Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Modulus | 4.27 GPa @Thickness 6.40 mm |
619 ksi @Thickness 0.252 in |
ASTM D638 |
SABIC Innovative Plastics Lexan® FL920 PC Various weight reductions at .250"" (6.35 mm) wall, 20% GR. Excellent flex mod, high tensile strength/heat resistance. V-0/5V at .250"" (6.35mm). |
|||
Tensile Modulus | 4.27 GPa @Thickness 6.40 mm |
619 ksi @Thickness 0.252 in |
ASTM D638 |
SABIC Innovative Plastics Lexan® FL920 PC (Asia Pacific) Various weight reductions at .250"" (6.35 mm) wall, 20% GR. Excellent flex mod, high tensile strength/heat resistance. V-0/5V at .250"" (6.35mm). |
|||
Tensile Modulus | 4.27 GPa | 619 ksi | 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics Ultem 2212 PEI 20% Milled glass filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Modulus | 4.27 GPa | 619 ksi | 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics Ultem 2212 PEI (Asia Pacific) 20% Milled glass filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Tensile Modulus | 4.27 GPa | 619 ksi | 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM 2212R PEI 20% Milled glass filled, enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing. |
|||
Tensile Modulus | 4.27 GPa | 619 ksi | 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM 2212R PEI (Asia Pacific) 20% Milled glass filled, enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing. |
|||
Tensile Modulus | 4.27 GPa | 619 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP DFZ22P PC (Asia Pacific) LNP* THERMOCOMP* DFZ22P is a compound based on Polycarbonate resin containing Glass Fiber, Milled Glass. Added features of this material include: Exceptional Processing. |
|||
Tensile Modulus | 4.27 GPa | 619 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP DFZ22P PC LNP THERMOCOMP* DFZ22P is a compound based on Polycarbonate resin containing 10% Glass Fiber, 10% Milled Glass. Added features of this material include: Exceptional Processing. |
|||
Tensile Modulus | 4.27 GPa | 619 ksi | |
Hexcel® HexPly® F263 Epoxy Resin HexPly® F263 is a structural, heat resistant epoxy resin formulated for excellent translation of high modulus carbon fiber properties in typically aerospace applications. HexPly® F263 is a high te.. |