Polymer Property : Tensile Modulus = 6.20 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Modulus	6.20 GPa	899 ksi	ISO 527
Nilit FRIANYL C73 H-GV15 Nylon 6.6/6 for injection molding, 15% glass fiber reinforced Nylon 6.6/6 for injection molding, medium viscosity, heat stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Tensile Modulus	6.20 GPa @Temperature 23.0 °C	899 ksi @Temperature 73.4 °F	ISO 527-2/1
PolyOne Bergadur™ PB40 G20 UF UV Polybutylene Terephthalate (PBT) Information provided by PolyOne
Tensile Modulus	6.20 GPa	899 ksi	1[mm/min]; ISO 527-1/2
Akro-Plastic Akromid® S3 GF 30 4 (3552) PA 6.10 Conditioned, 30% Glass Filled (discontinued **) A characteristic property of AKROMID® S (PA 6.10) is that it has a renewable-resource content of up to 70 % and therefore fulfils the current definition of a bioplastic. The plant-based raw materia..
Tensile Modulus	6.20 GPa	899 ksi	Conditioned; ISO 527-1/-2
Lanxess DurethanÂ® BKV 30 G H2.0 900051 Nylon 6, 30% Glass Fiber PA 6, injection molding grade, 30% glass fibers, better surface finish and resistance to alcoholic calcium chloride-solution than BKV 30 H2.0, heat-stabilized, good heat-ageing resistance, good UV s..
Tensile Modulus	6.20 GPa	899 ksi	Conditioned; ISO 527-1/-2
Lanxess DurethanÂ® BKV 30 G H2.0 900116 Nylon 6, 30% Glass Fiber PA 6, injection molding grade, 30% glass fibers, better surface finish and resistance to alcoholic calcium chloride-solution than BKV 30 H2.0, heat-stabilized, good heat-ageing resistance
Tensile Modulus	6.20 GPa	899 ksi	ISO 527 Type 1A
Solvay TECHNYLÂ® A 21T2 V25 PA66, 25% glass fiber, Conditioned Description: Flame retardant polyamide 66, reinforced with 25% of glass fiber, heat stabilized, for injection molding.Available in: Asia Pacific, Europe, Latin America and North AmericaProduct Appl..
Tensile Modulus	6.20 GPa	899 ksi	ISO 527
Solvay TechnylÂ® C 216 Nylon 6, 30% Glass Fiber, EH50 Polyamide PA6, reinforced with 30% of glass fiber, for injection molding.It has good mechanical properties. It is used in all sectors of industry, offering an excellent combination between thermal ..
Tensile Modulus	6.20 GPa	899 ksi	ISO 527 Type 1A
Solvay TECHNYLÂ® C 216 V30 PA6, 30% glass fiber, Conditioned Description: Polyamide PA6, reinforced with 30 % of glass fiber, for injection molding.Available in: Asia Pacific and Latin AmericaProduct Applications: It has good mechanical properties, it is used..
Tensile Modulus	6.20 GPa	899 ksi	ISO 527 Type 1A
Solvay TECHNYLÂ® C 218 V 30 PA6, 30% glass fiber, Conditioned Description: TECHNYLÂ® C 218 V30 is a polyamide 6, heat stabilized, reinforced with 30% of glass fiber, for injection molding. This product is available in black color.Benefits: The product offers..
Tensile Modulus	6.20 GPa	899 ksi	ISO 527 Type 1A
Solvay TECHNYLSTARâ„¢ S 216 V30 PA6, 30% glass filled, Conditioned Description: TECHNYL STAR TM Polyamide, reinforced with 30% of glass fiber, for injection molding. Characterized by a high fluidity of the melt.Available in: Asia Pacific, Europe and North AmericaPr..
Tensile Modulus	6.20 GPa	899 ksi	ISO 527 Type 1A
Solvay TECHNYLSTARâ„¢ S 218 V30 PA6, 30% glass filled, Conditioned Description: TECHNYLSTARâ„¢ S 218 V30 is based on a patented high flow polyamide 6 resin (TechnylStar), heat stabilized, reinforced with 30% of glass fiber, for injection molding. This product is..
Tensile Modulus	6.20 GPa	899 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP GF004 PSU LNP* Thermocomp* GF004 is a compound based on Polysulfone resin containing 20% Glass Fiber.
Tensile Modulus	6.20 GPa	899 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP JF003XXZ PES (Asia Pacific) LNP* Thermocomp* JF003XXZ is a compound based on Polyethersulfone resin containing Glass Fiber.
Tensile Modulus	6.20 GPa	899 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP PCAF04FRHH PC+ABS (Europe-Africa-Middle East) LNP* THERMOCOMP* PCA04FRHH is a 20 % glass reinforced PC+ABS blend without chlorinated or brominated flame retardants. LNP* THERMOCOMP* complies with the material requirements as specified in TCO'99..
Tensile Modulus	6.20 GPa	899 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP RB00A PA 66 (Europe-Africa-Middle East) 50% glass beads filled Polyamide 66 injection moulding resin.
Tensile Modulus	6.20 GPa	899 ksi	5 mm/min; ASTM D638
SABIC Innovative Plastics NORYL GFN2 PPE+PS PPE+PS blend. 20% Glass reinforced. UL746C F1. NSF 61 listing in several colors (restrictions apply). FDA compliance (restrictions apply). Low water absorption. Hydrolytic stability. Dimensional sta..
Tensile Modulus	6.20 GPa	899 ksi	1 mm/min; ISO 527-1
Sax Polymers SAXALEN PPH305G30 Polypropylene Homopolymer, 30% Glass Filled SAXALEN PPH305G30 is a 30% glass filled Polypropylene - Homopolymer injection molding grade with high stiffness, low creep under load and good flow properties.Information provided by SAX Polymers
Tensile Modulus	6.20 GPa	899 ksi	5 mm/min; ASTM D638
SABIC Innovative Plastics NORYL GFN1520V PPE+HIPS NORYL GFN1520V is a 20% glass fibre reinforced material with improved hydrolytic stability. This grade has been certified for potable water applications up to 85C in Europe and North America, color ..
Tensile Modulus	6.20 GPa	899 ksi	Conditioned; ISO 527 2/1A
Solvay Technyl Starâ„¢ S 218 V30 30% Glass Reinforced Nylon 6 Heat stabilized, low viscosity, injection grade.Information provided by Rhodia; Rhodia has been acquired by Solvay.
Tensile Modulus	6.20 GPa	899 ksi	ISO 527-1/-2
DSM Akulon® K222-KMV5 Nylon 6-25% Mineral Reinforced (European and Asian Grade) (Dry) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier ..
Tensile Modulus	6.20 GPa @Temperature 23.0 °C	899 ksi @Temperature 73.4 °F	ISO 527
DuPont Performance Polymers Rynite® 515CS BK575M PET Rynite® 515CS BK575M is a 15% glass fiber reinforced, black polyethylene terephthalate resin modified for improved color stability after heat aging.Information provided by DuPont Performance Polyme..
Tensile Modulus	6.20 GPa	899 ksi	ISO 527-1/-2
DuPont Performance Polymers Sorona® 3015G BK001 Polytrimethylene Terephthalate (PTT) (Unverified Data**)& 15% Glass Reinforced Polytrimethylene Terephthalate with Resin Made from Bio-PDO Sorona 3015G BK001 is a 15% glass reinforced black PTT resin containing 31% renewably sourced ingredients by weight (..
Tensile Modulus	6.20 GPa	899 ksi	1 mm/min; ISO 527
Eurostar Starflam BFR430A PA6, Glass Fiber Filled, Flame Retardant, Injection Molded Starflam BFR430A is a Flame Retardant, Glass Fiber Reinforced Polyamide 6, Injection Molding ResinInformation provided by Eurostar.
Tensile Modulus	6.20 GPa	899 ksi	1 mm/min; ISO 527
Eurostar Starflam PZ0042E PA6, 20% Glass Filled, Injection Molded PZ0042E is a Halogen Free and Red Phosphorous Free, Flame Retardant, Glass Reinforced, Polyamide 6 Injection Molding (also known as PF1004Z222 or PA620GFU9Z22)Information provided by Polymer Technol..
Tensile Modulus	6.20 GPa	899 ksi	ISO 527
Cossa Polimeri ESTABLEND PA 1050 GF HI ABS / Nylon 6 Blend, 25% Glass Filled ESTABLEND PA is a blend of acrylonitrile butadiene styrene and polyamide 6.25% glass fiber reinforcedHigh impact strength, high chemical resistance, excellent heat resistance, high dimensional stabi..
Tensile Modulus	6.20 GPa	899 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP GF004 PSU (Asia Pacific) LNP* Thermocomp* GF004 is a compound based on Polysulfone resin containing Glass Fiber.
Tensile Modulus	6.20 GPa	899 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP Thermocomp PK0069 PA 6 (Europe-Africa-Middle East) LNP* THERMOCOMP* PK0069 is a compound based on PA 6 resin containing Glass Bead, Flame Retardant. Added features include Flame Retardant.This data was supplied by SABIC-IP for the Europe-Africa-Midd..