Material Notes:
Forged thick blocks in Alumold® 500 have been developed to provide high and consistent strength across the thickness, good dimensional stability and excellent machinability, in order to respond to the high requirements of the applications in plastics transformation. Typical applications include compression or injection moulds for plastics.Information provided by manufacturer
Physical Properties Metric English Comments
Density 2.82 g/cc
0.102 lb/in³
Mechanical Properties Metric English Comments
Hardness, Brinell 150

@Thickness 450 - 700 mm
 150

@Thickness 17.7 - 27.6 in
 long-transverse direction
160

@Thickness 400 - 450 mm
 160

@Thickness 15.7 - 17.7 in
 long-transverse direction
165

@Thickness 300 - 400 mm
 165

@Thickness 11.8 - 15.7 in
 long-transverse direction
Tensile Strength >= 410 MPa

@Thickness 450 - 700 mm
 >= 59500 psi

@Thickness 17.7 - 27.6 in
 long-transverse direction
>= 430 MPa

@Thickness 400 - 450 mm
 >= 62400 psi

@Thickness 15.7 - 17.7 in
 long-transverse direction
>= 450 MPa

@Thickness 300 - 400 mm
 >= 65300 psi

@Thickness 11.8 - 15.7 in
 long-transverse direction
450 MPa

@Thickness 400 - 450 mm
 65300 psi

@Thickness 15.7 - 17.7 in
 long-transverse direction
480 MPa

@Thickness 450 - 700 mm
 69600 psi

@Thickness 17.7 - 27.6 in
 long-transverse direction
520 MPa

@Thickness 300 - 400 mm
 75400 psi

@Thickness 11.8 - 15.7 in
 long-transverse direction
Tensile Strength, Yield >= 340 MPa

@Strain 0.200 %,
Thickness 450 - 700 mm
 >= 49300 psi

@Strain 0.200 %,
Thickness 17.7 - 27.6 in
 long-transverse direction
>= 350 MPa

@Strain 0.200 %,
Thickness 400 - 450 mm
 >= 50800 psi

@Strain 0.200 %,
Thickness 15.7 - 17.7 in
 long-transverse direction
>= 370 MPa

@Strain 0.200 %,
Thickness 300 - 400 mm
 >= 53700 psi

@Strain 0.200 %,
Thickness 11.8 - 15.7 in
 long-transverse direction
420 MPa

@Strain 0.200 %,
Thickness 450 - 700 mm
 60900 psi

@Strain 0.200 %,
Thickness 17.7 - 27.6 in
 long-transverse direction
460 MPa

@Strain 0.200 %,
Thickness 300 - 400 mm
 66700 psi

@Strain 0.200 %,
Thickness 11.8 - 15.7 in
 long-transverse direction
460 MPa

@Strain 0.200 %,
Thickness 400 - 450 mm
 66700 psi

@Strain 0.200 %,
Thickness 15.7 - 17.7 in
 long-transverse direction
Elongation at Break >= 3.0 %

@Thickness 300 - 400 mm
 >= 3.0 %

@Thickness 11.8 - 15.7 in
 long-transverse direction
>= 3.0 %

@Thickness 400 - 450 mm
 >= 3.0 %

@Thickness 15.7 - 17.7 in
 long-transverse direction
>= 3.0 %

@Thickness 450 - 700 mm
 >= 3.0 %

@Thickness 17.7 - 27.6 in
 long-transverse direction
7.0 %

@Thickness 400 - 450 mm
 7.0 %

@Thickness 15.7 - 17.7 in
 long-transverse direction
7.0 %

@Thickness 450 - 700 mm
 7.0 %

@Thickness 17.7 - 27.6 in
 long-transverse direction
8.0 %

@Thickness 300 - 400 mm
 8.0 %

@Thickness 11.8 - 15.7 in
 long-transverse direction
Modulus of Elasticity 72.0 GPa
10400 ksi
tensile
73.0 GPa
10600 ksi
compression
Poissons Ratio 0.33
0.33
Thermal Properties Metric English Comments
CTE, linear 23.7 µm/m-°C

@Temperature 20.0 - 100 °C
 13.2 µin/in-°F

@Temperature 68.0 - 212 °F
Specific Heat Capacity 0.857 J/g-°C
0.205 BTU/lb-°F
Thermal Conductivity 153 W/m-K
1060 BTU-in/hr-ft²-°F
Descriptive Properties Value Comments
Thermal Diffusivity 63 mm²/s