Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ISO 527-3 |
Polimeri Europa Clearflex® H&T FGH 196 Hexene Copolymer Linear Low Density Polyethylene Clearflex H&T FGH 196 is a hexene copolymer linear low density polyethylene (C6-LLDPE), with antioxidants and processing aid, suitable for blown film extrusion.Films obtained from Clearflex H&T FGH .. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ISO 527-3 |
Polimeri Europa Flexirene® FH 56 A Butene Copolymer Linear Low Density Polyethylene Flexirene FH 56 A is a butene copolymer with medium density (C4-LLDPE), with antioxidants and processing aid, suitable for blown film extrusion.Films manufactured with Flexirene FH 56 A are characte.. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ISO 527-3 |
Polimeri Europa Clearflex® FG B0 Very Low Density Polyethylene Clearflex FG B0 is a linear low density polyethylene, with antioxidants, suitable for blown film technology.Films made with Clearflex FG B0 are highly transparent, have good sealing properties, even.. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ISO 527-3 |
Polimeri Europa Clearflex® H&T LGH 138 Octene Copolymer Linear Low Density Polyethylene Clearflex H&T LGH 138 is an octene copolymer linear low density polyethylene (C8-LLDPE), with antioxidants, slip agent, antiblocking and processing aid, suitable for blown film extrusion.Films obtai.. |
|||
Film Tensile Strength at Break, MD | 40.0 - 42.0 MPa | 5800 - 6090 psi | Average value: 41.0 MPa Grade Count:4 |
Overview of materials for Nylon 66/6 This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6". Each property range of values reported is minimum and maximum values of appropriate MatWeb .. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
LyondellBasell Petrothene® GA501020 Linear Low Density Polyethylene ApplicationsPETROTHENE GA 501series of resins are pelletized linear low density polyethylene for film extrusion applications requiring excellent drawdown and toughness. These resins have excellent .. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
LyondellBasell Petrothene® GA501021 Linear Low Density Polyethylene ApplicationsPETROTHENE GA 501series of resins are pelletized linear low density polyethylene for film extrusion applications requiring excellent drawdown and toughness. These resins have excellent .. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
LyondellBasell Petrothene® GA501022 Linear Low Density Polyethylene ApplicationsPETROTHENE GA 501series of resins are pelletized linear low density polyethylene for film extrusion applications requiring excellent drawdown and toughness. These resins have excellent .. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
Iran Petrochemical (PCC) LL 18XF5 N Linear Low Density Polyethylene LL 18XF5 N is a terpolymer of ethylene, propylene and butene-1 for high film strength applications, especially heavy duty shipping sacks, ice bags, frozen food bags, potato bags, and agriculture fil.. |
|||
Film Tensile Strength at Break, MD | 40.0 - 60.0 MPa | 5800 - 8700 psi | ISO 527-3 |
Borealis BA11CF Polypropylene Copolymer BA110CF is a heterophasic copolymer. This grade is suitable for use on chill roll processes. This grade is suitable for the manufacturing of unoriented films on cast and tubular quench film lines. .. |
|||
Film Tensile Strength at Break, MD | 40.0 - 60.0 MPa | 5800 - 8700 psi | ISO 527-3 |
Borealis BB213CF Polypropylene Copolymer BB213CF is a heterophasic copolymer. This grade is suitable for the manufacturing of unoriented films on cast and tubular quench film lines. Applications: BB213CF is recommended for food packaging.. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | |
UBE 5033FDX27 Air Blown Nylon 6/66 Film Specialties: High slip typeMedium shrinkApplications: General purposeSuitable for Water cooling processProcessing: Sausage casings (Water)Big bag (Air blown)Information provided by UBE. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | |
Dow DOWLEX™ 2071 Linear Low Density Polyethylene DOWLEX® 2071 Polyethylene resin is a linear low density polyethylene resin specifically designed for the manufacture of high strength, thin gauge films for use in applications such as grocery sacks.. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
Dow ELITE™ 5220G Enhanced Polyethylene Resin High impact and puncture resistance Excellent on-pallet load elongation for higher yields on regular loads Complies with U.S. FDA 21 CFR 177.1520 (c) 3.2a Information provided by Dow |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM-D882 |
Braskem FL31 LLDPE Cast Film Extrusion Polyethylene Copolymer FL31 is a linear low-density polyethylene, copolymer of butene-1, produced by the solution process. It was developed for cast film extrusion. Films obtained with this product show a good processing .. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM-D882 |
Braskem GM9450F HDPE Blown Film Extrusion Polyethylene HDPE GM9450F is a high-density polyethylene developed for the high molecular weight film extrusion segment produced with bimodal technology. The film produced from this resin has high tenacity and e.. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
Braskem Green PE SLH118 Blow Film Extrusion and Cast Film Extrusion Linear Low Density Polyethylene Description: SLH118 is a Linear Low Density Polyethylene, copolymer of hexene-1. Developed for blown film extrusion in blends with polyethylenes. Films obtained with this product show a good process.. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
Braskem Green PE SLH218 Blow Film Extrusion and Cast Film Extrusion Linear Low Density Polyethylene Description: SLH218 is a LLDPE Hexene copolymer produced by Braskem. It shows a good balance between optical properties, mechanical properties (Mainly stretchability), sealability and processability.. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
Braskem Green PE SLL118/21 Blow Film Extrusion and Cast Film Extrusion Linear Low Density Polyethylene Description: SLL118/21 is a LLDPE Butene copolymer produced by Braskem. It is a general purpose product that shows a good processing performance balanced with good optical and mechanical properties .. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
Braskem Green PE SLL218 Blow Film Extrusion and Cast Film Extrusion Linear Low Density Polyethylene Description: SLL218 is a Linear Low Density Polyethylene, copolymer of butene-1. Developed for cast film extrusion. Films obtained with this product show a good processing performance balanced with .. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
Braskem LH 218 LLDPE Cast Film Extrusion Polyethylene 38µm film gauge, obtained in 40mm extruder, with blow up ratio 2, 2:1Applications: Stretch film; shrink film; "liners"; general purpose; HDPE and LDPE blends. Information provided by Braskem |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
Braskem LH218 Cast Film Extrusion Linear Low Density Polyethylene Description: LH218 is a LLDPE Hexene copolymer produced by Braskem. It shows a good balance between optical properties, mechanical properties (Mainly stretchability), sealability and processability... |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
Braskem LHB 118/21 AF LLDPE Blown Film Extrusion Polyethylene Description: LHB118/21 AF is a LLDPE copolymer produced by Braskem. It is a ready-to-use product since it contains 10% LDPE. Its additive package was optimized to avoid blocking, even at low thickne.. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
Braskem LL 218 LLDPE Cast Film Extrusion Polyethylene Description: LL218 is a Linear Low Density Polyethylene, copolymer of butene-1, produced by Spherilene process. Developed for cast film extrusion. Films obtained with this product show a good proces.. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
Braskem LL218 Cast Film Extrusion Linear Low Density Polyethylene Stretch films; Liners; LDPE and HDPE blends; Packages for general use.Information provided by Braskem. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM-D882 |
Braskem LL6802N LLDPE Blown Film Extrusion Polyethylene Copolymer LL6802N resin is a linear low-density polyethylene, copolymer of octene-1, produced by the solution process for blown film extrusion with excellent mechanical properties. It contains processing aid .. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM-D882 |
Braskem LL6901S LLDPE Blown Film Extrusion Polyethylene Copolymer LL6901S is a LLDPE Butene copolymer produced by Braskem. It is a ready to use product since it's been compounded with 15% LDPE. It is a general purpose product that shows a good processing performan.. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
Braskem BF0323/12HC Blown Film Extrusion Low Density Polyethylene Shrink films; Automatic packaging of liquid products (FFS).Additives: Antiblock, DInformation provided by Braskem. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
ExxonMobil Exceed™ 2018EB Blown Film Resin
(discontinued **) Exceed 2018EB resin is an ethylene based polymer produced with metallocene single site catalysts using ExxonMobil Chemicals Exxpol® Technology. The higher melt index makes this polymer ideally sui.. |
|||
Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
Braskem BF0323HC Blown Film Extrusion Low Density Polyethylene Heavy-duty bags; Agriculture, Coextruded and shrink films for pallets.Information provided by Braskem. |