LG Chemical LUTENE-H BE0400 HDPE
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE |
| Manufacturer | LG Chemical |
| Trade Name | LUTENE-H |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUTENE-H BE0400 HDPE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: LUTENE - H BE0400 is an excellent materials for blow-molded articles with high density and rigidity. It has good flow characteristics and impact resistance.Applications: Blow molded containers with capacities ranging a few milliliters up to 20 liters, SheetCAS No. 9002-88-4Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.957 g/cc | 0.957 g/cc | ASTM D792 |
| Environmental Stress Crack Resistance | 50 hour | 50 hour | F50; ASTM D1693 |
| Melt Flow | 0.25 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.25 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 64 | 64 | ASTM D2240 |
| Tensile Strength, Yield | 30.4 MPa @Thickness 3.20 mm |
4410 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | >= 600 % @Thickness 3.20 mm |
>= 600 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Modulus | 1.37 GPa | 199 ksi | 15mm/min; ASTM D790 |
| Izod Impact, Notched | 2.45 J/cm @Thickness 6.40 mm, Temperature 20.0 °C |
4.59 ft-lb/in @Thickness 0.252 in, Temperature 68.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 133 °C | 271 °F | DSC |
| Brittleness Temperature | <= -80.0 °C | <= -112 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Adapter Temperature | 180 °C | 356 °F | Ideal, Extrusion Blow Molding |
| 180 - 190 °C | 356 - 374 °F | Extrusion Blow Molding | |
| Die Temperature | 170 °C | 338 °F | Ideal, Extrusion Blow Molding |
| 160 - 190 °C | 320 - 374 °F | Extrusion Blow Molding | |
| Melt Temperature | 180 °C | 356 °F | Ideal, Extrusion Blow Molding |
| 180 - 200 °C | 356 - 392 °F | Extrusion Blow Molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Barrel | 160-185°C | Intake Zone, Extrusion Blow Molding |
| 165°C | Intake Zone, Ideal, Extrusion Blow Molding | |
| 175-195°C | Compression Zone, Extrusion Blow Molding | |
| 180°C | Compression Zone, Ideal, Extrusion Blow Molding | |
| 180-200°C | Metering Zone, Extrusion Blow Molding | |
| 190°C | Metering Zone, Ideal, Extrusion Blow Molding | |
| Cross Head | 165-195°C | Extrusion Blow Molding |
| 180°C | Extrusion Blow Molding |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Rigid Extrusion 87554 Polyvinyl Chloride, Rigid (PVC, Rigid)
- SABIC Innovative Plastics LNP LUBRICOMP DBL32 PC
- Ineos R35C-00 Polypropylene Random Copolymer
- LATI Latamid 66 H2 K/50 PA 66, 50% Carbon Fiber Reinforced, Heat Stabilized
- Saint-Gobain Meldin® 7001 CM Compression Molded Polyimide
- Sax Polymers SAXALEN PPH305G30 Polypropylene Homopolymer, 30% Glass Filled
- Master Bond MasterSil 710 Silicone Paste Meets MIL Spec
- Chase Plastics CP Pryme® A100HI ABS Molding Resin, High Impact
- Trelleborg Fillite® 106 Alumino-silicate Cenospheres
Copyright © lookpolymers.com All Rights Reserved