Polimeri Europa Flexirene® CL 10 Butene Copolymer Linear Low Density Polyethylene

Category Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Butene, Film
Manufacturer Polimeri Europa (Former EniChem)
Trade Name Flexirene®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa Flexirene® CL 10 Butene Copolymer Linear Low Density Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Flexirene CL 10 is a butene copolymer linear low density polyethylene (C4-LLDPE), with antioxidants, suitable for cast extrusion of thin film with high optical properties.Main Applications: Flexirene CL 10 is recommended for the production of stretch film to be used in both manual and automatic wrapping machines. In a multilayer film, Flexirene CL 10 enhances the optical properties of the global formulation; moreover, for its high processability, the resin is recommended whenever high productivity has to be reached. Information provided by Polimeri Europa.
Physical Properties Metric English Comments
Specific Gravity 0.918 g/cc
0.918 g/cc
ISO 1183
Thickness 10.0 - 50.0 microns
0.394 - 1.97 mil
Recommended
Melt Flow 2.6 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.6 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 9.00 MPa
1310 psi
ISO 527-3
Film Tensile Strength at Yield, TD 8.00 MPa
1160 psi
ISO 527-3
Film Elongation at Break, MD 600 %
600 %
ISO 527-3
Film Elongation at Break, TD 800 %
800 %
ISO 527-3
Coefficient of Friction, Dynamic >= 0.50
>= 0.50
ISO 8295
Elmendorf Tear Strength, MD 3.8722 g/micron
98.354 g/mil
ISO 6383-2
Elmendorf Tear Strength, TD 10.5 g/micron
267 g/mil
ISO 6383-2
Dart Drop Test 100 g
0.221 lb
F50; ISO 7765-1
Film Tensile Strength at Break, MD 35.0 MPa
5080 psi
ISO 527-3
Film Tensile Strength at Break, TD 25.0 MPa
3630 psi
ISO 527-3
1% Secant Modulus, MD 90.0 MPa
13100 psi
ISO 527-3
1% Secant Modulus, TD 105 MPa
15200 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 121 °C
250 °F
Internal method
Vicat Softening Point 97.0 °C

@Load 1.00 kg
207 °F

@Load 2.20 lb
ISO 306/A
Brittleness Temperature <= -70.0 °C
<= -94.0 °F
ASTM D746
Optical Properties Metric English Comments
Haze 2.0 %
2.0 %
ISO 14782
Gloss 91 %
91 %
45°; ASTM D2457