Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 29.0 MPa | 4200 psi | ASTM D638 |
Multibase Multi-Pro® 3018 TU Polypropylene Talc Filled, 30% by weight.Forms:PelletsProcessing Methods:Injection MoldingUses: Automotive Under the HoodInformation provided by Multibase |
|||
Tensile Strength, Yield | 29.0 MPa | 4200 psi | ASTM D638 |
Multibase Multi-Pro® 4008 T Polypropylene Talc Filled, 40% by weight.Forms:PelletsProcessing Methods:Injection MoldingUses: ConnectorsElectrical/Electronic ApplicationsAppliancesInformation provided by Multibase |
|||
Tensile Strength, Yield | 29.0 MPa | 4210 psi | 500 mm/min |
NOVA Chemicals Sclair® 2714 HDPE Injection Molding Resin Features: Excellent processability for applications requiring good stiffness and toughness, good cold temperature impact properties.Applications: Food containers and lids, frozen food containers.Dat.. |
|||
Tensile Strength, Yield | 29.0 MPa | 4210 psi | ASTM D638 |
NOVA Chemicals Sclair® 58D HDPE Blow Molding Resin
(discontinued **) Features: Good ESCR, high stiffness, good impact strength, slightly tougher alternative to Sclair 58A.Applications: Small part blow molding, food, pharmaceuticals, HIC containers.Data provided by th.. |
|||
Tensile Strength, Yield | 29.0 MPa | 4210 psi | ASTM D638 |
Ineos ABS Centrex® 401 AES Extrusion
(discontinued **) Properties tested in transverse direction (worst case) on 125-mil (3.2 mm) extruded sheets specimens with |
|||
Tensile Strength, Yield | 29.0 - 68.9 MPa | 4210 - 10000 psi | Average value: 32.2 MPa Grade Count:17 |
Overview of materials for ECTFE Fluoropolymer This property data is a summary of similar materials in the MatWeb database for the category "ECTFE Fluoropolymer". Each property range of values reported is minimum and maximum values of appropriat.. |
|||
Tensile Strength, Yield | 29.0 MPa | 4210 psi | ASTM D638 |
Flint Hills 23S1Acs256 Random Copolymer Polypropylene Features: High contact clarity, blush resistant, good impact and flexural modulus. Product does not contain animal derived components.Applications: Blow molded articles - Food, health, medical an.. |
|||
Tensile Strength, Yield | 29.0 MPa | 4210 psi | ASTM D638 |
LG Chemical LUPOL GP-3154F General Purpose Polypropylene, 15% Mineral Fillers, High Modulus, Flame Retardant LUPOL resins, based on polyolefin with a wide range of characteristics, are a family of low cost engineering plastics.Applications: Automotive: Bumper cover, instrument panel, glove box, air cleaner.. |
|||
Tensile Strength, Yield | 29.0 MPa | 4210 psi | ISO 527 |
Iran Petrochemical (PCC) I3S HC 7260(THE) High Density Polyethylene I3 is a high density polyethylene with 1-Butene as co monomer. It has low warpage, good flowability, high density, hardness and stiffness, good impact strength, and good stress cracking resistance... |
|||
Tensile Strength, Yield | 29.0 MPa | 4210 psi | 2 in/min; ASTM D638 |
A. Schulman PP 3475-01 Polypropylene High Melt Homopolymer Polypropylene DescriptionPolypropylene PP 3475-01 Natural is a high melt homopolymer polypropylene with consistent general purpose homopolymer characteristics. Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 29.0 MPa | 4210 psi | ASTM D638 |
Washington Penn PPH4CF2.5 Polypropylene, 25% Calcium Carbonate Filled UV Stabilized; Injection molding grade.Applications: High flow for thin wall parts requiring long-flow. Outdoor furniture.Data provided by Washington Penn Plastic Co., Inc. |
|||
Tensile Strength, Yield | 29.0 MPa | 4210 psi | ASTM D638 |
A. Schulman POLYFORT™ FPP 1237 CaCO3 filled homopolymer polypropylene DescriptionPolyfort® FPP 1237 is a 20% CAC03 filled homopolymer polypropylene product. Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 29.0 MPa | 4200 psi | ASTM D638 |
Westlake Plastics Propylux® Void-Free Polypropylene Propylux is made from polypropylene resin. Among its most notable characteristics are its mechanical toughness, chemical resistance and resistance to abrasion. These properties make it suitable fo.. |
|||
Tensile Strength, Yield | 29.0 MPa | 4210 psi | ASTM D638 |
A. Schulman POLYFORT™ FPP 1237 CaCO3 filled homopolymer polypropylene DescriptionPolyfort® FPP 1237 is a 20% CAC03 filled homopolymer polypropylene product. Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 29.0 MPa | 4210 psi | ISO 527-2 |
Total PPC 3645 Polypropylene, Heterophasic Copolymer ATOFINA Polypropylene PPC 3645 is a nucleated heterophasic copolymer. PPC 3645 is characterized by improved stiffness, creep resistance and high impact resistance.ApplicationPPC 3645 has been devel.. |
|||
Tensile Strength, Yield | 29.0 MPa | 4200 psi | 2" (50mm) per min; ASTM D638 |
Formosa Plastics Formolene® 3335E Random Copolymer Polypropylene Random Copolymer for Clear Storage Boxes, Pill Vials and Containers Formolene® 3335E is a high melt flow random copolymer with fast cycle time and easy mold release. It is designed for injection mo.. |
|||
Tensile Strength, Yield | 29.0 MPa | 4210 psi | ASTM D638 |
A. Schulman POLYFORT™ FPP 1609 Mica Fortified Copolymer Polypropylene DescriptionPolyfort® FPP 1609 is a 10% mica fortified copolymer polypropylene product. Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 29.0 MPa | 4200 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 20 PHR Suprex Clay Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 29.0 MPa | 4210 psi | ASTM D 638 |
Cossa Polimeri ESTASTIR HG 0808 Polystyrene High gloss polystyreneHigh impact resistance, good physical and mechanical characteristics, good processabilityInformation provided by Cossa Polimeri S.r.l. |
|||
Tensile Strength, Yield | 29.0 MPa | 4210 psi | 2 in/min, Type IV bar; ASTM D638 |
Chevron Phillips Marlex® K605 HDPE Blow Molding Resin Resin Type: Ethylene HomopolymerCharacteristics: Good ESCRExceptional rigidityExcellent melt strengthApplications: Automotive bumper beamsInformation provided by Chevron Phillips. |
|||
Tensile Strength, Yield | 29.0 MPa | 4210 psi | ASTM D638 |
Aclo Accutech Polypropylene Homopolymer HP0336C30L1 Calcium Reinforced |
|||
Tensile Strength, Yield | 29.0 MPa | 4210 psi | ASTM D638 |
Aclo Accutech Polypropylene HP0335T40V Homopolymer Talc Reinforced Approved to ESF-M4D355B White B12391 |
|||
Tensile Strength, Yield | 29.0 MPa | 4210 psi | ISO R 527 |
Addiplast Addilene J 510 Polypropylene Copolymer UnreinforcedInformation provided by Addiplast. |
|||
Tensile Strength, Yield | >= 29.0 MPa | >= 4200 psi | ASTM D638 |
Buckeye Polymers BP RPP 2008 T NAT Polypropylene, Talc Filled Product Information: Our Talc filled product lines exhibit excellent properties such as high stiffness, surface aesthetics, low coefficient of thermal expansion, low shrinkage, improved scratch and .. |
|||
Tensile Strength, Yield | 29.0 - 234 MPa | 4200 - 34000 psi | Average value: 104 MPa Grade Count:192 |
Overview of materials for Nylon 6, Heat Stabilized This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Heat Stabilized". Each property range of values reported is minimum and maximum values of appro.. |
|||
Tensile Strength, Yield | 29.0 MPa | 4210 psi | ASTM D638 |
Ineos Nova 5711 High Impact Polystyrene
(discontinued **) High flow, High impact, USP Class VIApplications: Thin wall, Medical, Housewares, ToysProperties were determined on injection molded specimens at 23°C and 50% R.H. unless otherwise specified.Inform.. |
|||
Tensile Strength, Yield | 29.0 MPa | 4210 psi | ISO 527-2 |
Borealis MB350WG Polypropylene Compound, Mineral Filled MB350WG is a 30% mineral filled polypropylene compound intended for injection molding. This material has a very high impact strength while maintaining good stiffness and is easy to process. Applic.. |
|||
Tensile Strength, Yield | 29.0 MPa | 4210 psi | |
BASF Novolen® 3248 RC Polypropylene Grade containing nucleating and antistatic agents for injection molded parts.Data was collected by ISO methods and provided by BASF. |
|||
Tensile Strength, Yield | 29.0 MPa | 4210 psi | ASTM D638 |
NOVA Chemicals Sclair® 2915 HDPE Injection Molding Resin
(discontinued **) Features: Excellent balance of stiffness and toughness, low odor, permits light weight container design.Applications: Thin walled food containers, frozen food containers.Data provided by the manufac.. |