- Polymer Property : Tensile Strength at Break = 8850 psi
Polymer Property : Tensile Strength at Break = 8850 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 61.0 MPa | 8850 psi | ISO.527 DIN.53455 |
| Omnia Plastica Akulon® PA 66 - Akulon 66 - at 50% RH Polyamide obtained by the polymerisation of Hexamethylenediamine and Adipic acid. It is one of the oldest engineering plastics, having been created in the USA in 1930. Due to its origin it is widely.. |
|||
| Tensile Strength at Break | 61.0 MPa | 8850 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics Lexan® BY2710X PC (Asia Pacific) BY2710X is a modified Polycarbonate (PC) resin. It is a non-filled, injection moldable grade with UL-94 V0 rating and is available in various opaque color options. |
|||
| Tensile Strength at Break | 61.0 MPa | 8850 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics Lexan® EXL1330 PC Copolymer Lexan* EXL1330 polycarbonate (PC) siloxane copolymer resin is a UV stabilized opaque injection molding (IM) and sheet extrusion grade. This resin offers extreme low temperature (-60 C) ductility in .. |
|||
| Tensile Strength at Break | 61.0 MPa | 8850 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics Lexan® EXL1330 PC Copolymer (Asia Pacific) Lexan* EXL1330 polycarbonate (PC) siloxane copolymer resin is a UV stabilized opaque injection molding (IM) and sheet extrusion grade. This resin offers extreme low temperature (-60 C) ductility in .. |
|||
| Tensile Strength at Break | 61.0 MPa | 8850 psi | Type I, 50 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Lexan® EXL1330 PC Copolymer (Europe-Africa-Middle East) Lexan* EXL1330 polycarbonate (PC) siloxane copolymer resin is a UV stabilized opaque injection molding (IM) and sheet extrusion grade. This resin offers extreme low temperature (-60 C) ductility in .. |
|||
| Tensile Strength at Break | 61.0 MPa | 8850 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® EXL1413T PC Copolymer Lexan* EXL1413T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade. This resin offers excellent low temperature (-30 °C) ductility in combination with medium f.. |
|||
| Tensile Strength at Break | 61.0 MPa | 8850 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® EXL1413T PC Copolymer (Asia Pacific) Lexan* EXL1413T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade. This resin offers excellent low temperature (-30 °C) ductility in combination with medium f.. |
|||
| Tensile Strength at Break | 61.0 MPa | 8850 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® EXL1413T PC Copolymer (Europe-Africa-Middle East) Lexan* EXL1413T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade. This resin offers excellent low temperature (-30 °C) ductility in combination with medium f.. |
|||
| Tensile Strength at Break | 61.0 MPa | 8850 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® EXL1433T PC Copolymer (Asia Pacific) Lexan* EXL1433T polycarbonate (PC) siloxane copolymer resin is a UV stabilized transparent injection molding grade. This resin offers excellent low temperature (-30 C) ductility in combination with .. |
|||
| Tensile Strength at Break | 61.0 MPa | 8850 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® EXL1433T PC Copolymer (Europe-Africa-Middle East) Lexan* EXL1433T polycarbonate (PC) siloxane copolymer resin is a UV stabilized transparent injection molding grade. This resin offers excellent low temperature (-30 C) ductility in combination with .. |
|||
| Tensile Strength at Break | 61.0 MPa | 8850 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® EXL1443T PC Copolymer Lexan* EXL1443T polycarbonate (PC) siloxane copolymer resin is an injection molding grade with FDA and EU food contact compliance. This resin offers excellent low temperature (-30 C) ductility in co.. |
|||
| Tensile Strength at Break | 61.0 MPa | 8850 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® EXL1463T PC Copolymer Lexan* EXL1463T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade. This resin offers excellent low temperature (-30 C) ductility in combination with medium flow ch.. |
|||
| Tensile Strength at Break | 61.0 MPa | 8850 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® EXL1463T PC Copolymer (Asia Pacific) Lexan* EXL1463T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade. This resin offers excellent low temperature (-30 C) ductility in combination with medium flow ch.. |
|||
| Tensile Strength at Break | 61.0 MPa | 8850 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® HPX4EU PC Copolymer (Europe-Africa-Middle East) Medium flow specialty polycarbonate - improved processability & autoclavability. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP.. |
|||
| Tensile Strength at Break | 61.0 MPa | 8850 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® SD1278 PC Copolymer Lexan* SD1278 polycarbonate (PC) siloxane copolymer resin is a transparent extrusion grade for food contact applications for sheet extrusion. This resin offers extreme low temperature (-40 °C) .. |
|||
| Tensile Strength at Break | 61.0 MPa | 8850 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP COLORCOMP D1000 PC (Europe-Africa-Middle East) LNP* COLORCOMP* D1000 is a compound based on Polycarbonate resin containing Unfilled Custom Color |
|||
| Tensile Strength at Break | 61.0 MPa | 8850 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics Lexan® EXL9330 PC Copolymer (Europe-Africa-Middle East) Opaque PC-Siloxane copolymer with excellent processability. Non-chlorinated, non-brominated flame retardant product in most colors. UV-stabilized. UL rated f1/V-0/5VA. |
|||
| Tensile Strength at Break | 61.0 MPa | 8850 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® FXE1413T PC Copolymer Clear PC-siloxane copolymer with excellent processability, for Visual fX capability in "Energy" colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color packa.. |
|||
| Tensile Strength at Break | 61.0 MPa | 8850 psi | ASTM D638 |
| LG Chemical LUCEL N115 POM, Unreinforced, High Viscosity LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m.. |
|||
| Tensile Strength at Break | 61.0 MPa | 8850 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP Lexan_WR6300 AES+PC+SAN (Asia Pacific) Wear resistant PC+SAN, with proprietary lubricant, for business equipment applications. |
|||
| Tensile Strength at Break | 61.0 MPa | 8850 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics REMEX VR4831 PBT 15% Glass filled PBT, Flame retardant, UL Recognized, Utility grade, Black color only |
|||
| Tensile Strength at Break | 61.0 MPa | 8850 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP QL002 PA 6/10 LNP* LUBRICOMP* QL002 is a compound based on Nylon 6/10 containing 10% PTFE. Added features of this grade are: Wear Resistant. |
|||
| Tensile Strength at Break | 61.0 MPa | 8850 psi | ASTM D638 |
| SABIC Innovative Plastics LNP LUBRILOY D20009 PC LNP LUBRILOY* D20009 is a compound based on Polycarbonate resin containing Proprietary Lubricant. Added features of this material include: Flame Retardant, Wear Resistant. |
|||
| Tensile Strength at Break | 61.0 MPa | 8850 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP LUBRILOY Lexan_WR6300 AES+PC+SAN LNP* Lubriloy* Lexan_WR6300 compound is a wear resistant PC+SAN, with proprietary lubricant, for business equipment applications. |
|||
| Tensile Strength at Break | 61.0 MPa | 8850 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP RI001 PA 66 LNP* LUBRICOMP* RI001 is a compound based on Nylon 66 resin containing 2% Silicone. Added feature of this grade is: Wear Resistant. |
|||
| Tensile Strength at Break | 61.0 MPa | 8850 psi | Type I, 50 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Xenoy® X5600WX PC+POLYESTER (Europe-Africa-Middle East) Unreinforced, opaque Polyester+PC alloy. Chemical resistance, dimensional stability and mechanical performance. UV Stabilized. Mold ReleaseThis data was supplied by SABIC-IP for the Europe-Africa-Mi.. |
|||
| Tensile Strength at Break | 61.0 MPa | 8850 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics NORYL GTX GTX679 PPE+PA6 (Europe-Africa-Middle East) Noryl GTX* GTX679 Resin is a blend of Polyphenylene Ether(PPE) + Polyamide(PA) resin that is mineral filled, conductive, and suitable for injection molding. The conductivity level is optimized to al.. |
|||
| Tensile Strength at Break | 61.0 MPa | 8850 psi | ISO 527-93 |
| Wellman Wellamid® 22LHI6 XE-NBK1 Impact Modified Nylon 66 Description: Impact Modified Nylon 66Information provided by Wellman. |
|||
| Tensile Strength at Break | 61.0 MPa | 8850 psi | ISO 527 - 1 & - 2 |
| Asahi Kasei Tenac®-C MT754 Copolymer Acetal Resin 20% Mineral filled, high stiffness, low warp gradeInformation provided by Asahi Kasei Corporation. |
|||