Polymer Property : Flexural Yield Strength = 89.0 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Yield Strength | 89.0 MPa | 12900 psi | ASTM D790 |
| NYCOA 2062 Copolymer Nylon 6/66 FDA approved extrusion grade for film.Information provided by NYCOA, Inc. |
|||
| Flexural Yield Strength | 89.0 MPa | 12900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| SABIC Innovative Plastics Cycoloy® CY9650 PC+ABS PC+ABS, High Impact and High Flow, ductility at low temperature, excellent properties retention after Hydrolytic and Heat AgingThis data was supplied by SABIC-IP for the Americas region. |
|||
| Flexural Yield Strength | 89.0 MPa | 12900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Cycoloy® XCY630 PC+ABS (Asia Pacific) PC+ ABS Automotive applications, High Impact and High Flow, ductility at low temperature, excellent properties retention after Hydrolytic and Heat Aging |
|||
| Flexural Yield Strength | 89.0 MPa | 12900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| SABIC Innovative Plastics Cycoloy® XCY630 PC+ABS (Europe-Africa-Middle East) PC+ ABS Automotive applications, High Impact and High Flow, ductility at low temperature, excellent properties retention after Hydrolytic and Heat AgingThis data was supplied by SABIC-IP for the Eur.. |
|||
| Flexural Yield Strength | 89.0 MPa | 12900 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Lexan® EXL1112T PC Copolymer Lexan* EXL1112T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding (IM) grade. This resin offers good low temperature (-20 C) ductility in combination with high flow char.. |
|||
| Flexural Yield Strength | 89.0 MPa | 12900 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Lexan® EXL1132T PC Copolymer Lexan* EXL1132T polycarbonate (PC) siloxane copolymer resin is a UV stabilized transparent injection molding (IM) grade with extra release properties. This resin offers good low temperature (-20 C) .. |
|||
| Flexural Yield Strength | 89.0 MPa | 12900 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Lexan® EXL1132T PC Copolymer (Asia Pacific) Lexan* EXL1132T polycarbonate (PC) siloxane copolymer resin is a UV stabilized transparent injection molding (IM) grade with extra release properties. This resin offers good low temperature (-20 C) .. |
|||
| Flexural Yield Strength | 89.0 MPa | 12900 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Lexan® EXL1132T PC Copolymer (Europe-Africa-Middle East) Lexan* EXL1132T polycarbonate (PC) siloxane copolymer resin is a UV stabilized transparent injection molding (IM) grade with extra release properties. This resin offers good low temperature (-20 C) .. |
|||
| Flexural Yield Strength | 89.0 MPa | 12900 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Lexan® EXL1162T PC Copolymer (Europe-Africa-Middle East) Lexan* EXL1162T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding (IM) grade with extra release properties. This resin offers good low temperature (-20 C) ductility in c.. |
|||
| Flexural Yield Strength | 89.0 MPa | 12900 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Lexan® EXL1192T PC Copolymer Lexan* EXL1192T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding (IM) grade with extra release properties for food contact applications. This resin offers good low temp.. |
|||
| Flexural Yield Strength | 89.0 MPa | 12900 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Lexan® EXL1192T PC Copolymer (Asia Pacific) Lexan* EXL1192T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding (IM) grade with extra release properties for food contact applications. This resin offers good low temp.. |
|||
| Flexural Yield Strength | 89.0 MPa | 12900 psi | 6.4 mm; ASTM D790 |
| SABIC Innovative Plastics Lexan® FL903 PC Various weight reductions at 0.250"" (6.35 mm). High heat/creep resistance, excellent impact, flexural strength/rigidity. UV-stabilized. |
|||
| Flexural Yield Strength | 89.0 MPa @Thickness 3.17 mm |
12900 psi @Thickness 0.125 in |
ASTM D790 |
| PTS PCA-2010NH Non-Bromine, Non-Chlorine, Flame Retardant PC/ABS Alloy This is a non-halogenated flame retardant grade. Information provided by Polymer Technology and Services, LLC (PTS). |
|||
| Flexural Yield Strength | 89.0 MPa | 12900 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Lexan® FXD1414T PC Copolymer (Asia Pacific) PC-siloxane copolymer in special light diffusion colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color package may affect performance. |
|||
| Flexural Yield Strength | 89.0 MPa | 12900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| SABIC Innovative Plastics Lexan® FXD1433T PC Copolymer Clear PC-siloxane copolymer with excellent processability in special light diffusion colors. Medium flow, UV stabilized. Improved toughness compared to standard PC in same color. Color package may .. |
|||
| Flexural Yield Strength | 89.0 MPa | 12900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Lexan® ML7682 PC Copolymer (Asia Pacific) Lexan ML7682 resin is a flame retardant polycarbonate blend featuring high flow, good processability, good impact, good heat resistance, and UV stability. It is of non-chlorine and non-bromine flame.. |
|||
| Flexural Yield Strength | 89.0 MPa | 12900 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP DL0039E PC (Europe-Africa-Middle East) LNP* LUBRICOMP* DL0039E is a compound based on Polycarbonate resin containing PTFE, Flame retardant. Added features include: Easy Molding, Internally Lubricated, Flame retardant. |
|||
| Flexural Yield Strength | 89.0 MPa @Thickness 3.17 mm |
12900 psi @Thickness 0.125 in |
ASTM D790 |
| PTS PCA-2010NHV Non-Bromine, Non-Chlorine, Flame Retardant UV PC/ABS Alloy This is a non-halogenated flame retardant, UV stabilized grade. Information provided by Polymer Technology and Services, LLC (PTS). |
|||
| Flexural Yield Strength | 89.0 MPa | 12900 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Lexan® HFD1014 PC Copolymer 7 MFR LEXAN HFD Copolymer |
|||
| Flexural Yield Strength | 89.0 - 320 MPa | 12900 - 46400 psi | Average value: 212 MPa Grade Count:106 |
| Overview of materials for Nylon 66, Glass Fiber/PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Glass Fiber/PTFE Filled". Each property range of values reported is minimum and maximum values.. |
|||
| Flexural Yield Strength | 89.0 MPa | 12900 psi | |
| Aardvark Polymers AARTEL® 820UV Acetal Copolymer Rotational Molding Resin Aartel 820UV is a natural acetal copolymer with added UV stabilizers.Aartel 820UV is a low viscosity resin with excellent flow characteristics.Aartel 820UV is available in natural white and may be p.. |
|||
| Flexural Yield Strength | 89.0 MPa | 12900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| SABIC Innovative Plastics Noryl PX6021 PPE+PS (Asia Pacific) Low heat, flame retardant PPO/HIPS alloy.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Flexural Yield Strength | 89.0 MPa | 12900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Valox® HX215HP PBT High Flow, Unreinforced, Polybutylene Terephthalate (PBT). For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food conta.. |
|||
| Flexural Yield Strength | 89.0 MPa | 12900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Xenoy® ENH2900 PBT+PC (Asia Pacific) Xenoy* ENH2900 is a Non-Braominated, Non Chlorinated flame retarded PC/PBT resin with good flow, high impact and excellent chemical resistance. It was designed quite suitable for E&E housing applic.. |
|||
| Flexural Yield Strength | 89.0 MPa | 12900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Xenoy® IQNH2900 PBT+PC Import Grade. UL94 V-0 Performance with Non-Brominated Flame Retardant. PCR% is up to 12% by using Valox iQ* resin. |
|||
| Flexural Yield Strength | 89.0 MPa | 12900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| SABIC Innovative Plastics NORYL GTX GTX902 PPE+PS+PA Unreinforced. Excellent chemical resistance and paintability. 312F (155C) HDT. |
|||
| Flexural Yield Strength | 89.0 MPa | 12900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics NORYL PN275F PPE+PS PPE+PS with low mineral loading. High heat, platable applications. NSF approved for water contact applications. |
|||
| Flexural Yield Strength | 89.0 MPa | 12900 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP STAT-KON KEL22A Acetal Homopolymer (Europe-Africa-Middle East) LNP* LUBRICOMP* KEL22A is a compound based on Acetal Homopolymer resin containing Carbon Fiber, PTFE. Added features include: Electrically Conductive, Internally Lubricated. |
|||
| Flexural Yield Strength | 89.0 MPa | 12900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Valox® 745 PBT (Asia Pacific) 30% mineral reinforced polyester improved toughness and low warpage. Typical applications are telephone ringer frames and card racks. |
|||
| Flexural Yield Strength | 89.0 MPa | 12900 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics NORYL FP6130 PPE+PS (Europe-Africa-Middle East) Noryl* FP6130 is an unfilled, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and high flow , this resin also uses non-chlorinated, non-brominated FR a.. |
|||