Solvay Technyl Starâ„¢ S 218 V30 30% Glass Reinforced Nylon 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl Star™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Technyl Starâ„¢ S 218 V30 30% Glass Reinforced Nylon 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Heat stabilized, low viscosity, injection grade.Information provided by Rhodia; Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 |
| Water Absorption | 0.95 % @Time 86400 sec |
0.95 % @Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0035 cm/cm | 0.0035 in/in | Rhodia Test |
| Linear Mold Shrinkage, Transverse | 0.0065 cm/cm | 0.0065 in/in | Rhodia Test |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 110 MPa | 16000 psi | Conditioned; ISO 527 2/1A |
| 190 MPa | 27600 psi | DAM; ISO 527 2/1A | |
| Elongation at Break | 3.8 % | 3.8 % | DAM; ISO 527 2/1A |
| 4.5 % | 4.5 % | Conditioned; ISO 527 2/1A | |
| Tensile Modulus | 6.20 GPa | 899 ksi | Conditioned; ISO 527 2/1A |
| 9.60 GPa | 1390 ksi | DAM; ISO 527 2/1A | |
| Flexural Modulus | 4.90 GPa | 711 ksi | Conditioned; ISO 178 |
| 8.40 GPa | 1220 ksi | DAM; ISO 178 | |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | DAM; ISO 180/1A |
| 21.0 kJ/m² | 9.99 ft-lb/in² | Conditioned; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | DAM; ISO 180/1U |
| 14.0 kJ/m² | 6.66 ft-lb/in² | Conditioned; ISO 180/1U | |
| Charpy Impact Unnotched | 8.10 J/cm² | 38.5 ft-lb/in² | DAM; ISO 179/1eU |
| 9.00 J/cm² | 42.8 ft-lb/in² | Conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | DAM; ISO 179/1eA |
| 3.20 J/cm² | 15.2 ft-lb/in² | Conditioned; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 222 °C | 432 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | DAM; ISO 75-2/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 220 - 225 °C | 428 - 437 °F | |
| Middle Barrel Temperature | 225 - 235 °C | 437 - 455 °F | |
| Front Barrel Temperature | 235 - 245 °C | 455 - 473 °F | |
| Mold Temperature | 80.0 °C | 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.15 % | <= 0.15 % |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 1-8181 Polyamide 66, with carbon fiber, toughness-modified
- Gouda Vuurvast GOLITE 140 Refractory Insulating Castable
- SABIC Innovative Plastics LNP LUBRILOY RF206AXH PA 66
- Teknor Apex APEX® 3300-85 Polyvinyl Chloride, Flexible
- Borealis Borclean™ HC314BF Polypropylene Homopolymer for Capacitor Film
- Lubrizol ISOPLAST™ 202EZ Engineering Thermoplastic Polyurethane Resin
- Elgiloy® Co-Cr-Ni Alloy, Wire, Heat Treated
- AK Steel DI-MAX® M-22 Nonoriented Electrical Steel
- BorsodChem ONGRONAT PA-22 MDI Isocyanate
- PolyOne Geon™ Vinyl Rigid Extrusion L6256 Polyvinyl Chloride, Rigid (PVC, Rigid)
Copyright © lookpolymers.com All Rights Reserved