Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 37.0 MPa | 5370 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Cycolac® MG8000SR ABS (Europe-Africa-Middle East) This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | Type 1, 2"/min; ASTM D638 |
Proto3000 ABSi Fused Deposition Modeling Polymer Description: Stratasys ABSi is an ideal material for conceptual modeling, functional prototyping and direct digital manufacturing. Its strength is superior to standard Stratasys ABS, and the translu.. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Geloy XTWE280 ASA Weatherble ASA profile extrusion gradeThis data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Geloy XTWM206 ASA (Asia Pacific) Next generation ASA optimized for outstanding weatherability, colorability and higher heat applications requiring UV exposure resistance.This data was supplied by SABIC-IP for the Asia Pacific regio.. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | ISO 527 |
SABIC Innovative Plastics LNP FARADEX AS003 ABS (Europe-Africa-Middle East) LNP* Faradex* AS003 is a compound based on Acrylonitrile Butadiene Styrene resin containing Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | ISO 527 |
Total Finathene® 53140 HDPE, blow molding, sheet
(discontinued **) Finathene® 53140 is a high density polyethylene produced by the slurry loop low pressure polymerization process FINATHENE® 53140 has been especially developed for the manufacturing of blow molded .. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | 50mm/min; ASTM D638 |
3M Dyneon™ PVDF 6020/1001 Polyvinylidene Fluoride
(discontinued **) Ultra-high molecular weight grade PVDFPowder gradeExcellent chemical resistance to a wide variety of aggressive fluids and solventsGood permeation resistanceExcellent strength and dimensional stabil.. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | ISO R 527 |
Fainplast Compounds RK 435 Rigid PVC, Extrusion Lead Free Electrical channels |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | 50mm/min; ASTM D638 |
Kingfa FW-650 Flame Retardant ABS Features:Weather resistanceSuper high impact resistanceApplications:Injection moldingSwitchSocketInformation Provided by Kingfa Sci. & Tech. Co., Ltd. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | |
GrafTech eGRAF® SPREADERSHIELD™ SS1500 Graphite Made from flexible graphite, eGRAF® SPREADERSHIELD™ products function as both a passive heat spreader and heat shield. SPREADERSHIELD™ material can be die-cut, press-formed, or laminate.. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP KL005 Acetal Copolymer LNP LUBRICOMP* KL005 is a compound based on Acetal Copolymer resin containing 25% PTFE. Added feature of this material is: Wear Resistant. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP WP004 PBT LNP* LUBRICOMP* WP004 is a compound based on PBT resin containing 20% PTFE/Silicone. Added feature of this grade is: Wear Resistant. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | (Wire/Cable), break Initial |
SABIC Innovative Plastics ULTEM STM1500 PEI Copolymer Siloxane polyetherimide block copolymer. Wire and cable use. Strength and flexibility. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | ISO R 527 |
Stir SpA HE 625 A (PVC) Application: Economic medium shock resistantInformation provided by STIR SpA |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL WCV065 PPE+Polyolefin (Asia Pacific) Flexible, non-halogenated FR, PPE+Polyolefin resin designed for evaluation in Automotive ISO6722 Class A-C applications. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-LOY NX13401 PC+ABS LNP* STAT-LOY* NX13401 is a compound based on PC+ABS blend. Added features of this material include: Antistat, Flame Retardant, Excellent Release. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP DB0049F PC LNP* THERMOCOMP* DB0049F is a compound based on Polycarbonate resin containing 20% Glass Bead. Added features of this material include: Flame Retardant, Superior Molding. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP DB0049F PC (Asia Pacific) LNP* Thermocomp* DB0049F is a compound based on Polycarbonate resin containing Glass Bead, Flame Retardant. Added features of this material include: Flame Retardant, Superior Molding. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | 50mm/min; ASTM D638 |
Denka TE-10 Transparent Resin Polymer (MABS resin) ABS "TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a.. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | 50mm/min; ISO 527-2 |
Denka MALECCA K-600 ABS A heat-resistant ABS resin based on "DENKA IP" – a Styrene-N-Phenylmaleimide copolymer. It has been designed as an easy-to-use resin by improving conventional heat-resistant ABS resins which had de.. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | ASTM-D638 |
Braskem GM7040G HDPE High Density Extrusion Polyethylene GM7040G is a high-density polyethylene compound specially developed for the manufacturing of extruded pipes for a gas pressurized line. It is produced with bimodal technology and has high molar mass.. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | ASTM D638 |
Aclo Accutech Polypropylene Homopolymer HP0339G10CL Glass Reinforced Coupled |
|||
Tensile Strength at Break | 37.1 MPa | 5370 psi | ASTM D3759 |
3M 2515 Flat Back Paper Masking Tape 3M™ Flat Back Paper Masking Tape 2515 can be used for splicing, bundling, holding, fastening, tabbing and packaging applications.Information provided by 3M |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | ASTM D1457 |
Asahi Glass Fluon® CD145 PTFE Coagulated Dispersion Powder Fluon®PTFE coagulated dispersion powders (fine powders) are used for paste extrusion to make tapes, tubes, rods and wire coatings.Information provided by Asahi Glass Company, Inc. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOTUF MX00619 PP (Asia Pacific) LNP* Thermotuf* MX00619 is a compound based on Polypropylene resin containing Proprietary Filler(s). |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | 5 mm/min; ISO 527 |
Polimeri Europa Edistir N 1910 Polystyrene Very easy flow general purpose polystyrene. Used for injection of thin-wall, multi-cavity, very fast-cycle mouldings and for sheet extrusion in glossy capping of HIPS and in blend with HIPS or clear.. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® HFD4471 PC (Asia Pacific) Lexan* HFD4471 is a 10% glass filled, medium flow, impact modified, injection moldable grade designed for high flow and superior surface appearance. HFD4417 has enhanced mold release, impact ductili.. |