Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 12.0 MPa | 1740 psi | ISO 527 |
Premix Thermoplastics PRE-ELEC® PE 1294 PRE-ELEC PE 1294 is a conductive thermoplastic compound based on PE-HD. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC PE 129.. |
|||
Tensile Strength, Ultimate | 12.0 MPa | 1740 psi | |
3M Dyneon™ Fluorel™ FC-2145 Fluoroelastomer VF2 + HFP Dipolymer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Non-incorporated cure polymer, 65.9%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, 4% Ca(OH)2, 1.4% Dihydroxy Crosslinker, 0.4% Phosp.. |
|||
Tensile Strength, Ultimate | 12.0 - 85.0 MPa @Temperature 60.0 - 150 °C |
1740 - 12300 psi @Temperature 140 - 302 °F |
Average value: 41.5 MPa Grade Count:3 |
Overview of materials for Polybutylene Terephthalate (PBT), Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Flame Retardant". Each property range of values reported is minimum an.. |
|||
Tensile Strength, Ultimate | 12.0 MPa | 1740 psi | 500 mm/min (20 in./min.); ASTM D638, Type IV Specimen |
Eastman Voridian 800P Polyethylene
(discontinued **) General purpose low density formulation used for extrusion coating applications that require good stress resistance. This formula complies with FDA regulations at 21 CFR 177.1520(c)(2.1) for use i.. |
|||
Tensile Strength, Ultimate | 12.0 MPa | 1740 psi | ASTM D638 |
Huntsman PE1037 Film Extrusion Polyethylene
(discontinued **) Homopolymer, and FDA compliant.Features: Medium clarity packaging film and good draw down characteristics.Applications: Film extrusion: general purpose packaging and film applications.FDA Notes: Con.. |
|||
Tensile Strength, Ultimate | 12.0 MPa | 1740 psi | ASTM D638 |
Huntsman PE5020 Extrusion Coating Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: High draw down, low neck-in, excellent heat sealability, and excellent adhesion.Applications: Extrusion: coating grade and thin coatings.FDA Notes: Conforms t.. |
|||
Tensile Strength, Ultimate | 12.0 MPa | 1740 psi | ASTM D638 |
Huntsman PE5050 Extrusion Coating Polyethylene
(discontinued **) Homopolymer, Drug Master File listed product, and FDA compliant.Features: High draw down, low neck-in, excellent heat sealability, and excellent adhesion.Applications: Extrusion: coating grade and t.. |
|||
Tensile Strength, Ultimate | 12.0 MPa | 1740 psi | ASTM D638 |
ExxonMobil Escorene® LD-722 High EVA Film and Compounding Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A high vinyl acetate copolymer resin for specialty film and compounding applications. Outstanding heat sealability along with excellent strength pr.. |
|||
Tensile Strength, Ultimate | 12.0 MPa | 1740 psi | ASTM D638 |
Huntsman PE1903 EVA Film Extrusion
(discontinued **) 9% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Excellent toughness and flexibility at low temperatures, and good heat-seal response.Applications: Film extrusion: laminating film, controll.. |
|||
Tensile Strength, Ultimate | 12.0 - 37.0 MPa | 1740 - 5370 psi | Average value: 26.8 MPa Grade Count:212 |
Overview of materials for Polypropylene with 20% Talc Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 20% Talc Filler".Specific grades with primary filler content between 15% and 24% are .. |
|||
Tensile Strength, Ultimate | 12.0 MPa | 1740 psi | ASTM D638 |
ExxonMobil Iotek® 7520 Zinc Ionomer Molding/Extrusion Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A "soft" zinc ionomer with excellent flexibility and impact strength. This ionomer has outstanding adhesion to glass, metals and paper. IOTEK iono.. |
|||
Tensile Strength, Ultimate | 12.0 - 714 MPa | 1740 - 104000 psi | Average value: 124 MPa Grade Count:86 |
Overview of materials for Polyvinylidinefluoride (PVDF), Molded/Extruded This property data is a summary of similar materials in the MatWeb database for the category "Polyvinylidinefluoride (PVDF), Molded/Extruded". Each property range of values reported is minimum and m.. |
|||
Tensile Strength, Ultimate | 12.0 MPa @Thickness 2.00 mm |
1740 psi @Thickness 0.0787 in |
ASTM D4894 |
3M Dyneon™ TFM™ 4212 Modified PTFE, 10% Electrocarbon Filled
(discontinued **) Applications include bearings, seals/gaskets, packings, piston rings.Data provided by Dyneon. |
|||
Tensile Strength, Ultimate | 12.0 MPa | 1740 psi | ASTM D412 |
Multibase Multi-Flex® TPE A 3104-10 AGATE 5ES The material is based on Kraton G rubber. It has been engineered for single shot. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 12.0 MPa | 1740 psi | ASTM D638 |
LyondellBasell Hifaxâ„¢ CA199AC Thermoplastic Olefin Resin Key Features: low melt flow, medium low modulus, paintable thermoplastic olefin resin, excellent balance of properties, high toughness, good paintability, flexibleApplications: automotive air bag do.. |
|||
Tensile Strength, Ultimate | 12.0 MPa | 1740 psi | ASTM D638 |
Toyobo Pelprene™ P-70B Polyester TPE Key Feature: Pelprene P typePelprene™ can be processed into a wide variety of articles from ultra-small precision parts to sheets by injection, extrusion, and blow molding. The 'P' type is a block.. |
|||
Tensile Strength, Ultimate | 12.0 MPa | 1740 psi | ISO 527-1 |
Chengdu Polyster FH3303 Thermoplastic Polyether-ester Elastomer (TPEE) Blend of H3303 and self-made flame retardant material. Excellent flex resistance at low temperatures. Excellent flex-fatigue resistance. Applications requiring flexibility at low temperatures and fl.. |
|||
Tensile Strength, Ultimate | 12.0 MPa | 1740 psi | |
Dow DOWLEX™ IP-50 High Density Polyethylene DOWLEX® IP-50 resin is an improved processing high density polyethylene resin with controlled molecular weight distribution designed for thin wall food containers. This resin is recommended for flo.. |
|||
Tensile Strength, Ultimate | 12.0 - 24.0 MPa | 1740 - 3480 psi | |
ATG s.r.l. CSM Chlorosulphonated Polyethylene |
|||
Tensile Strength, Ultimate | 12.0 MPa @Temperature 250 °C |
1740 psi @Temperature 482 °F |
ASTM D638 |
Asahi Glass Fluon® P-805UP PFA Perfluoropolymer Fluon® PFA is a copolymer of tetrafluoroethylene (C2F4) and perfluoroalkoxyethylene, which has excellent chemical, electrical, mechanical and surface properties. PFA retains many inherent character.. |
|||
Tensile Strength, Ultimate | 12.0 MPa | 1740 psi | ASTM D638 |
Huntsman PE1076 Film Extrusion Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: Yields film with high clarity and excellent stiffness.Applications: Film extrusion: overwrap packaging.FDA Notes: Conforms to FDA regulation 21 CFR 177.1520 (.. |
|||
Tensile Strength, Ultimate | 12.0 - 37.2 MPa | 1740 - 5400 psi | Average value: 25.7 MPa Grade Count:47 |
Overview of materials for Ionomer, Molded This property data is a summary of similar materials in the MatWeb database for the category "Ionomer, Molded". Each property range of values reported is minimum and maximum values of appropriate Ma.. |
|||
Tensile Strength, Ultimate | 12.0 MPa | 1740 psi | ASTM D638 |
ExxonMobil Escorene® UL-7760 EVA Copolymer, Adhesive and Sealant Grade
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A 28% vinyl acetate copolymerApplications: Hot melt adhesives; Wax blends; Industrial sealants. |
|||
Tensile Strength, Ultimate | 12.0 MPa | 1740 psi | ASTM D638 |
Huntsman PE1345 EVA Film Extrusion
(discontinued **) 3.4% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Excellent balance of optical and strength, toughness and flexibility at low temperatures, and good heat seal characteristic.Applications: .. |
|||
Tensile Strength, Ultimate | 12.0 - 15.0 MPa | 1740 - 2180 psi | |
Dow Advanta® 3650 Specialty Elastomer
(discontinued **) Advanta® specialty elastomers provides good fluid resistance and better high temperature performance than nitrile or HNBR and lower cost than fluoroelastomers. Available in two grades. ASTM D2000.. |