Braskem Flexus® 9211 LLDPE Blow Film Extrusion Polyethylene Copolymer

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Hexene, Film Grade
Manufacturer	Braskem
Trade Name	Flexus®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Braskem Flexus® 9211 LLDPE Blow Film Extrusion Polyethylene Copolymer.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Braskem Flexus 9211 is a LLDPE hexene copolymer produced through a metallocene catalyst, which presents excellent impact and puncture strength beyond a differential sealing performance compared with another typical LLDPE. It contains medium slip, medium blocking, and medium level processing aid additives. Its applications include: automatic packaging (FFS), multilayer packaging films, and films for lamination.

Physical Properties	Metric	English	Comments
Density	0.917 g/cc	0.0331 lb/in³	ASTM-D792
Melt Flow	1.0 g/10 min @Load 2.16 kg, Temperature 190 °C	1.0 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM-D1238

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	850 %	850 %	ASTM-D882
Film Elongation at Break, TD	840 %	840 %	ASTM-D882
Elmendorf Tear Strength MD	230 g	230 g	ASTM-D1922
Elmendorf Tear Strength TD	790 g	790 g	ASTM-D1922
Dart Drop Test	>= 850 g	>= 1.87 lb	ASTM-D1709
Film Tensile Strength at Break, MD	35.0 MPa	5080 psi	ASTM-D882
Film Tensile Strength at Break, TD	25.0 MPa	3630 psi	ASTM-D882
1% Secant Modulus, MD	150 MPa	21800 psi	ASTM-D882
1% Secant Modulus, TD	160 MPa	23200 psi	ASTM-D882

Optical Properties	Metric	English	Comments
Haze	7.0 %	7.0 %	ASTM-D1003
Gloss	84 %	84 %	Angle 60°; ASTM-D2457