- Polymer Property : Tensile Strength, Yield = 207 MPa
Polymer Property : Tensile Strength, Yield = 207 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 207 MPa | 30000 psi | ASTM D638 |
| Oxford Polymers Oxnilon 6-50GF 50% Glass Fiber Filled Nylon 6 for Injection Molding 50% Glass Fiber Filled Nylon 6 for Injection MoldingInformation provided by Oxford Polymers. |
|||
| Tensile Strength, Yield | 207 MPa | 30000 psi | |
| Pacific Sintered Materials FN-255-S Nickel Steel Powdered Metal Good impact resistant mechanical components. Good hardenability.Equivalent MPIF Specification: FN-0205-25All information provided by Pacific Sintered Metals. |
|||
| Tensile Strength, Yield | 207 MPa | 30000 psi | ASTM D638 |
| Polymer Resources NY6-G50 Nylon 6, 50% Glass Reinforced Nylon 6, 50% Glass Reinforced, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are teste.. |
|||
| Tensile Strength, Yield | 207 MPa | 30000 psi | ASTM D638 |
| Solvay Specialty Polymers Kadel® E-1230 Polyketone
(discontinued **) Electrical Conductor. High performance proprietary semi-crystalline polymer based resins with exceptional solvent resistance and high temperature performance. They provide strength and stiffness, p.. |
|||
| Tensile Strength, Yield | 207 MPa @Strain 0.200 % |
30000 psi @Strain 0.200 % |
|
| FloMet Fe-50%Co Soft Magnetic Alloy FloMet provides precision miniature components through metal injection molding (MIM). Metal powders are mixed with thermoplastic binders to form a homogeneous mixture, with approximately 60% volume.. |
|||
| Tensile Strength, Yield | 207 MPa | 30000 psi | ASTM D638 |
| Techmer ES HiFill® PA6 GF50 L BN047 LE 50% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 50% Filler by WeightAdditive: LubricantFeatures: Low Extractables and LubricatedAppearance: BeigeInformation.. |
|||
| Tensile Strength, Yield | 207 MPa | 30000 psi | ASTM D638 |
| Techmer ES HiFill® PA6/6 GF60 HS L BK 60% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 60% Filler by WeightAdditive: Lubricant and Heat StabilizerFeatures: Lubricated and Heat StabilizedUL File N.. |
|||
| Tensile Strength, Yield | 207 MPa | 30000 psi | ASTM D638 |
| Techmer ES HiFill® PEEK CF20 TL15 HF 20% Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber Reinforcement, 20% Filler by WeightAdditive: LubricantFeatures: High Flow and LubricatedInformation provided by TP Composi.. |
|||
| Tensile Strength, Yield | 207 MPa | 30000 psi | ASTM D638 |
| Techmer ES Luriblend® PA6/6 GF30 ML HS 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 30% Filler by WeightAdditive: Heat Stabilizer and Molybdenum Disulfide LubricantFeatures: Lubricated and Heat StabilizedIn.. |
|||
| Tensile Strength, Yield | 207 MPa | 30000 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP STAT-KON RE0069S PA 66 LNP* STAT-KON* RE0069S is a compound based on Nylon 66 resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant, Heat Stabilized. |
|||
| Tensile Strength, Yield | 207 MPa | 30000 psi | ISO 527 |
| SABIC Innovative Plastics LNP STAT-KON REF42 PA 66 LNP* STAT-KON* REF42 is a compound based on Nylon 66 resin containing 20% Glass Fiber, 10% Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
| Tensile Strength, Yield | 207 MPa | 30000 psi | ASTM D638 |
| Techmer ES HiFill® PA4/6 CF40 IM HS 40% Carbon Filled (Conditioned) Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber Reinforcement, 40% Filler by WeightAdditive: Heat StabilizerFeatures: Heat StabilizedInformation provided by TP Composites.. |
|||
| Tensile Strength, Yield | 207 MPa | 30000 psi | ASTM D638 |
| Techmer ES HiFill® PA6/6 GF60 HS L 60% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 60% Filler by WeightAdditive: Lubricant and Heat StabilizerFeatures: Lubricated and Heat StabilizedUL File N.. |
|||
| Tensile Strength, Yield | >= 207 MPa | >= 30000 psi | 0.2% Offset |
| Eagle Brass 301 Austenitic Stainless Steel, Annealed Type 301 is a chromium-nickel stainless steel that provides high strength and good ductility with chromium and nickel contents lowered to increase the work hardening range. This permits higher tens.. |
|||
| Tensile Strength, Yield | >= 207 MPa | >= 30000 psi | 0.2% Offset |
| Eagle Brass 302 Austenitic Stainless Steel, Annealed Types 302 is a widely used variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled.Information provided by Eagle Brass Compa.. |
|||
| Tensile Strength, Yield | >= 207 MPa | >= 30000 psi | 0.2% Offset |
| Eagle Brass 316 Austenitic Stainless Steel, Annealed The Mo addition increases general corrosion resistance to pitting from chloride ion solutions, and provides increased strength at elevated temperatures. Properties are similar to those of Type 304 .. |
|||
| Tensile Strength, Yield | 207 - 303 MPa | 30000 - 44000 psi | 0.2% offset |
| Eagle Brass 102 OF COPPER (Non-Certified), 1/2 Hard Alloy 102 is an oxygen-free copper which has better forming, resistance to hydrogen embrittlement, and brazing characteristics than C110 ETP. C102 has good solder-ability and corrosion resistance an.. |
|||
| Tensile Strength, Yield | >= 207 MPa | >= 30000 psi | 0.2% Offset |
| Eagle Brass 304 Austenitic Stainless Steel, Annealed Types 304 is a widely used variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled.Information provided by Eagle Brass Compa.. |
|||
| Tensile Strength, Yield | >= 207 MPa @Strain 0.200 % |
>= 30000 psi @Strain 0.200 % |
|
| Carlson 317L 4 Austenitic Stainless Steel General DescriptionCarlson’s 317L, 317L 4, and 317L 4N are austenitic chromium-nickel-molybdenum stainless steels with alloy contents greater than the 316 grades. The additional chromium, nickel a.. |
|||
| Tensile Strength, Yield | >= 207 MPa @Strain 0.200 % |
>= 30000 psi @Strain 0.200 % |
|
| Carlson 317L Austenitic Stainless Steel Carlson’s 317L, 317L 4, and 317L 4N are austenitic chromium-nickel-molybdenum stainless steels with alloy contents greater than the 316 grades. The additional chromium, nickel and molybdenum prese.. |
|||
| Tensile Strength, Yield | >= 207 MPa @Strain 0.200 % |
>= 30000 psi @Strain 0.200 % |
|
| Carlson 330 Austenitic Alloy General DescriptionCarlson Alloy 330 is a nickel-iron-chromium-silicon austenitic alloy. It combines high strength with excellent resistance to carburization and oxidation at temperatures to 2200°.. |
|||
| Tensile Strength, Yield | 207 MPa | 30000 psi | |
| AK Steel Cold Rolled Carbon Steel, Commercial Steel (CS Type B), Standard Grade May be moderately formed. A specimen cut in any direction can be bent flat on itself without cracking.Information provided by AK Steel |
|||
| Tensile Strength, Yield | 207 MPa | 30000 psi | Typical |
| Alpase M-1™ Aluminum Mold Plate M-1™ features and benefits include: Dimensional stability, fully weldable, anodizable, consistent hardness - regardless of size, can be nickel plated, good machinability, no heat treatment required.. |
|||
| Tensile Strength, Yield | 207 MPa @Strain 0.200 % |
30000 psi @Strain 0.200 % |
|
| ATI Allvac® Nickelvac® 601 UNS N06601 Nickel Superalloy Uses: Weld wire, woven wire mesh belts, rod for heat treat baskets, heat treat fixtures.Property values are for samples in the metallurgical condition: 1950°C anneal.Information provided by Allvac,.. |
|||
| Tensile Strength, Yield | 207 MPa @Strain 0.200 %, Temperature 316 °C |
30000 psi @Strain 0.200 %, Temperature 601 °F |
|
| Carpenter Gall-Tough® Stainless Data provided by Carpenter Technology Corporation.6.4 mm diameter tensile specimens from center of 25.4 mm diameter bar annealed 1066°C 1 hour, water quenched, and ground.Threshold Galling Stress 1.. |
|||
| Tensile Strength, Yield | 207 MPa @Strain 0.200 %, Temperature 371 °C |
30000 psi @Strain 0.200 %, Temperature 700 °F |
|
| Carpenter Gall-Tough® Stainless Data provided by Carpenter Technology Corporation.6.4 mm diameter tensile specimens from center of 25.4 mm diameter bar annealed 1066°C 1 hour, water quenched, and ground.Threshold Galling Stress 1.. |
|||
| Tensile Strength, Yield | 207 MPa @Temperature 427 °C |
30000 psi @Temperature 801 °F |
Annealed |
| ATI Allegheny Ludlum Allcorr® Nickel-Based, Corrosion Resistant Alloy Characteristics: non-age hardenable; outstanding resistance to general corrosion, pitting corrosion, crevice corrosion, intergranular corrosion, and stress corrosion cracking; high strength; high du.. |
|||
| Tensile Strength, Yield | 207 MPa | 30000 psi | ISO 527 |
| SABIC Innovative Plastics LNP STAT-KON REF42 PA 66 (Asia Pacific) LNP* Stat-kon* REF42 is a compound based on Nylon 66 resin containing Glass Fiber, Carbon Fiber. |
|||
| Tensile Strength, Yield | 207 MPa | 30000 psi | ASTM D638 |
| Techmer ES HiFill FR® PA6/6 GF50 FR-N BK 50% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 50% Filler by WeightFeatures: Flame Retardant and Halogen FreeAppearance: BlackInformation provided by TP Composites, Inc... |
|||