Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 370 MPa @Strain 0.200 % |
53700 psi @Strain 0.200 % |
Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1 |
Outokumpu 253MA® High Temperature Austenitic Stainless Steel Variant of 1.4828 with increased nitrogen content and has been microalloyed with rare earth metals (REM). The most suitable temperature range is 850-1100°C, because structural changes when used be.. |
|||
Tensile Strength, Yield | 370 MPa @Strain 1.00 % |
53700 psi @Strain 1.00 % |
Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1 |
Outokumpu 4724 High Temperature Ferritic Stainless Steel Truly stainless high temperature grade with 13% chromium. Not critical in terms of embrittlement.Applications: Mostly used in high temperature applications with sulphurous atmospheres and/or low te.. |
|||
Tensile Strength, Yield | 370 MPa @Strain 1.00 % |
53700 psi @Strain 1.00 % |
Typical after Solution Annealing |
Industeel SIRIUS S15 Rare Earth Containing Heat Resistant Steel CLI SIRIUS S15 grade is a fully austenitic stainless steel containing 21 Cr, 1.7 Si, 0.17 N and Rare Earth elements (Cerium, Lanthanum,...etc) which make the alloy particularly well designed for hig.. |
|||
Tensile Strength, Yield | 370 MPa @Strain 0.200 %, Thickness 152.4 - 203.2 mm |
53700 psi @Strain 0.200 %, Thickness 6.000 - 8.000 in |
Typical Strength |
Constellium Alumold® 400 Aluminum The Alumold®-400 alloy has been optimized to provide good shape stability and high strength properties throughout the plate thickness. Typical applications include blow moulds, thermoforming moulds.. |
|||
Tensile Strength, Yield | >= 370 MPa @Strain 0.200 %, Thickness 38.1 - 76.2 mm |
>= 53700 psi @Strain 0.200 %, Thickness 1.50 - 3.00 in |
Tempers T651 / T652 |
Constellium Alumold® 400 Aluminum The Alumold®-400 alloy has been optimized to provide good shape stability and high strength properties throughout the plate thickness. Typical applications include blow moulds, thermoforming moulds.. |
|||
Tensile Strength, Yield | >= 370 MPa @Strain 0.200 %, Thickness 76.2 - 127 mm |
>= 53700 psi @Strain 0.200 %, Thickness 3.00 - 5.00 in |
Tempers T651 / T652 |
Constellium Alumold® 400 Aluminum The Alumold®-400 alloy has been optimized to provide good shape stability and high strength properties throughout the plate thickness. Typical applications include blow moulds, thermoforming moulds.. |
|||
Tensile Strength, Yield | >= 370 MPa @Strain 0.200 %, Thickness 300 - 400 mm |
>= 53700 psi @Strain 0.200 %, Thickness 11.8 - 15.7 in |
long-transverse direction |
Constellium Alumold® 500 Forged Aluminum Forged thick blocks in Alumold® 500 have been developed to provide high and consistent strength across the thickness, good dimensional stability and excellent machinability, in order to respond to .. |
|||
Tensile Strength, Yield | >= 370 MPa @Strain 0.200 %, Thickness 325 - 400 mm |
>= 53700 psi @Strain 0.200 %, Thickness 12.8 - 15.7 in |
Temper T652 |
Constellium Certal® SPC Forged Aluminum Certal® SPC forged has been optimized to provide excellent machinability, good shape stability and high strength properties throughout the plate thickness. Uniform strength is an important property.. |
|||
Tensile Strength, Yield | 370 MPa @Strain 0.200 %, Thickness 5.90 - 15.0 mm |
53700 psi @Strain 0.200 %, Thickness 0.232 - 0.591 in |
Typical Strength |
Constellium Unidal® High-Strength Rolled Precision Aluminum Plate, Milled Both Sides Unidal® precision plates offers a combination of dimensional stability and high mechanical strength. The very low internal stress reduces the risk of deformation during machining, thereby reducing .. |
|||
Tensile Strength, Yield | 370 MPa @Strain 0.200 %, Thickness 12.7 mm |
53700 psi @Strain 0.200 %, Thickness 0.500 in |
|
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |