SABIC Innovative Plastics LNP COLORCOMP D1000 PC (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Colorcomp |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP COLORCOMP D1000 PC (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* COLORCOMP* D1000 is a compound based on Polycarbonate resin containing Unfilled Custom Color
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Water Absorption | 0.18 % @Time 86400 sec |
0.18 % @Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0090 cm/cm | 0.0060 - 0.0090 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 61.0 MPa | 8850 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 67.0 MPa | 9720 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 6.8 % | 6.8 % | 50 mm/min; ISO 527 |
| 7.1 % | 7.1 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
| Tensile Modulus | 2.45 GPa | 355 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 91.0 MPa | 13200 psi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 120 kJ/m² | 57.1 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 68.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
37.8 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 75.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
41.7 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C | 270 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PP CQX10030 R3 Polypropylene, Mineral Reinforced, Scratch Resistant
- SABIC Innovative Plastics Lexan® XHT2141 PC Copolymer
- Fibre Glast Saf-T-Poxy 2410 / 2184 Epoxy (discontinued **)
- MMCC Al/SiC 3DP Particulate Aluminum Matrix Composite
- Solvay Chemicals 2,2,2-Trifluoroethanol
- SMAC SMACWRAP® ST Damping Material, 1 mm
- Total HDPE HL 535 High Density Polyethylene, Film Resin
- BASF Elastollan R 2002 25% Glass Filled TPUR
- Axiall 34551 Wire & Cable Flexible PVC
- DuPont Performance Polymers Neoprene AD-20 Polychloroprene Rubber (discontinued **)
Copyright © lookpolymers.com All Rights Reserved