- Polymer Property : Tensile Strength, Ultimate = 620 MPa
Polymer Property : Tensile Strength, Ultimate = 620 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 620 MPa | 89900 psi | Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1 |
| Outokumpu 4406 Cr-Ni-Mo Austenitic Stainless Steel Applications: Wet corrosion resistance and general service.Available in hot rolled plate (Quarto), hot rolled strip/sheet (CPP), cold rolled strip/sheet, cold rolled narrow strip, bar, and rod forms.. |
|||
| Tensile Strength, Ultimate | 620 MPa | 89900 psi | Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1 |
| Outokumpu 4833 High Temperature Austenitic Stainless Steel Standardized high temperature steel for service at temperatures of up to 950-1000°C in dry air. Utilization in the temperature range of 600-900°C can lead to embrittlement.Applications: Heat and .. |
|||
| Tensile Strength, Ultimate | 620 - 750 MPa | 89900 - 109000 psi | Solution Annealed and Aged |
| Materion Beryllium Copper Alloy 10C Castings (UNS C82000) Pouring Temperature: 1095-1175°CHeat treatment required for max strength (Annealing): 870-900°C/water quenchHeat treatment required for max strength (Hardening): 870-900°C/water quenchTabul.. |
|||
| Tensile Strength, Ultimate | 620 - 870 MPa | 89900 - 126000 psi | |
| Materion Beryllium Copper Alloy 165 Plate & Rolled Bar; H (TD04) Temper; over 9.5 to 25 mm Thickness (UNS C17000) Treatment required for max strength: as suppliedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to.. |
|||
| Tensile Strength, Ultimate | 620 - 900 MPa | 89900 - 131000 psi | |
| Materion Beryllium Copper Alloy 165 Plate & Rolled Bar; H (TD04) Temper; up to 9.5 mm Thickness (UNS C17000) Treatment required for max strength: as suppliedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to.. |
|||
| Tensile Strength, Ultimate | 620 - 870 MPa | 89900 - 126000 psi | |
| Materion Beryllium Copper Alloy 165 Rod and Bar; H (TD04) Temper; over 9.5 to 25.4 mm (UNS C17000) Treatment required for max strength: as suppliedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to.. |
|||
| Tensile Strength, Ultimate | 620 - 900 MPa | 89900 - 131000 psi | |
| Materion Beryllium Copper Alloy 165 Rod and Bar; H (TD04) Temper; up to 9.5 mm (UNS C17000) Treatment required for max strength: as suppliedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to.. |
|||
| Tensile Strength, Ultimate | 620 - 900 MPa | 89900 - 131000 psi | |
| Materion Beryllium Copper Alloy 25 Plate & Rolled Bar; H (TD04) Temper; up to 9.5 mm Thickness (UNS C17200) Treatment required for max strength: as suppliedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to.. |
|||
| Tensile Strength, Ultimate | 620 - 870 MPa | 89900 - 126000 psi | |
| Materion Beryllium Copper Alloy 25 Rod and Bar; H (TD04) Temper; over 9.5 to 25.4 mm (UNS C17200) Treatment required for max strength: as suppliedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to.. |
|||
| Tensile Strength, Ultimate | 620 - 900 MPa | 89900 - 131000 psi | |
| Materion Beryllium Copper Alloy 25 Tube; H (TD04) Temper; up to 9.5 mm o.d. (UNS C17200) Treatment required for max strength: as suppliedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to.. |
|||
| Tensile Strength, Ultimate | 620 - 800 MPa | 89900 - 116000 psi | |
| Materion Beryllium Copper Alloy 25 Wire; 1/4H (TD01) Temper; 1.3-12.7 mm Diameter (UNS C17200) Treatment required for max strength: as suppliedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to.. |
|||
| Tensile Strength, Ultimate | 620 - 800 MPa | 89900 - 116000 psi | |
| Materion Beryllium Copper Alloy M25 Wire; 1/4H (TD01) Temper; 1.3-12.7 mm Diameter (UNS C17300) Treatment required for max strength: as suppliedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to.. |
|||
| Tensile Strength, Ultimate | >= 620 MPa | >= 89900 psi | |
| MetalTek MTEK 220-01 Cast UNS J82090 Martensitic Stainless Steel Information provided by MetalTek |
|||
| Tensile Strength, Ultimate | >= 620 MPa | >= 89900 psi | |
| MetalTek MTEK 222-01 Cast UNS J82090 Martensitic Stainless Steel Information provided by MetalTek |
|||
| Tensile Strength, Ultimate | >= 620 MPa | >= 89900 psi | |
| MetalTek MTEK 230 Cast UNS C95500 Aluminum Bronze Versatile alloy with high strength, good ductility, unusual toughness, plus exceptional wear resistance. Aluminum Bronze heat treated to higher mechanical properties where necessary.Information prov.. |
|||
| Tensile Strength, Ultimate | >= 620 MPa | >= 89900 psi | |
| MetalTek Nitronic® 33 Austenitic Stainless Steel Produced under license of ARMCO Advanced Materials Corp. Information provided by MetalTekWrought Grade NITRONIC 33® |
|||
| Tensile Strength, Ultimate | >= 620 MPa | >= 89900 psi | |
| MetalTek Nitronic® 40 Austenitic Stainless Steel Produced under license of ARMCO Advanced Materials Corp. Information provided by MetalTek |
|||
| Tensile Strength, Ultimate | 620 MPa @Temperature 760 °C |
89900 psi @Temperature 1400 °F |
|
| Haynes 25 alloy, hot rolled and 1230°C solution annealed sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Tensile Strength, Ultimate | 620 - 870 MPa | 89900 - 126000 psi | |
| Materion Beryllium Copper Alloy M25 Rod and Bar; H (TD04) Temper; over 9.5 to 25.4 mm (UNS C17300) Treatment required for max strength: as suppliedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to.. |
|||
| Tensile Strength, Ultimate | 620 MPa @Temperature 760 °C |
89900 psi @Temperature 1400 °F |
|
| Haynes 188 alloy, cold rolled and 1175°C solution annealed sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Tensile Strength, Ultimate | 620 MPa | 89900 psi | Annealed prior to test |
| Special Metals BRIGHTRAY® Alloy B Electrical Resistance Alloy A nickel-iron-chromium electrical-resistance alloy for use at operating temperatures up to 2010°F (1100°C). It contains rare-earth additions for increased oxidation resistance, especially und.. |
|||
| Tensile Strength, Ultimate | 620 MPa | 89900 psi | |
| SSAB Tunnplat Domex® 044 BOR Rolled Boron Steel Domex® is the brand name of hot rolled products from SSAB Tunnplat. Compared to conventional quenched and tempered steels, boron steel have several benefits including better formability. Boron .. |
|||
| Tensile Strength, Ultimate | >= 620 MPa | >= 89900 psi | |
| TIMET TIMETAL® 3-2.5 Titanium Alloy (Ti-3Al-2.5V; ASTM Grade 9) Annealed Cold Workable Medium Strength Alloy. UTS, TYS, Elongation, R.A. and bend radius data below are specific to annealed material; other specific condition entries are also available in MatWeb.Features.. |
|||
| Tensile Strength, Ultimate | 620 MPa | 89900 psi | Solution Treated (Typical) |
| ATI Allegheny Ludlum Altemp® A286 Iron-Base Superalloy, UNS S66286 Allegheny Ludlum Altemp A286 alloy is an iron-base superalloy useful for applications requiring high strength and corrosion resistance up to 704 degrees Celsius and for lower stress applications at .. |
|||
| Tensile Strength, Ultimate | 620 MPa | 89900 psi | ASTM D638 |
| Quantum Composites QC-8805 66% Glass Fiber Vinyl Ester SMC
(discontinued **) QC-8805 is a vinyl ester-based sheet molding compound (SMC) reinforced with continuous, unidirectional (0°) glass fibers. It provides high strength, stiffness, and fatigue resistance in the fiber .. |
|||
| Tensile Strength, Ultimate | 620 MPa | 89900 psi | Annealed prior to test |
| Special Metals INCOLOY® Alloy 020 A nickel-iron-chromium alloy with additions of copper and molybdenum. It also contains niobium for stabilization against sensitization and resultant intergranular corrosion. The alloy has excellen.. |
|||