Constellium Certal® SPC Forged Aluminum

Category Metal , Nonferrous Metal , Aluminum Alloy , 7000 Series Aluminum Alloy
Manufacturer Constellium
Trade Name Certal®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Constellium Certal® SPC Forged Aluminum.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Certal® SPC forged has been optimized to provide excellent machinability, good shape stability and high strength properties throughout the plate thickness. Uniform strength is an important property in many types of applications. Typical applications include compression or injection moulds for plastics.Information provided by manufacturer
Physical Properties Metric English Comments
Density 2.82 g/cc
0.102 lb/in³
Mechanical Properties Metric English Comments
Hardness, Brinell 140

@Thickness 450 - 700 mm
 140

@Thickness 17.7 - 27.6 in
 Temper T652
150

@Thickness 400 - 450 mm
 150

@Thickness 15.7 - 17.7 in
 Temper T652
155

@Thickness 325 - 400 mm
 155

@Thickness 12.8 - 15.7 in
 Temper T652
Tensile Strength >= 410 MPa

@Thickness 450 - 700 mm
 >= 59500 psi

@Thickness 17.7 - 27.6 in
 Temper T652
>= 430 MPa

@Thickness 400 - 450 mm
 >= 62400 psi

@Thickness 15.7 - 17.7 in
 Temper T652
>= 450 MPa

@Thickness 325 - 400 mm
 >= 65300 psi

@Thickness 12.8 - 15.7 in
 Temper T652
480 MPa

@Thickness 450 - 700 mm
 69600 psi

@Thickness 17.7 - 27.6 in
 Temper T652
520 MPa

@Thickness 325 - 400 mm
 75400 psi

@Thickness 12.8 - 15.7 in
 Temper T652
520 MPa

@Thickness 400 - 450 mm
 75400 psi

@Thickness 15.7 - 17.7 in
 Temper T652
Tensile Strength, Yield >= 340 MPa

@Strain 0.200 %,
Thickness 450 - 700 mm
 >= 49300 psi

@Strain 0.200 %,
Thickness 17.7 - 27.6 in
 Temper T652
>= 350 MPa

@Strain 0.200 %,
Thickness 400 - 450 mm
 >= 50800 psi

@Strain 0.200 %,
Thickness 15.7 - 17.7 in
 Temper T652
>= 370 MPa

@Strain 0.200 %,
Thickness 325 - 400 mm
 >= 53700 psi

@Strain 0.200 %,
Thickness 12.8 - 15.7 in
 Temper T652
420 MPa

@Strain 0.200 %,
Thickness 450 - 700 mm
 60900 psi

@Strain 0.200 %,
Thickness 17.7 - 27.6 in
 Typical Strength
460 MPa

@Strain 0.200 %,
Thickness 325 - 400 mm
 66700 psi

@Strain 0.200 %,
Thickness 12.8 - 15.7 in
 Typical Strength
460 MPa

@Strain 0.200 %,
Thickness 400 - 450 mm
 66700 psi

@Strain 0.200 %,
Thickness 15.7 - 17.7 in
 Typical Strength
Elongation at Break >= 3.0 %

@Thickness 325 - 400 mm
 >= 3.0 %

@Thickness 12.8 - 15.7 in
 Temper T652
>= 3.0 %

@Thickness 400 - 450 mm
 >= 3.0 %

@Thickness 15.7 - 17.7 in
 Temper T652
>= 3.0 %

@Thickness 450 - 700 mm
 >= 3.0 %

@Thickness 17.7 - 27.6 in
 Temper T652
7.0 %

@Thickness 400 - 450 mm
 7.0 %

@Thickness 15.7 - 17.7 in
 Typical Elongation
7.0 %

@Thickness 450 - 700 mm
 7.0 %

@Thickness 17.7 - 27.6 in
 Typical Elongation
8.0 %

@Thickness 325 - 400 mm
 8.0 %

@Thickness 12.8 - 15.7 in
 Typical Elongation
Modulus of Elasticity 72.0 GPa
10400 ksi
tensile
73.0 GPa
10600 ksi
compression
Thermal Properties Metric English Comments
CTE, linear 23.7 µm/m-°C

@Temperature 20.0 - 100 °C
 13.2 µin/in-°F

@Temperature 68.0 - 212 °F
Specific Heat Capacity 0.857 J/g-°C
0.205 BTU/lb-°F
Thermal Conductivity 153 W/m-K
1060 BTU-in/hr-ft²-°F
Component Elements Properties Metric English Comments
Aluminum, Al 89.08 - 92.35 %
89.08 - 92.35 %
as balance
Chromium, Cr <= 0.040 %
<= 0.040 %
Copper, Cu 0.40 - 0.90 %
0.40 - 0.90 %
Iron, Fe <= 0.25 %
<= 0.25 %
Magnesium, Mg 1.5 - 2.3 %
1.5 - 2.3 %
Manganese, Mn <= 0.40 %
<= 0.40 %
Silicon, Si <= 0.15 %
<= 0.15 %
Titanium, Ti <= 0.060 %
<= 0.060 %
Zinc, Zn 5.7 - 6.7 %
5.7 - 6.7 %
Zirconium, Zr 0.050 - 0.12 %
0.050 - 0.12 %