- Polymer Property : Flexural Yield Strength = 25600 psi
Polymer Property : Flexural Yield Strength = 25600 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Yield Strength | 177 MPa @Thickness 6.40 mm |
25600 psi @Thickness 0.252 in |
1.3mm/min; ASTM D790 |
| LG Chemical LUCON SP9306FL sPS+MF Description Injection Molding Grade, sPS+MF, Low Thermal Conductivity, Chemical Resistance, High Heat ResistanceApplication: Electrical or Electronic Parts CAS No. 9003-53-6, 65997-17-3, 68928-70-1 .. |
|||
| Flexural Yield Strength | 177 MPa | 25600 psi | DIN 53455; ASTM D790 |
| Kolon KOPA® KN133G33HIBL G/F Reinforced Nylon 6 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubr.. |
|||
| Flexural Yield Strength | 177 MPa | 25600 psi | DIN 53455; ASTM D790 |
| Kolon KOPEL® KP3355 General Purpose TPE Resin KOPEL® is a thermoplastic polyester elastomer which is a new engineering rubber having combined properties of conventional rubber and thermoplastic. Its flexibility and elastic recovery are very.. |
|||
| Flexural Yield Strength | 177 MPa @Thickness 3.20 mm |
25600 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| LG Chemical Lupox® GP2300G PBT+GF30% Description: Injection Molding, PBT+GF30%, HCFC ResistanceApplication: E&E (Muffler of Refrigerator)CAS No. 65997-17-3 and 24968-12-5Information provided by LG Chemical |
|||
| Flexural Yield Strength | 177 MPa | 25600 psi | ASTM D570 |
| LG Chemical Lupox® PBT-GP-2300 30% GFR PBT Information provided by US distributor Polymer Technology and Services, LLC (PTS). |
|||
| Flexural Yield Strength | 177 MPa | 25600 psi | ASTM D570 |
| LG Chemical Lupox® PBT-LW5303 30% Glass Filled Low Warp PBT Low Warpage. Information provided by US distributor Polymer Technology and Services, LLC (PTS). |
|||
| Flexural Yield Strength | 177 MPa | 25600 psi | ASTM D570 |
| LG Chemical Lupox® PBT-LW5303F 30% Glass Filled Low Warp Flame Retardant PBT Information provided by US distributor Polymer Technology and Services, LLC (PTS). |
|||
| Flexural Yield Strength | 177 MPa @Thickness 3.20 mm |
25600 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| LG Chemical LUPOY GP2300 PC+GF30%, Heat Resistance Description: Injection Molding, PC+GF30%, General Purpose, Heat ResistanceApplication: IT/OA, E&E Housing and Components, Automotive (Interior)CAS: 103598-77-2 and 65997-17-3Information provided by .. |
|||
| Flexural Yield Strength | 177 MPa @Thickness 3.20 mm |
25600 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| LG Chemical LUPOY SC2302 PC+GF30%, High Impact Description: Injection Molding, PC+GF30%, Good Toughness, Good Impact, Chemical ResistanceApplication: Mobile Phone HousingCAS: 103598-77-2 and 65997-17-3Information provided by LG Chemical |
|||
| Flexural Yield Strength | 177 MPa | 25600 psi | DIN 53455; ASTM D790 |
| Kolon KOPA® KN163G30 G/F Reinforced Nylon 6 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubr.. |
|||
| Flexural Yield Strength | 177 MPa @Thickness 3.20 mm |
25600 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| LG Chemical LUPOY GN2301F PC+GF30%, Halogen Free, Flame Retardant, Heat Resistance Description: Injection Molding, PC+GF30%, Halogen Free Flame Retardant, Heat ResistanceApplication: IT/OA, Electric & Electronic Housing and ComponentsCAS: 103598-77-2 and 65997-17-3Information prov.. |
|||
| Flexural Yield Strength | 177 MPa @Thickness 3.20 mm |
25600 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| LG Chemical LUSEP SP2300 SPS+GF30%, General Purpose Feature: Injection Molding, sPS+GF30%, General PurposeApplication: Pump Units, Pick-up Lends Holder, etc.CAS No. 9003-53-6 and 65997-17-3Information provided by LG Chemical |
|||
| Flexural Yield Strength | 177 MPa | 25600 psi | ASTM D790 |
| PlastxWorld CEVIAN® A5626 30% GF PA/ABS Alloy, DAM Property data is for dry as molded (DAM) samples.These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc. |
|||
| Flexural Yield Strength | 177 MPa | 25600 psi | ASTM D790 |
| Cheng Yu Plastic ML3430 PC, 30% Glass Fiber |
|||
| Flexural Yield Strength | 177 MPa | 25600 psi | ASTM D790 |
| Cheng Yu Plastic E2345 Flame Retardant PET, 45% Glass Fiber |
|||
| Flexural Yield Strength | 177 MPa | 25600 psi | ASTM D790 |
| Cheng Yu Plastic A706G15 SAN, 15% Glass Fiber |
|||
| Flexural Yield Strength | 177 MPa | 25600 psi | ASTM D790 |
| Cheng Yu Plastic FV30G20 POM, 20% Glass Fiber |
|||
| Flexural Yield Strength | 177 - 300 MPa | 25600 - 43500 psi | Average value: 258 MPa Grade Count:15 |
| Overview of materials for Polyethylene Terephthalate (PET), 50% Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), 50% Glass Reinforced". Specific grades with glass content between 45% .. |
|||
| Flexural Yield Strength | 176.5 MPa | 25600 psi | ASTM D790 |
| Cheng Yu Plastic ML1230 PC/PTFE, 30% Glass |
|||