Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 30.4 MPa | 4410 psi | ASTM D638 |
PolyMirae Moplen RP343N Injection Molding Grade Polypropylene Moplen RP343N is the polypropylene random copolymer manufactured by PMC under the license of BASELL using the Spheripol process. Moplen RP343N is a random copolymer particularly suitable for injecti.. |
|||
Tensile Strength, Yield | 30.4 MPa | 4410 psi | 5.1 mm/min; ASTM D638 |
PolyOne Geon™ L4605 Ivory 3098 Polyvinyl Chloride, Semi-Rigid (PVC, Semi-Rigid) Information provided by PolyOne |
|||
Tensile Strength, Yield | 30.4 - 55.9 MPa | 4410 - 8110 psi | Average value: 44.4 MPa Grade Count:35 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Transparent, Molded This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), Transparent, Molded". Each property range of values reported is m.. |
|||
Tensile Strength, Yield | 30.4 MPa | 4410 psi | ASTM D638 |
Hyosung Topilene C600 PP C600 Film Grade Butane Random CopolymerApplications: Metallizing CPPCharacteristics:Al bonding strengthHigh glossInformation provided by Hyosung Corporation |
|||
Tensile Strength, Yield | 30.4 MPa | 4410 psi | ASTM D638 |
Hyosung Topilene HB240P PP HB240P Applications:Industrial pipesSewerage pipesCharacteristics:High impact strengthHigh ring stiffnessInformation provided by Hyosung Corporation |
|||
Tensile Strength, Yield | 30.4 MPa | 4410 psi | ASTM D638 |
Hyosung Topilene HJ740 PP HJ740 High Isostatic PP Impact CopolymerApplications:CompoundingElectric applianceAutomobile partsCharacteristics:High stiffnessHeat resistanceMedium impactInformation provided by Hyosung Corporatio.. |
|||
Tensile Strength, Yield | 30.4 MPa | 4410 psi | ASTM D638 |
Hyosung Topilene J440F PP J440F Block CopolymerApplications: Retort CPPCharacteristics:Excellent impact strengthFish eye freeHeat resistanceGood clarityInformation provided by Hyosung Corporation |
|||
Tensile Strength, Yield | 30.4 MPa | 4410 psi | ASTM D638 |
Hyosung Topilene R601 PP R601 Injection Random CopolymerApplications:High transparent productISBM bottleCharacteristics:High transparencyStiffnessInformation provided by Hyosung Corporation |
|||
Tensile Strength, Yield | 30.4 MPa | 4410 psi | ASTM D638 |
Hyosung Topilene R701 PP R701 Injection Random CopolymerApplications:High transparent productISBM bottleCharacteristics:High transparencyStiffnessInformation provided by Hyosung Corporation |
|||
Tensile Strength, Yield | 30.4 MPa | 4410 psi | ASTM D638 |
Hyosung Topilene R701 PP R701 Random CopolymerApplications: General injectionCharacteristics: TransparenceInformation provided by Hyosung Corporation |
|||
Tensile Strength, Yield | 30.4 MPa | 4410 psi | ASTM D638 |
Hyosung Topilene R801H PP R801H Injection Random CopolymerApplications:High transparent productLarge articlesCharacteristics:High transparencyStiffnessInformation provided by Hyosung Corporation |
|||
Tensile Strength, Yield | 30.4 MPa @Thickness 3.20 mm |
4410 psi @Thickness 0.126 in |
50 mm/min; ASTM D638 |
LG Chemical HI100X ABS, High Impact, Semi-Transparency, Flexible Feature: Injection Molding, High Impact, Semi-Transparency, FlexibleApplication: Artificial Nails, Miscellaneous Goods)CAS No. 9010-94-0Information provided by LG Chemical |
|||
Tensile Strength, Yield | 30.4 MPa @Thickness 3.20 mm |
4410 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
LG Chemical LUPOL HF5254A PP+MF20% Description: Injection Molding, PP+MF20%, Good WeatherabilityApplication: Automotive Interior PartsCAS: 9003-07-0 and 14807-96-6Information provided by LG Chemical |
|||
Tensile Strength, Yield | 30.4 MPa @Thickness 3.20 mm |
4410 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
LG Chemical LUTENE-H BE0400 HDPE Description: LUTENE - H BE0400 is an excellent materials for blow-molded articles with high density and rigidity. It has good flow characteristics and impact resistance.Applications: Blow molded con.. |
|||
Tensile Strength, Yield | 30.4 MPa | 4410 psi | 50mm/min; ASTM D638 |
LG Chemical SEETEC M1315 Polypropylene Impact Copolymer Features: SEETEC M1315 is a heterophasic polypropylene copolymer for compression molding caps, especially SACMI machines. SEETEC M1315 exhibits an excellent stiffness, a high impact strength, a high.. |
|||
Tensile Strength, Yield | 30.4 MPa | 4410 psi | 50 mm/min; ASTM D638 |
LG Chemical SEETEC PB283 HDPE Features: This high molecular weight, hexane copolymer is tailored for light-weight blow-molded containers that require: Good stiffness and Excellent processabilityAdditives: Anti-OxidantsApplicatio.. |
|||
Tensile Strength, Yield | 30.4 MPa | 4410 psi | ASTM D638 |
Lotte Chemical Titan TITANEX® HB0972 High density polyethylene Hexene-1 resin HF0972 is a pelleted high density polyethylene Hexene-1 resin for blow molding.Applications: Large size shipping containers and drums, household and industrial chemical containers, toiletries and c.. |
|||
Tensile Strength, Yield | 30.4 MPa | 4410 psi | ASTM D638 |
IRPC Polimaxx Polene 1196NN Polypropylene Compound CHARACTERISTICS: POLYPROPYLENE HOMOPOLYMER UNREINFORCED, CONTAIN FLAME RETARDANT, UL 94 V-2 APPROVAL, HIGH IMPACT STRENGTHAPPLICATIONS: INJECTION MOLDING FOR ELECTRICAL APPLIANCES |
|||
Tensile Strength, Yield | 30.4 MPa | 4410 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Starex® HR-1360 HIPS, Unreinforced Heat Resistant Information provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 30.4 MPa | 4410 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Starex® HR-1360 HIPS, Unreinforced Heat Resistant Information provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 30.4 MPa | 4410 psi | ASTM D638 |
SCG Chemicals EL-Leneâ„¢ H6007JU High Density Polyethylene Injection Molding Key Characteristics:Good processabilityHigh rigidityHigh impact resistanceGood weathering resistance (UV stabilizer)Recommended Applications:Crates for soft drink, bottles, pallet, garbage bins, con.. |