Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 225 MPa | 32600 psi | ISO 527-2 |
Solvay Specialty Polymers Amodel® AS-1133 HS Polyphthalamide (PPA)
(Unverified Data**) Amodel AS-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) resin that provides excellent structural integrity in molded parts, even those with wall thicknesses greater than 0.. |
|||
Tensile Strength, Yield | 225 MPa | 32600 psi | ASTM D638 |
LNP Thermocomp® LC-1006 Polyetheretherketone, Carbon Fiber Reinforcement
(discontinued **) Forms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names.. |
|||
Tensile Strength, Yield | >= 225 MPa | >= 32600 psi | |
MetalTek MTEK E Cast UNS N24130 Nickel-Copper Alloy Acid and alkaline resistant. Weldable gradeApplications: Marine pumps, valves, seal housings, filter parts.Information provided by MetalTek |
|||
Tensile Strength, Yield | 225 MPa @Strain 0.200 %, Temperature 538 °C |
32600 psi @Strain 0.200 %, Temperature 1000 °F |
|
Haynes HR-160® alloy, solution annealed sheet Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Tensile Strength, Yield | >= 225 MPa | >= 32600 psi | |
MetalTek MTEK 25-35MA Heat Resistant Stainless Steel Information provided by MetalTek |
|||
Tensile Strength, Yield | 225 MPa @Strain 0.200 %, Temperature 650 °C |
32600 psi @Strain 0.200 %, Temperature 1200 °F |
|
Haynes 556® alloy, cold rolled, solution annealed sheet, 0.8-2.8 mm thick Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Tensile Strength, Yield | 225 MPa | 32600 psi | ISO 527-2 |
Solvay Specialty Polymers Amodel® AS-1133 HS Polyphthalamide (PPA), 33% Glass Fiber (Dry) Amodel® AS-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) resin that provides excellent structural integrity in molded parts, even those with wall thicknesses greater th.. |
|||
Tensile Strength, Yield | 225 MPa | 32600 psi | ISO 527 |
SABIC Innovative Plastics LNP Thermocomp RX06423 PA 66 LNP* Thermocomp* RX06423 is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized, UV Stabilized.This data was supplied b.. |
|||
Tensile Strength, Yield | 225 MPa | 32600 psi | ISO 527-2 |
Ascend Performance Materials Vydyne® R543H NT Nylon 66, 43% Glass Reinforced, DAM Vydyne® R543H NT is general-purpose, 43% glass-fiber reinforced PA66 resin. Available in natural, it is an injection-molding grade resin that is lubricated for machine feed, flow and mold release. .. |
|||
Tensile Strength, Yield | 225 MPa @Strain 0.200 % |
32600 psi @Strain 0.200 % |
|
ATI Allegheny Ludlum AL 409 Cb™ Brazeable Ferritic Stainless Steel AL 409 Cb™ is normally 12.5% chromium ferritic stainless steel with columbium stabilization and with restricted titanium and aluminum contents. As a result of these alloying adjustments, the braze.. |
|||
Tensile Strength, Yield | 225 MPa | 32600 psi | 50 mm/min; ISO 527-1/-2 |
BASF Ultramid® B3WG10 BK 00564 50% Glass Filled PA6 (Dry) Description: 50% glass-fiber reinforced and heat aging resistant injection-molding grade for technical parts with very high stiffness.Information provided by BASF |
|||
Tensile Strength, Yield | 225 MPa @Strain 0.200 %, Temperature 649 °C |
32600 psi @Strain 0.200 %, Temperature 1200 °F |
|
Haynes 230® alloy, as cast vacuum investment casting Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Tensile Strength, Yield | 225 MPa @Strain 0.200 %, Temperature 760 °C |
32600 psi @Strain 0.200 %, Temperature 1400 °F |
|
Haynes 230® alloy, as cast vacuum investment casting Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Tensile Strength, Yield | 225 MPa @Strain 0.200 %, Temperature 871 °C |
32600 psi @Strain 0.200 %, Temperature 1600 °F |
|
Haynes 230® alloy, cold rolled and 1232°C solution annealed sheet Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Tensile Strength, Yield | 225 MPa @Strain 0.200 %, Temperature 650 °C |
32600 psi @Strain 0.200 %, Temperature 1200 °F |
|
Special Metals UDIMET® alloy L-605 Co-Cr-W-Ni Alloy UDIMET® alloy L-605 (UNS R30605) is a solid solution strengthened cobalt-chromium-tungsten-nickel alloy with excellent high-temperature strength and excellent oxidation resistance to 2000°F (1093°.. |