Polymer Property : Tensile Strength, Yield = 66.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Yield 66.0 MPa
9570 psi
Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics Lexan® 4401R PPC+PC
LEXAN 4401R is a high heat resistant poly(ester)carbonate injection molding resin.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength, Yield 66.0 MPa
9570 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® 500R PC
10% GR PC. Optimum combination of high modulus plus excellent impact strength and flame retardance. Internal mold release.
Tensile Strength, Yield 66.0 MPa
9570 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® 503R PC
10% GR PC. Optimum combination of high modulus plus excellent impact strength and flame retardance. UV-stabilized. Internal mold release.
Tensile Strength, Yield 66.0 MPa
9570 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® 503R PC (Asia Pacific)
10% GR PC. Optimum combination of high modulus plus excellent impact strength and flame retardance. UV-stabilized. Internal mold release.
Tensile Strength, Yield 66.0 MPa
9570 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® 915AU PC (Asia Pacific)
LEXAN resin grade 915AU is a flame retardant polycarbonate featuring non brominated and non chlorinated FR systems, with good flow, and good UV stability. It is available in transparent colors, inte..
Tensile Strength, Yield 66.0 MPa
9570 psi
50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® 915AU PC (Asia Pacific)
LEXAN resin grade 915AU is a flame retardant polycarbonate featuring non brominated and non chlorinated FR systems, with good flow, and good UV stability. It is available in transparent colors, inte..
Tensile Strength, Yield 66.0 MPa
9570 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® CFR9712 PC COPOLYMER
Lexan* CFR9712 Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 2.0 mm and high flow capability. ..
Tensile Strength, Yield 66.0 MPa
9570 psi
Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics Lexan® FXM4701 PPC (Asia Pacific)
LEXAN FMX4701 is a high heat resistant poly(ester)carbonate injection molding resin. This grade is especially designed to visualize color effects.This data was supplied by SABIC-IP for the Asia Paci..
Tensile Strength, Yield 66.0 MPa
9570 psi
50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® LUX7436C PC COPOLYMER
Lexan* LUX7436C Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.2 mm / 5VA rating at 3.0mm a..
Tensile Strength, Yield 66.0 MPa
9570 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® BFL2000B PC (Asia Pacific)
Lexan BFL2000B resin is a Br- & Cl-free FR polycarbonate resin featuring high flow with balanced impact. It is available only in dark colors.
Tensile Strength, Yield 66.0 MPa
9570 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® CFR9712 PC COPOLYMER (Asia Pacific)
Lexan* CFR9712 Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 2.0 mm and high flow capability. ..
Tensile Strength, Yield 66.0 MPa
9570 psi
Plain Cast Resin; ASTM D638
TSE Industries EcoWIND® M110 General Purpose Filament Winding Polyurethane Resin
TSE-EcoWIND® resins are “Environmentally-Preferred Products” or EPP’s. They are a pair of polyurethane resins free of Styrene, and are “ultra-low” emitting during application. TSE-EcoWIND® re..
Tensile Strength, Yield 66.0 MPa
9570 psi
ASTM D638
Covestro Apec® DP9-9354T High-Heat Polycarbonate, Transparent, Flame-Retardant  (discontinued **)
Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This produ..
Tensile Strength, Yield 66.0 MPa
9570 psi
10%/min. ASTM D638
EVALCA EVAL® K102 Ethylene Vinyl Alcohol Copolymer Resin  (discontinued **)
38 mol % Ethylene.Data provided by EVALCA. Applications: Solid phase pressure forming. EVOH is used in packaging applications because of its outstanding gas barrier properties.EVAL™ is now produc..
Tensile Strength, Yield 66.0 MPa
9570 psi
ASTM D 638
SABIC Innovative Plastics LNP Thermotuf VF002 PA 66
LNP THERMOTUF* VF002 is a compound based on Nylon resin containing Glass Fiber. Added features of this material include: High Impact.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength, Yield 66.0 MPa
9570 psi
Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics Noryl FXN2090H PPE+HIPS
Noryl* FXN2090H resin is an unfilled, injection moldable grade. Designed for exceptionally high gloss and improved pencil hardness vs. standard Noryl grades, FXN2090H resin uses non-halogenated FR a..
Tensile Strength, Yield 66.0 MPa
9570 psi
50 mm/min; ISO 527
SABIC Innovative Plastics Noryl FXN2090H PPE+HIPS
Noryl* FXN2090H resin is an unfilled, injection moldable grade. Designed for exceptionally high gloss and improved pencil hardness vs. standard Noryl grades, FXN2090H resin uses non-halogenated FR a..
Tensile Strength, Yield 66.0 MPa
9570 psi
Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics Noryl FXN2090H PPE+HIPS (Europe-Africa-Middle East)
Noryl* FXN2090H resin is an unfilled, injection moldable grade. Designed for exceptionally high gloss and improved pencil hardness vs. standard Noryl grades, FXN2090H resin uses non-halogenated FR a..
Tensile Strength, Yield 66.0 MPa
9570 psi
50 mm/min; ISO 527-1,-2
Covestro Makrolon® 1952 Polycarbonate
Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Flame retardancy• Me..
Tensile Strength, Yield 66.0 MPa
9570 psi
ISO 527-1/-2
Covestro Makrolon® 2558 Polycarbonate
ISO 7391-PC,MR,(,,)-18-9MVR (300 °C/1.2 kg) 14.5 cm3/10 minMedical devicessuitable for ETO and steam sterilization at 121 °CComplies with the requirements of FDA-modified ISO 10993-1 and USP Class..
Tensile Strength, Yield 66.0 MPa
9570 psi
50 mm/min; ISO 527-1,-2
Covestro Makrolon® 2607 MAS167 Polycarbonate
Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• General purpose• Med..
Tensile Strength, Yield 66.0 MPa
9570 psi
50 mm/min; ISO 527-1,-2
Covestro Makrolon® 2665 MAS071 Polycarbonate
Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Flame retardant• Med..
Tensile Strength, Yield 66.0 MPa
9570 psi
50 mm/min; ISO 527-1,-2
Covestro Makrolon® ET3227 Polycarbonate
Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Extrusion• High visc..
Tensile Strength, Yield 66.0 MPa
9570 psi
ASTM D638
Aclo Accutech Polypropylene CP0435G43CV Copolymer Glass Reinforced Coupled
Approved to GMP.PP.039 Black A13054
Tensile Strength, Yield 66.0 MPa
9570 psi
ASTM D638
Solvay Specialty Polymers Mindel® S-1000 Modified Polysulfone  (discontinued **)
This product line was acquired by Solvay Advanced Polymers from BP Amoco in November 2001.
Tensile Strength, Yield 66.0 MPa
9570 psi
50mm/min; ISO 527
BASF Ultraform S 1320 0021 UNC POM
Ultraform S1320 0021 UNC is an easy flowing, rapidly freezing injection molding POM grade with enhanced stiffness and heat distortion resistance. It is highly stabilized to resist aggressive fuels,..