- NOVA Chemicals Sclair® FG220-A Octene LLDPE Film Resin
NOVA Chemicals Sclair® FG220-A Octene LLDPE Film Resin
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade |
| Manufacturer | NOVA Chemicals |
| Trade Name | Sclair® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NOVA Chemicals Sclair® FG220-A Octene LLDPE Film Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Exceptional toughnessLow gel level Applications: Cast stretch wrapNettingCo-extrusion and laminationInformation provided by Nova Chemicals
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ASTM D792 |
| Thickness | 20.0 microns | 0.787 mil | |
| Melt Flow | 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.3 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 8.89 MPa | 1290 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 8.41 MPa | 1220 psi | ASTM D882 |
| Film Elongation at Yield, MD | 435 % | 435 % | ASTM D638 |
| Film Elongation at Yield, TD | 760 % | 760 % | ASTM D882 |
| Puncture Energy | 1.60 J | 1.18 ft-lb | Low Friction Puncture |
| Elmendorf Tear Strength MD | 290 g | 290 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 650 g | 650 g | ASTM D1922 |
| Dart Drop Test | 190 g | 0.419 lb | ASTM D1709/A |
| Film Tensile Strength at Break, MD | 33.0 MPa | 4790 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 25.0 MPa | 3630 psi | ASTM D882 |
| 1% Secant Modulus, MD | 140.0 MPa | 20310 psi | ASTM D882 |
| 1% Secant Modulus, TD | 160.0 MPa | 23210 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 2.0 % | 2.0 % | ASTM D1003 |
| Gloss | 85 % | 85 % | at 45°; ASTM D2457 |
Users viewing this material also viewed the following:
- NatureWorks® Ingeo™ 3001D Injection Grade PLA
- Fujipoly Industries Sarcon® GR-Hb Gap Filler Pad
- SABIC Innovative Plastics LNP LUBRICOMP PDXF89080 PE
- Teknor Apex Monprene® MP-1662-L1 Thermoplastic Elastomer
- SABIC Innovative Plastics LNP THERMOCOMP RX06420 PA 66 (Asia Pacific)
- Zircar Zirconia BusterF Alumina Bulk Fiber Insulation
- Dow Corning HV 1660/65 LIGHT GRAY SILICONE RUBBER KP
- Arlon R34896R025 0.025" (0.635 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Braskem IJ33D LLDPE Injection Molding Polyethylene Copolymer
- Radici Radilon® A CF350 (cond.) Nylon 66
Copyright © lookpolymers.com All Rights Reserved