Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 126 MPa | 18300 psi | ASTM D638 |
Polymer Resources PPX-MF-FRG20 Modified-PPO, 40% Glass/Mineral Reinforced, Flame Retardant Modified-Polyphenylene Oxide, 40% Glass/Mineral Reinforced, Flame RetardantFeatures: • Bromine Free • Chlorine Free • Self ExtinguishingProcess: Injection MoldingNotes: All physical, mechanica.. |
|||
Tensile Strength, Yield | 126 MPa | 18300 psi | ASTM D638 |
Solvay Specialty Polymers Veradel® AG-230 Polyethersulfone
(discontinued **) For superior long-term performance at high temperatures in severe service environments. It offers especially good toughness, hydrolytic stability, chemical resistance, plus FDA and USDA compliance.N.. |
|||
Tensile Strength, Yield | 126 MPa | 18300 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP WFL28 PBT (Europe-Africa-Middle East) LNP* LUBRICOMP* WFL28 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, PTFE. Added features include: Internally Lubricated. |
|||
Tensile Strength, Yield | 126 MPa | 18300 psi | ASTM D638 |
Techmer ES Electrablend® PC NCF15 FR 15% Nickel-Coated Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Nickel-Coated Carbon Fiber Reinforcement, 20% Filler by WeightFeatures: Electromagnetic Shielding (EMI) and Flame RetardantInformation .. |
|||
Tensile Strength, Yield | 126 MPa | 18300 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON DEL139P PC LNP* STAT-KON* DEL139P is a compound based on Polycarbonate containing 15% Carbon Fiber, 5% PTFE. Added features of this grade include: Electrically Conductive, Exceptional Processing, Flame Retar.. |
|||
Tensile Strength, Yield | 126 MPa | 18300 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON DEL13EXC PC LNP STAT-KON* DEL13EXC is a compound based on Polycarbonate resin containing 15% Carbon Fiber, 5% PTFE. Added features of this material include: Easy Molding, Electrically Conductive, Wear Resistan.. |
|||
Tensile Strength, Yield | 126 MPa | 18300 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP LF004E PEEK (Asia Pacific) LNP* Thermocomp* LF004E is a compound based on Polyetheretherketone resin containing Glass Fiber. Added features of this material include: Easy Molding. |
|||
Tensile Strength, Yield | 126 MPa | 18300 psi | SABIC - Japan Method |
SABIC Innovative Plastics NORYL PX2956 PPE+PS (Asia Pacific) PPE+PS GF+Mineral Filler total 35% FR V-0 |
|||
Tensile Strength, Yield | 126 MPa | 18300 psi | ISO 527 |
SABIC Innovative Plastics LNP STAT-KON RE0029 PA 66 LNP* STAT-KON* RE0029 is a compound based on Nylon 66 resin containing 10% Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant. |
|||
Tensile Strength, Yield | 126 MPa @Temperature -40.0 °C |
18300 psi @Temperature -40.0 °F |
ASTM Test |
BASF Ultramid® 8202 HS PA6 (Dry) Ultramid 8202 HS is a heat stabilized, low viscosity, general purpose nylon 6 injection molding homopolymer. It possesses the combination of strength and toughness and has excellent chemical and ab.. |
|||
Tensile Strength, Yield | 126 MPa @Temperature -40.0 °C |
18300 psi @Temperature -40.0 °F |
ISO Data |
BASF Ultramid® 8202 HS PA6 (Dry) Ultramid 8202 HS is a heat stabilized, low viscosity, general purpose nylon 6 injection molding homopolymer. It possesses the combination of strength and toughness and has excellent chemical and ab.. |
|||
Tensile Strength, Yield | 126 MPa @Temperature -40.0 °C |
18300 psi @Temperature -40.0 °F |
ASTM Test |
BASF Ultramid® 8202 PA6 (Dry) Ultramid 8202 is a low viscosity, general purpose polyamide 6 injection molding homopolymer exhibiting excellent melt fluidity for filling thin sections. It is also available in heat stabilized (Ult.. |
|||
Tensile Strength, Yield | 126 MPa @Temperature -40.0 °C |
18300 psi @Temperature -40.0 °F |
ISO Data |
BASF Ultramid® 8202 PA6 (Dry) Ultramid 8202 is a low viscosity, general purpose polyamide 6 injection molding homopolymer exhibiting excellent melt fluidity for filling thin sections. It is also available in heat stabilized (Ult.. |
|||
Tensile Strength, Yield | 126 MPa | 18300 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP DX07408 PC LNP* THERMOCOMP* DX07408 is a compound based on Polycarbonate containing Proprietary Filler(s). Added feature of this grade is: UL Rated. |