Polimeri Europa Clearflex® FH 50 Linear Medium Density Polyethylene

Category Polymer , Thermoplastic , Polyethylene (PE) , MDPE , Linear Medium Density Polyethylene (LMDPE), Film
Manufacturer Polimeri Europa (Former EniChem)
Trade Name Clearflex®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa Clearflex® FH 50 Linear Medium Density Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Clearflex FH 50 is a linear medium density polyethylene, with antioxidants, suitable for blown film extrusion.Films manufactured with Clearflex FH 50 are characterized by a good balance between toughness and rigidity, have high temperature resistance together with optimum sealing properties.Main Applications: Due to its mechanical properties and excellent processability, Clearflex FH 50 is recommended in coextrusion for the production of film having good rigidity. Moreover, its very low gel content makes the resin ideal for lamination.Information provided by Polimeri Europa.
Physical Properties Metric English Comments
Specific Gravity 0.936 g/cc
0.936 g/cc
ISO 1183
Thickness 10.0 - 50.0 microns
0.394 - 1.97 mil
Recommended
Melt Flow 1.8 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.8 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 16.0 MPa
2320 psi
ISO 527-3
Film Tensile Strength at Yield, TD 18.0 MPa
2610 psi
ISO 527-3
Film Elongation at Break, MD 650 %
650 %
ISO 527-3
Film Elongation at Break, TD 750 %
750 %
ISO 527-3
Coefficient of Friction, Dynamic >= 0.50
>= 0.50
ISO 8295
Elmendorf Tear Strength, MD 0.8152 g/micron
20.71 g/mil
ISO 6383-2
Elmendorf Tear Strength, TD 10.19 g/micron
258.8 g/mil
ISO 6383-2
Dart Drop Test 50.0 g
0.110 lb
F50; ISO 7765-1
Film Tensile Strength at Break, MD 35.0 MPa
5080 psi
ISO 527-3
Film Tensile Strength at Break, TD 25.0 MPa
3630 psi
ISO 527-3
1% Secant Modulus, MD 450 MPa
65300 psi
ISO 527-3
1% Secant Modulus, TD 500 MPa
72500 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 128 °C
262 °F
Internal method
Vicat Softening Point 117 °C

@Load 1.00 kg
243 °F

@Load 2.20 lb
ISO 306/A
Brittleness Temperature <= -70.0 °C
<= -94.0 °F
ASTM D746
Optical Properties Metric English Comments
Haze 18 %
18 %
ISO 14782
Gloss 55 %
55 %
45°; ASTM D2457
Transmission, Visible 90 %
90 %
clear; thickness not quantified