent c.. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ASTM D638 |
Aardvark Polymers Aarlon® 2000 Rotational Molding Resin, DAM Aarlon® 2000 PA 6/6 is a high performance nylon for rotational molding applications. Aarlon® 2000 offers high heat capabilities with exceptional mechanical properties.Information provided by G.. |
|||
Tensile Strength, Ultimate | 83.0 MPa @Temperature 1205 °C |
12000 psi @Temperature 2201 °F |
|
Haynes 188 alloy, hot rolled and 1175°C solution annealed plate Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Tensile Strength, Ultimate | 83.0 MPa @Temperature 1095 °C |
12000 psi @Temperature 2003 °F |
|
Haynes Waspaloy™ alloy, sheet Age-hardenable superalloy with very good strength at temperatures up 980°C (1800°F), can be cold-formed in the annealed condition, may also be hot formed at 1040°C (1900°F) and above, go.. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | DIN 53455; ASTM D638 |
Kolon Kopa® KN138R Nylon 6 Resin KOPA is widely used in the automobile and industrial parts.General KOPA N-6 Features: Good mechanical properties, Extreme toughness, Outstanding self-lubrication and abrasion resistance, Excellent c.. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ASTM D638 |
Sumitomo Bakelite North America RX® 3-1-525F-P Short-Glass Reinforced Diallyl Phthalate Ortho Resin Isomer (DAP). Used for critical, high-performance military and commercial electrical components where long-term reliability is demanded.Meets the requirements of ASTM D5948 Type SDG-F.I.. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ASTM D638 |
Sumitomo Bakelite North America RX® 3-2-520F-P Short-Glass Reinforced Diallyl Phthalate Isophthalate DAP Resin Isomer. Used for critical, high-performance military and commercial electrical components where long-term reliability is demanded.Meets the requirements of ASTM D5948 Type SI.. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ASTM D638 |
Plenco 1530 Polyester, Briquette, Transfer Molded PLENCO 01530 is a glass and mineral reinforced pelletized polyester molding compound, offering improved mechanical strength properties along with excellent electrical properties and dimensional stab.. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | |
Cosmic Plastics E4940 Mineral & Glass Filled Epoxy Molding Compound, Encapsulated Grade Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | |
Cosmic Plastics E486 lass Filled Epoxy Molding Compound, Electrical Grade Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | |
Cosmic Plastics E487 lass Filled Epoxy Molding Compound, Electrical Grade Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | |
Cosmic Plastics E4930 Mineral & Glass Filled Epoxy Molding Compound, Encapsulated Grade Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ATSM D638 |
Ashley Polymers Ashlene® 520S-13GU Nylon 66, 13% Glass Reinforced Nylon 66, 13% Glass reinforced resin with heat stabilizer, utility grade. Also available in black (520S-13GBU).Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ATSM D638 |
Ashley Polymers Ashlene® 528LS Nylon 66 A general purpose Nylon 66, lubricated and heat stabilized for injection molding.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ATSM D638 |
Ashley Polymers Ashlene® 62M Nylon 66, 40% Mineral reinforced A 40% mineral reinforced Nylon 66 resin modified for reduced shrinkage.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ATSM D638 |
Ashley Polymers Ashlene® P1525B Polycarbonate A rigid flame retardant black polycarbonate, for applications requiring superior dimensional stability and overall toughness.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | Static |
Channel Industries 5800 Lead Zirconate Titanate Piezoelectric Characterized by high coupling factors and high piezoelectric and dielectric constants over extended temperature ranges and stress amplitudes, lead zirconate titanates are the most extensively used .. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ASTM D638 |
A. Schulman ComAlloy Hiloy® 431 Glass Reinforced, PBT Alloy Data provided by the manufacturer, ComAlloy International Company.15% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ASTM D638 |
A. Schulman ComAlloy Hiloy® 511 Polycarbonate, Glass Reinforced, UL Data provided by the manufacturer, ComAlloy International Company.10% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ATSM D638 |
Ashley Polymers Ashlene® 1420B Polycarbonate, 20% Glass Reinforced A 20% glass reinforced polycarbonate for increased mechanical strength and thermal properties, modified for good impact with increased dimensional stability and overall toughness. 1423B with UV sta.. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ATSM D638 |
Ashley Polymers Ashlene® 830 Nylon 6 Basic Nylon 6, medium viscosity, unlubricated.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ATSM D638 |
Ashley Polymers Ashlene® 830L Nylon 6 Basic Nylon 6, medium viscosity, lubricated.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | Static |
Channel Industries 5804 Lead Zirconate Titanate Piezoelectric Navy Type IIICharacterized by high coupling factors and high piezoelectric and dielectric constants over extended temperature ranges and stress amplitudes, lead zirconate titanates are the most exte.. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | |
Cookson Group Plaskon® 3300S Mineral Filled Novolac Epoxy Molding Compound
(discontinued **) Test specimens were transfer molded and post cured 4 hours at 175°C.A low stress, flame retardant, novolac hardened epoxy molding compound designed to provide hermeticity protection exceeding that .. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | DIN 53455; ASTM D638 |
Kolon Kopa® KN173MT40 Nylon 6 Resin KOPA is widely used in the automobile and industrial parts.General KOPA N-6 Features: Good mechanical properties, Extreme toughness, Outstanding self-lubrication and abrasion resistance, Excellent c.. |