Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 66.2 - 297 MPa | 9600 - 43100 psi | Average value: 234 MPa Grade Count:23 |
Overview of materials for Polyphenylene Sulfide (PPS) with 30% Carbon Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 30% Carbon Fiber Filler". Specific grades with carbon fiber content bet.. |
|||
Flexural Yield Strength | 66.2 - 278 MPa | 9600 - 40300 psi | Average value: 209 MPa Grade Count:57 |
Overview of materials for Polyphenylene Sulfide (PPS), Mineral/Glass-Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS), Mineral/Glass-Fiber Filled". Each property range of values reported is mini.. |
|||
Flexural Yield Strength | 66.2 MPa | 9600 psi | ASTM D790 |
Spartech Royalite R522 PVC Alloy Aircraft Grade Sheet Description: Aircraft Grade SheetInformation provided by Spartech. |
|||
Flexural Yield Strength | 66.2 MPa | 9600 psi | ASTM D790 |
Spartech Royalite R60 PVC/Acrylic Aircraft Grade Sheet Description: Aircraft Grade SheetInformation provided by Spartech. |
|||
Flexural Yield Strength | 66.2 MPa | 9600 psi | ASTM D790 |
Spartech SP-9020 Premium ABS Sheet Description: ABS SheetInformation provided by Spartech. |
|||
Flexural Yield Strength | 66.2 MPa | 9600 psi | ASTM D790 |
Techmer ES Plaslube® AC-80/TF/15 Acetal (Copolymer), 15% PTFE Plaslube polytetrafluoroethylene (PTFE) lubricated acetal copolymer grades offer additional wear and friction performance over neat acetal. Typical applications include bearings, slides and small g.. |
|||
Flexural Yield Strength | 66.2 MPa | 9600 psi | ASTM D790 |
Clariant PA131 Nylon 66, Highly Impact Modified Data provided by Clariant Masterbatches |
|||
Flexural Yield Strength | 66.2 MPa | 9600 psi | ASTM D790 |
Clariant PA131G2GN-91 Green Nylon 66, Highly Toughened Data provided by Clariant Masterbatches |
|||
Flexural Yield Strength | 66.2 MPa | 9600 psi | ASTM D790 |
Clariant Renol PA133 Nylon 66, Highly Impact Modified, Heat Stabilized, Lubricated Data provided by Clariant Masterbatches |
|||
Flexural Yield Strength | 66.2 MPa | 9600 psi | ASTM D790 |
Clariant Renol PA133GN-109 Nylon 66, High Impact, Heat Stabilized, Lubricated Data provided by Clariant Masterbatches |
|||
Flexural Yield Strength | 66.2 MPa @Thickness 6.40 mm |
9600 psi @Thickness 0.252 in |
ASTM D-790 |
Bhansali Engineering Abstron HR-60 ABS Heat Resistant High, Medium Impact Heat Resistant Grades with good flowInformation provided by Bhansali |
|||
Flexural Yield Strength | 66.2 MPa @Thickness 6.40 mm |
9600 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
Bhansali Engineering Abstron HR60N ABS Heat Resistant High ImpactInformation provided by Bhansali |
|||
Flexural Yield Strength | 66.2 MPa @Thickness 6.40 mm |
9600 psi @Thickness 0.252 in |
ASTM D-790 |
Bhansali Engineering Abstron IM-11G ABS Injection Molding Grade High Impact, High Rigidity, High Fatigue, Low Flow, PaintableInformation provided by Bhansali |
|||
Flexural Yield Strength | 66.2 MPa @Thickness 6.40 mm |
9600 psi @Thickness 0.252 in |
ASTM D-790 |
Bhansali Engineering Abstron HR-60 ABS Heat Resistant High, Medium Impact Heat Resistant Grades with good flowInformation provided by Bhansali |
|||
Flexural Yield Strength | 66.2 MPa @Thickness 6.40 mm |
9600 psi @Thickness 0.252 in |
ASTM D-790 |
Bhansali Engineering Abstron IM-11G ABS Injection Molding Grade High Impact, High Rigidity, High Fatigue, Low Flow, PaintableInformation provided by Bhansali |
|||
Flexural Yield Strength | 66.2 MPa @Thickness 6.40 mm |
9600 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
Bhansali Engineering Abstron HR60N ABS Heat Resistant High ImpactInformation provided by Bhansali |