Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Break, TD | 25.0 MPa | 3630 psi | ISO 527-3 |
Polimeri Europa Clearflex® FH 50 Linear Medium Density Polyethylene Clearflex FH 50 is a linear medium density polyethylene, with antioxidants, suitable for blown film extrusion.Films manufactured with Clearflex FH 50 are characterized by a good balance between toug.. |
|||
Film Tensile Strength at Break, TD | 25.0 MPa | 3630 psi | ASTM D882 |
NOVA Chemicals Sclair® FG220-A Octene LLDPE Film Resin Features: Exceptional toughnessLow gel level Applications: Cast stretch wrapNettingCo-extrusion and laminationInformation provided by Nova Chemicals |
|||
Film Tensile Strength at Break, TD | 25.0 MPa | 3630 psi | ASTM D882 |
NOVA Chemicals Surpass® FPs317-A Octene sLLDPE Film Resin Features: Exceptional puncture resistanceVery good tear propertiesLow gel levelExcellent optical properties Excellent elongation characteristics Easy to process, no drying required Applications: Cas.. |
|||
Film Tensile Strength at Break, TD | 25.0 MPa | 3630 psi | ISO 527-3 |
Polimeri Europa Flexirene® CL 10 Butene Copolymer Linear Low Density Polyethylene Flexirene CL 10 is a butene copolymer linear low density polyethylene (C4-LLDPE), with antioxidants, suitable for cast extrusion of thin film with high optical properties.Main Applications: Flexire.. |
|||
Film Tensile Strength at Break, TD | 25.0 MPa | 3630 psi | ASTM D 882 |
NOVA Chemicals Novapol® PF-0218-E Butene Copolymer LLDPE Film Resin PF-0218-E complies with the U.S. FDA specifications for olefin polymers and may be used in the U.S. as an article or component of an article intended for use in contact with food, without temperatur.. |
|||
Film Tensile Strength at Break, TD | 25.0 MPa | 3630 psi | ASTM D882 |
Huntsman PE1651 EVA Film Extrusion
(discontinued **) 6.5% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Yields film with outstanding low temperature strength, excellent clarity, and good heat seal.Applications: Film extrusion: ice bags, liqui.. |
|||
Film Tensile Strength at Break, TD | 25.0 MPa | 3630 psi | ISO R527-1 |
Iran Petrochemical (PCC) 2501TN00 Low Density Polyethylene LDPE 2501TN00 Hygienic Film It is used in diaper film, lamination film and in applications where low blocking behavior without the help of additives is required.Information provided by Iran Petroch.. |
|||
Film Tensile Strength at Break, TD | 25.0 - 45.0 MPa | 3630 - 6530 psi | ISO 527-3 |
Borealis BD712CF Polypropylene Copolymer BD712CF is a heterophasic copolymer. This grade is suitable for the manufacturing of unoriented films on cast and tubular quench film lines. Applications: BD712CF is recommended for food packaging.. |
|||
Film Tensile Strength at Break, TD | 25.0 - 35.0 MPa | 3630 - 5080 psi | ISO 527-3 |
Borealis Borclear™ RB709CF Polypropylene Ethylene Copolymer Borclear™ RB709CF is a propylene -ethylene copolymer. This grade is suitable for the manufacturing of unoriented film on blown film lines. Applications: Borclear™ RB709CF is recommended for seal.. |
|||
Film Tensile Strength at Break, TD | 25.0 - 45.0 MPa | 3630 - 6530 psi | ISO 527-3 |
Borealis BorPure™ RD234CF Polypropylene Random Copolymer BorPure™ RD234CF is a random copolymer. This grade is suitable for the manufacturing of unoriented films on chill roll processes. Applications: RD234CF is recommended for food packaging, stationa.. |
|||
Film Tensile Strength at Break, TD | 25.0 - 45.0 MPa | 3630 - 6530 psi | ISO 527-3 |
Borealis BorPURE™ RD266CF Polypropylene Random Copolymer BorPure™ RD266CF is a random copolymer. This grade is suitable for the manufacturing of unoriented films on chill roll processes. Applications: BorPure™ RD266CF is recommended for
food packaging.. |
|||
Film Tensile Strength at Break, TD | 25.0 - 45.0 MPa | 3630 - 6530 psi | ISO 527-3 |
Borealis Borseal™ RE239CF Polypropylene Copolymer Borseal™ RE239CF is a random copolymer. This grade is suitable for the manufacturing of unoriented films for metallization. Applications: Borseal™ RE239CF is recommended for food packaging, high.. |
|||
Film Tensile Strength at Break, TD | 25.0 MPa | 3630 psi | ISO 527-3 |
Borealis Borseal™ RE939CF Polypropylene Copolymer Borseal™ RE939CF is a random copolymer. This grade is suitable for the manufacturing of unoriented films on chill roll processes. Applications: Borseal™ RE939CF is designed for: Food packaging,.. |
|||
Film Tensile Strength at Break, TD | 25.0 - 45.0 MPa | 3630 - 6530 psi | ISO 527-3 |
Borealis Borsoft™ SD233CF High Impact Polypropylene Random Heterophasic Copolymer for Cast Film Borsoft SD233CF is a very soft random heterophasic copolymer, suitable for use on chill roll process. The product combines unique softness with outstanding mechanical properties making it the ideal.. |
|||
Film Tensile Strength at Break, TD | 25.0 - 45.0 MPa | 3630 - 6530 psi | ISO 527-3 |
Borealis HD204CF Polypropylene HD204CF is a homopolymer film resin, suitable for the manufacturing of unoriented film on chill roll process. Applications: HD204CF is recommended for medical applications, inner layer in co extru.. |
|||
Film Tensile Strength at Break, TD | 25.0 - 45.0 MPa | 3630 - 6530 psi | ISO 527-3 |
Borealis HD234CF Polypropylene HD234CF is a homopolymer film resin, suitable for the manufacturing of unoriented film on chill roll process. Applications: HD234CF is recommended for food packaging, lamination films, stationery f.. |
|||
Film Tensile Strength at Break, TD | 25.0 MPa | 3630 psi | ISO 527-3 |
Borealis Himod™ FT3280 LDPE for Film Himod FT3280 is a tubular, low-density polyethylene grade for the production of packaging films. Compared to standard LDPE grades, the Himod products provide a combination of higher stiffness and i.. |
|||
Film Tensile Strength at Break, TD | 25.0 - 45.0 MPa | 3630 - 6530 psi | ISO 527-3 |
Borealis RD204CF Polypropylene Random Copolymer RD204CF is a random copolymer. This grade is suitable for the manufacturing of unoriented films on chill roll processes. Applications: RD204CF is recommended for blending, food packaging, high qua.. |
|||
Film Tensile Strength at Break, TD | 25.0 - 45.0 MPa | 3630 - 6530 psi | ISO 527-3 |
Borealis RD734CF Polypropylene Random Copolymer RD734CF is a random copolymer. This grade is suitable for the manufacturing of unoriented films on chill roll processes. Applications: RD734CF is recommended for food packaging, high quality stati.. |
|||
Film Tensile Strength at Break, TD | 25.0 - 45.0 MPa | 3630 - 6530 psi | ISO 527-3 |
Borealis BorPURE™ RD208CF Polypropylene Random Copolymer BorPure™ RD208CF is a random copolymer. This grade is suitable for the manufacturing of unoriented films on chill roll processes. This grade is suitable for the manufacturing of unoriented films o.. |
|||
Film Tensile Strength at Break, TD | 25.0 - 45.0 MPa | 3630 - 6530 psi | ISO 527-3 |
Borealis RD735CF Polypropylene Random Copolymer RD735CF is a random copolymer. This grade is suitable for the manufacturing of unoriented films on chill roll processes. Applications: RD735CF is recommended for food packaging, textile packaging .. |
|||
Film Tensile Strength at Break, TD | 25.0 MPa | 3630 psi | ASTM-D882 |
Braskem Flexus® 9211 LLDPE Blow Film Extrusion Polyethylene Copolymer Braskem Flexus 9211 is a LLDPE hexene copolymer produced through a metallocene catalyst, which presents excellent impact and puncture strength beyond a differential sealing performance compared with.. |
|||
Film Tensile Strength at Break, TD | 25.0 MPa | 3630 psi | ASTM-D882 |
Braskem TX7001 LDPE Blown Film Extrusion Polyethylene TX7001 is a low-density polyethylene (LDPE) with high molecular weight designed to satisfy those applications that require high mechanical strength and environmental stress cracking resistance (ESCR.. |
|||
Film Tensile Strength at Break, TD | 25.0 MPa | 3630 psi | ASTM D882 |
Braskem EB 861/51 LDPE Blown Film Extrusion Polyethylene 38µm film gauge, obtained in 75mm extruder, die gap 1.0mm, output 1.75 kg/h-cm with 2:1 BUR. Applications: Coextruded films; Shrink films for pallets; general purpose. Information provided by Brask.. |
|||
Film Tensile Strength at Break, TD | 25.0 MPa | 3620 psi | ASTM D882 |
Formosa Plastics Formolene® L62005E2T1 Film (Hexene Grade) LLDPE
(discontinued **) Hexene Copolymer (High slip and antiblock, with processing aid)Applications: Blown film, high strength applicationsBlown film, high strength applicationsMeets all requirements of the U.S. Food and D.. |
|||
Film Tensile Strength at Break, TD | 25.0 MPa | 3630 psi | ASTM D882 |
Iran Petrochemical (PCC) Arak 0640AA LLDPE
(discontinued **) Information provided by Iran Petrochemical Commercial Co. |
|||
Film Tensile Strength at Break, TD | 25.0 MPa | 3630 psi | ISO 1184 |
Iran Petrochemical (PCC) Tabriz 0640AA LLDPE
(discontinued **) Information provided by Iran Petrochemical Commercial Co. |
|||
Film Tensile Strength at Break, TD | 25.0 - 44.0 MPa | 3630 - 6380 psi | Average value: 34.7 MPa Grade Count:16 |
Overview of materials for Linear Medium Density Polyethylene (LMDPE), Film This property data is a summary of similar materials in the MatWeb database for the category "Linear Medium Density Polyethylene (LMDPE), Film". Each property range of values reported is minimum and.. |
|||
Film Tensile Strength at Break, TD | 25.0 MPa | 3630 psi | ASTM D882 |
Huntsman PE1201 EVA Film Extrusion
(discontinued **) 2% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Good optical, medium impact strength, and good processability.Applications: Film extrusion: heavy duty packaging.FDA Notes: Conforms to FDA .. |
|||
Film Tensile Strength at Break, TD | 25.0 MPa | 3630 psi | ASTM D882 |
Huntsman PE1451 EVA Film Extrusion
(discontinued **) 4.5% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Excellent balance of optical and strength, toughness and flexibility at low temperatures, and good heat seal characteristic.Applications: .. |