Outokumpu 4406 Cr-Ni-Mo Austenitic Stainless Steel

Category Metal , Ferrous Metal , Austenitic , Stainless Steel
Manufacturer Outokumpu
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Outokumpu 4406 Cr-Ni-Mo Austenitic Stainless Steel.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Applications: Wet corrosion resistance and general service.Available in hot rolled plate (Quarto), hot rolled strip/sheet (CPP), cold rolled strip/sheet, cold rolled narrow strip, bar, and rod forms.
Physical Properties Metric English Comments
Density 8.00 g/cc
0.289 lb/in³
RT
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 620 MPa
89900 psi
Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1
440 MPa

@Temperature 300 °C
 63800 psi

@Temperature 572 °F
 EN min.; EN 10002-5
460 MPa

@Temperature 200 °C
 66700 psi

@Temperature 392 °F
 EN min.; EN 10002-5
520 MPa

@Temperature 100 °C
 75400 psi

@Temperature 212 °F
 EN min.; EN 10002-5
800 MPa

@Temperature -80.0 °C
 116000 psi

@Temperature -112 °F
 EN min; EN 10002-5
1150 MPa

@Temperature -196 °C
 167000 psi

@Temperature -321 °F
 EN min; EN 10002-5
Tensile Strength, Yield 280 MPa

@Strain 0.200 %
 40600 psi

@Strain 0.200 %
 EN min.,RT; EN 10002-1
320 MPa

@Strain 0.200 %
 46400 psi

@Strain 0.200 %
 Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1
360 MPa

@Strain 1.00 %
 52200 psi

@Strain 1.00 %
 Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1
128 MPa

@Strain 0.200 %,
Temperature 500 °C
 18600 psi

@Strain 0.200 %,
Temperature 932 °F
 EN min.; EN 10002-5
135 MPa

@Strain 0.200 %,
Temperature 400 °C
 19600 psi

@Strain 0.200 %,
Temperature 752 °F
 EN min.; EN 10002-5
145 MPa

@Strain 0.200 %,
Temperature 300 °C
 21000 psi

@Strain 0.200 %,
Temperature 572 °F
 EN min.; EN 10002-5
158 MPa

@Strain 1.00 %,
Temperature 500 °C
 22900 psi

@Strain 1.00 %,
Temperature 932 °F
 EN min.; EN 10002-5
164 MPa

@Strain 1.00 %,
Temperature 400 °C
 23800 psi

@Strain 1.00 %,
Temperature 752 °F
 EN min.; EN 10002-5
167 MPa

@Strain 0.200 %,
Temperature 200 °C
 24200 psi

@Strain 0.200 %,
Temperature 392 °F
 EN min.; EN 10002-5
175 MPa

@Strain 1.00 %,
Temperature 300 °C
 25400 psi

@Strain 1.00 %,
Temperature 572 °F
 EN min.; EN 10002-5
198 MPa

@Strain 1.00 %,
Temperature 200 °C
 28700 psi

@Strain 1.00 %,
Temperature 392 °F
 EN min.; EN 10002-5
211 MPa

@Strain 0.200 %,
Temperature 100 °C
 30600 psi

@Strain 0.200 %,
Temperature 212 °F
 EN min.; EN 10002-5
246 MPa

@Strain 1.00 %,
Temperature 100 °C
 35700 psi

@Strain 1.00 %,
Temperature 212 °F
 EN min.; EN 10002-5
380 MPa

@Strain 0.200 %,
Temperature -80.0 °C
 55100 psi

@Strain 0.200 %,
Temperature -112 °F
 EN min.; EN 10002-5
450 MPa

@Strain 1.00 %,
Temperature -80.0 °C
 65300 psi

@Strain 1.00 %,
Temperature -112 °F
 EN min.; EN 10002-5
600 MPa

@Strain 0.200 %,
Temperature -196 °C
 87000 psi

@Strain 0.200 %,
Temperature -321 °F
 EN min.; EN 10002-5
700 MPa

@Strain 1.00 %,
Temperature -196 °C
 102000 psi

@Strain 1.00 %,
Temperature -321 °F
 EN min.; EN 10002-5
Elongation at Break 50 %
50 %
Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1
30 %

@Temperature -196 °C
 30 %

@Temperature -321 °F
 EN min
35 %

@Temperature -80.0 °C
 35 %

@Temperature -112 °F
 EN min
Modulus of Elasticity 200 GPa
29000 ksi
RT
165 GPa

@Temperature 500 °C
 23900 ksi

@Temperature 932 °F
172 GPa

@Temperature 400 °C
 24900 ksi

@Temperature 752 °F
179 GPa

@Temperature 300 °C
 26000 ksi

@Temperature 572 °F
186 GPa

@Temperature 200 °C
 27000 ksi

@Temperature 392 °F
194 GPa

@Temperature 100 °C
 28100 ksi

@Temperature 212 °F
Poissons Ratio 0.30
0.30
RT
Shear Modulus 77.0 GPa
11200 ksi
calculated
Impact Test >= 60.0 J
>= 44.3 ft-lb
Hot rolled plate/Cold rolled strip/sheet, 10x10mm test pieces; EN 10045-1
Thermal Properties Metric English Comments
CTE, linear 16.0 µm/m-°C

@Temperature 100 °C
 8.89 µin/in-°F

@Temperature 212 °F
17.5 µm/m-°C

@Temperature 400 °C
 9.72 µin/in-°F

@Temperature 752 °F
Specific Heat Capacity 0.500 J/g-°C
0.120 BTU/lb-°F
RT
Thermal Conductivity 15.0 W/m-K
104 BTU-in/hr-ft²-°F
RT
20.0 W/m-K

@Temperature 400 °C
 139 BTU-in/hr-ft²-°F

@Temperature 752 °F
Component Elements Properties Metric English Comments
Carbon, C 0.020 %
0.020 %
Chromium, Cr 17.2 %
17.2 %
Iron, Fe 70.24 %
70.24 %
Molybdenum, Mo 2.1 %
2.1 %
Nickel, Ni 10.3 %
10.3 %
Nitrogen, N 0.14 %
0.14 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000750 ohm-cm
0.0000750 ohm-cm
RT