Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | ASTM D638 |
NCMT NanoPAC™ S206 High Performance Polypropylene Nanocomposite Characteristics: High stiffness Supplementary of ABS Good impact resistant Less shrinkage Good thermal conductivity Applications: Toys Industry AutomobileInformation provided by Nano Composite Mater.. |
|||
Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | ISO 527 |
Premix Thermoplastics PRE-ELEC® PP 1395 PRE-ELEC PP 1395 is a dissipative thermoplastic compound based on polypropylene. The electrical dissipation is achieved by using special conductive carbon black. In addition to stable surface resist.. |
|||
Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | |
3M Dyneon™ Fluorel™ FC-2121 Fluoroelastomer VF2 + HFP Dipolymer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Incorporated cure polymer, 65.9%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, and 4% Ca(OH)2. Excellent processability. Suggested .. |
|||
Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | |
3M Dyneon™ Fluorel™ FE-5622Q Fluoroelastomer VF2 + HFP Dipolymer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Incorporated cure polymer, 65.9%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, and 4% Ca(OH)2. The FE series grades are Dyneon's cle.. |
|||
Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | |
3M Dyneon™ Fluorel™ FE-5642Q Fluoroelastomer VF2 + HFP Dipolymer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Incorporated cure polymer, 65.9%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, and 4% Ca(OH)2. The FE series grades are Dyneon's cle.. |
|||
Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | |
3M Dyneon™ Fluorel II™ FX-11900 Fluoroelastomer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Incorporated cure polymer, 59%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, and 4% Ca(OH)2. Excellent processability. Good metal a.. |
|||
Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | ASTM D638 |
ExxonMobil Escorene® LD-612 EVA Injection Molding Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A 5.8% vinyl acetate copolymer resin designed for molding and extrusion applications requiring low temperatures, flexibility and toughness. This re.. |
|||
Tensile Strength, Ultimate | 16.0 MPa @Thickness 2.00 mm |
2320 psi @Thickness 0.0787 in |
ASTM D4894 |
3M Dyneon™ TFM™ 4105 Modified PTFE, 25% Glass Fiber Filled
(discontinued **) Type II PTFE. Applications include valve seats, bearings, seals/gaskets, moldings, piston rings.Data provided by Dyneon. |
|||
Tensile Strength, Ultimate | 16.0 MPa @Thickness 2.00 mm |
2320 psi @Thickness 0.0787 in |
ASTM D4894 |
3M Dyneon™ TF 4215 PTFE 25% Electrocarbon Filled
(discontinued **) Applications include bearings, seals/gaskets, packings, piston rings.Data provided by Dyneon. |
|||
Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | ASTM D638 |
ITW Plexus Plexusâ„¢ 3940 Methacrylate Adhesive An adhesive with versatile substrate and application capabilities for a wide range of industrial product assembly applications.Fast tacking, low pressure sprayable adhesive with long bonding range, .. |
|||
Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | |
Momentive Performance Materials TSE392 Translucent Adhesive Sealant, Thixotropic Paste One-part totally non-corrosive alkoxy cure. Alkoxy cure silicones are neutral cure materials that offer exceptional adhesion and are non-corrosive to most metals. Typical uses: Non-corrosive adhes.. |
|||
Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 301 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 342 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 342 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 342 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 301 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 301 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 342 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | GB/T 528 |
Chengdu Polyster 9500 General Grade TPV Information provided by Chengdu Polyster Co., Ltd. |
|||
Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | ASTM D638/D412 |
Covestro Bayflex® 110 RIM-LITE Polyurethane Elastomeric RIM, 13% Mineral Filled, MDI-based 2-Component Liquid System Contains 10% calcium silicate and 3% glass microspheres.0.15 in. thickness. RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, .. |
|||
Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | JIS 6251 (Dumbbells) |
DuPont Performance Polymers Kalrez® 8002 FFKM Perfluoroelastomer Kalrez® 8002 is a specialty compound targeted specifically for select semiconductor plasma and gas deposition applications. This clear, unfilled compound offers very low particle generation in oxyg.. |
|||
Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | ISO 527-1/-2 |
DSM Arnitel® EL250 TPC-ET Injection Molding |
|||
Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | Die C (35 min / 145°C); ASTM D412 |
Dow SE BR-1220L Stereospecific high cis-1,4 Polybutadiene (BR) SE BR-1220L is manufactured by a solution process using cobalt catalyst which produces polymers with a very light color and low ash content. A non-staining stabilizer is added during the production.. |
|||
Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 342 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | ASTM D638 |
ExxonMobil Escorene® LD-730 High EVA Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A high vinyl acetate copolymer with a low melting temperature and excellent strength properties and toughness.Applications: Injection molding; Foams.. |
|||
Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | ASTM D638 |
Huntsman PE1403 EVA Film Extrusion
(discontinued **) 4% Vinyl Acetate EVA Copolymer, DMF listed and FDA compliantFeatures: High clarity film with good toughness and flexibility at low temperatures.Applications: Film extrusion: frozen food and general .. |
|||
Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | ASTM D638 |
LyondellBasell Astryn 65F5-4 Polypropylene Homopolymer, 40% Calcium Carbonate Key Features: conventional melt flow, high modulus, mineral-filled polypropylene homopolymer, high stiffness, excellent chemical resistance, good surface qualityApplications: automotive components, .. |
|||
Tensile Strength, Ultimate | 16.0 - 67.0 MPa | 2320 - 9720 psi | Average value: 42.9 MPa Grade Count:7 |
Overview of materials for ABS/Polyurethane Alloy This property data is a summary of similar materials in the MatWeb database for the category "ABS/Polyurethane Alloy". Each property range of values reported is minimum and maximum values of appropr.. |