Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 24.1 MPa | 3500 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Wire & Cable 8800FR Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | Type I, 51 mm/min; ASTM D638 |
PolyOne Maxxam™ PPC-30T UV EXT 1148 Polypropylene Copolymer (PP Copolymer) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car.. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | TM R050-36 |
Resinlab® EP750 Clear Unfilled Epoxy Structural Adhesive Resinlab™ EP750 Clear is a two part unfilled epoxy structural adhesive which ingredients are listed in the Code of Federal Regulations Title 21 175.105 (Adhesives) and 175.300 (Resinous and polymer.. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | ASTM D638 |
ExxonMobil Escorene® HD-6705 HDPE, Injection Grade
(discontinued **) Data Provided by Exxon Chemical Canada.Characteristics: Medium Flow, Good Stiffness, Good ImpactUses: Food containers, Housewares, Toys |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | ASTM D638 |
Ineos Nova Zyntar® F7080UV Developmental Flame Retardant Polystyrene
(discontinued **) Features: General purpose non-Deca based resin (does not combine with Decabromodiphenyloxide)Good indoor UV light color stability(grey colors)UL94 V-0 @ 1.5 mm for all colors Good aesthetics for inj.. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with Monoplex DOS Plasticizer MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | ASTM D638 |
LyondellBasell Alathon® L5008HP High Density Polyethylene, Pressure Pipe Extrusion Grade ALATHON L5008HP is a bimodal, high molecular weight, high density polyethylene resin with excellent processability designed to meet the high performance requirements of pressure pipe applications in.. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | |
Kraton® G1650 + PP blend + Talc (12/21/67) Unmodified polypropylene has high rigidity and good heat resistance, but poor impact resistance, especially at low temperatures. Blending KRATON D and G polymers with PP significantly improves the .. |
|||
Tensile Strength, Yield | 24.1 MPa @Temperature 23.0 °C |
3500 psi @Temperature 73.4 °F |
ASTM D638 |
Ineos L12N-00 Polypropylene Impact Copolymer This is a medium melt flow rate, nucleated impact copolymer polypropylene for injection molding and compounding applications. This material meets the requirements of the U.S. Food and Drug Administ.. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | ASTM D638 |
Techmer ES HiFill® HDPE TM5 5% Talc Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Talc Filler, 5% Filler by WeightInformation provided by TP Composites, Inc. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | ASTM D638 |
Spartech Korad® SP-2011 Cap/HIPS Polystyrene Sheet Description: Polystyrene SheetKorad is a registered trademark of Polymer Extruded Products, Inc..Information provided by Spartech. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | ASTM D638 |
Spartech PP5240 Calcium Carbonate Filled Homopolymer Offers improved stiffness versus unfilled materials. They offer substantial improvements in drop weight (Gardner) impact over both unfilled polypropylene and other types of filled polypropylene. Cal.. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | ASTM D638 |
Spartech Sound X Noise Abatement Alloy Specialty Sheet Description: Specialty SheetInformation provided by Spartech. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | ASTM D-882 |
Saint-Gobain Norton® FEP Fluoropolymer Film Features/Benefits:Outstanding clarityOutstanding anti-stick release propertiesPerformance from -254°C (-425°F) to 205°C (400°F)Exceptional chemical resistance and electric propertiesComp.. |
|||
Tensile Strength, Yield | >= 24.1 MPa | >= 3500 psi | ASTM D-882 |
Saint-Gobain Norton® T-100 Virgin Skived PTFE Sheet (0.125" thick) T-100/T-200 Features/Benefits: Outstanding heat and chemical resistance; High dielectric strength; Anti-stick properties; Can be chemically etched for bondability; Applications include laminate rele.. |
|||
Tensile Strength, Yield | >= 24.1 MPa | >= 3500 psi | ASTM D-882 |
Saint-Gobain Norton® T-100 Virgin Skived PTFE Sheet (0.250" thick) T-100/T-200 Features/Benefits: Outstanding heat and chemical resistance; High dielectric strength; Anti-stick properties; Can be chemically etched for bondability; Applications include laminate rele.. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | 2"/min; ASTM D638 |
A. Schulman LP554-01 Narrow Molecular Weight Homopolymer, High-Density Polyethylene DescriptionLP 554-01 is a narrow molecular weight homopolymer high-density polyethylene exhibiting toughness, rigidity and warpage resistance. ApplicationApplications of LP 554-01 include crates, t.. |
|||
Tensile Strength, Yield | >= 24.1 MPa | >= 3500 psi | ASTM D638 |
Total HDPE XT25N High Density Polyethylene, Pipe Resin Polyethylene: High molecular weight, bimodal pipe resin. PPI TR4 designation PE4710 /PE100 for demanding installations. Every batch certified to meet 2500 hrs PENT according to ASTM F1473.Charact.. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | 2"/min; ASTM D638 |
A. Schulman LP554-01 Narrow Molecular Weight Homopolymer, High-Density Polyethylene DescriptionLP 554-01 is a narrow molecular weight homopolymer high-density polyethylene exhibiting toughness, rigidity and warpage resistance. ApplicationApplications of LP 554-01 include crates, t.. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | ASTM D638 |
Lubrizol Hipscon™ M-520 Static Control High Impact Polystyrene Hipscon™ M-520 is a conductive, carbon black filled, High Impact Polystyrene available as extruded sheet. Thermoformed trays are easily formed into deep pockets that maintain uniform static protec.. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | 2" (50mm) per min.; ASTM D638 |
Formosa Plastics Formolene® 6520A Injection Molding Polypropylene Impact CopolymerApplications: Closures, Housewares, Small Appliance ApplicationsFormolene 6520A is a medium impact copolymer of polypropylene characterized by its easy mold flow, physical property b.. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | 100% elongation; ASTM D412; ASTM D638 |
Lubrizol Estane® 58144 Thermoplastic Polyurethane Type: Estane® 58144 is a 65D Polyether-type thermoplastic polyurethane (TPU) compound.Features: FDA (contact Lubrizol for details). Pre-drying: 2 hours at 104C (220F) in Dehumidifying Hopper Dryer.. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | ASTM D638 |
ExxonMobil HDPE BU46-055 High Density Polyethylene Resin Product Description: BU46-055 is a high molecular weight, high density polyethylene copolymer which contains a UV inhibitor. It possesses a combination of excellent processability, outstanding melt .. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | molded and tested in accordance with ASTM D 4101; ASTM D638 |
Dow 6D43 Polypropylene Resin DOW 6D43 is intended for use fiber spinning processes.Information provided by DowDow Announced Sale of Global Polypropylene Business to Braskem in July 2011. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | ASTM D638 |
Techmer ES Statiblend® PP CO 99074 Availability: North AmericaForms: PelletsFeature: Copolymer and Semi ConductiveUL File Number: E157318Information provided by TP Composites, Inc. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | ASTM D638 |
A. Schulman POLYFORT™ FPP 1200 Calcium Carbonate-Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1200 is a 40% calcium carbonate-filled homopolymer polypropylene. Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | ASTM D638 |
ExxonMobil Paxon™ BA46-055 Blow Molding Resin Product Description: BA46-055 is a high molecular weight high density polyethylene copolymer. It possesses a combination of excellent processability, outstanding melt strength, high impact strength.. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | 2.0 in/min; ASTM D638 |
LTL Color Compounds ColorFast® FRPS200 Styrene, High Impact V0/5VA high impact styreneAll information provided by LTL Color Compounders, Inc. |
|||
Tensile Strength, Yield | >= 24.1 MPa | >= 3500 psi | ASTM D 638 type IV |
Total XT10 N Natural HDPE, pipe Applications: Potable water, industrial and mining, sewer and sewer relining, gas and oil gathering, general pipe relining, pipe coatingInformation provided provided by Total Petrochemicals.Total Pe.. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | ASTM D638 |
Techmer ES HiFill® TPU 0445 A Availability: North AmericaForms: PelletsFeatures: High Density and High Specific GravityInformation provided by TP Composites, Inc. |