Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 31.0 MPa | 4500 psi | |
Plastcom SLOVALEN PH 72 T 40 PP, 40% mineral filling FeaturesModified homopolymer PP for injection moulding with the content of 40% microground, floated, thermo stable, chemically modified talc. General application in all industry branches - covers of.. |
|||
Tensile Strength at Break | 31.0 MPa | 4500 psi | 2 in/min; ASTM D638 |
RheTech Products M20P100-01 20% Mica Reinforced Polypropylene, Black Applications: Fan shroudsFiller panelsAir ductsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 31.0 MPa | 4500 psi | 2 in/min; ASTM D638 |
RheTech Products T20P100-00 20% Talc Reinforced Polypropylene, Natural Applications: Electronic housingsConsolesIP componentsHVAC ducts - air distributionClose out panelDurable goodsInjection molding conditions reported in table.Information provided by RheTech Products.. |
|||
Tensile Strength at Break | 31.0 MPa | 4500 psi | 2 in/min; ASTM D638 |
RheTech Products T20P100-01 20% Talc Reinforced Polypropylene, Black Applications: Electronic housingsIP componentsHVAC ducts - air distributionClose out panelDurable goodsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 31.0 MPa | 4500 psi | 2 in/min; ASTM D638 |
RheTech Products T20P104-01 20% Talc Reinforced Polypropylene, Black Applications: Electronic housingsIP componentsHVAC ducts - air distributionClose out panelDurable goodsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 31.0 MPa | 4500 psi | 50 mm/min; ISO 527 |
Polimeri Europa Edistir RT 461F Polystyrene High impact, heat resistant polystyrene with good stiffness. Recommended for improving the thermal performance of injection moulded technical parts which are submitted to high temperature in service.. |
|||
Tensile Strength at Break | 31.0 MPa | 4500 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Cycolac® MG29 ABS (Asia Pacific) Super high impact ABS. Good low temperature toughness. High gloss. |
|||
Tensile Strength at Break | <= 31.0 MPa | <= 4500 psi | ISO/R527 |
Polykemi AB POLYfill PPH T4030 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | 31.0 MPa | 4500 psi | 2 in/min; ASTM D638 |
Ineos K44-15-186 Polyethylene Copolymer K44-15-186 is a blue high-density polyethylene copolymer designed specifically for extrusion of pipe by blending K44-15-122 natural resin with G38-70C BLU II concentrate or an approved equivalent. .. |
|||
Tensile Strength at Break | 31.0 MPa | 4500 psi | 2 in/min; ASTM D638 |
Ineos TUB 172 HDPE TUB 172 is a yellow medium density polyethylene copolymer designed specifically for the extrusion of natural gas pipe. It exhibits excellent long term stress life and slow crack growth resistance. T.. |
|||
Tensile Strength at Break | 31.0 MPa | 4500 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Thermocomp FF004 PE LNP THERMOCOMP* FF004 is a compound based on Polyethylene resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 31.0 MPa | 4500 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-LOY K3000SZ Acetal Copoly LNP* STAT-LOY* K3000SZ is a compound based on Acetal Copolymer resin. Added feature of this material is: AntiSstatic. |
|||
Tensile Strength at Break | 31.0 MPa | 4500 psi | ISO 527 |
SABIC Innovative Plastics LNP STAT-LOY KX95702 Acetal LNP STAT-LOY* KX95702 is a compound based on Acetal resin containing Proprietary Filler(s). Added feature of this material is: Antistat. |
|||
Tensile Strength at Break | 31.0 MPa | 4500 psi | at max load; ASTM D638 |
A. Schulman PP 1632-01 Polypropylene Random Copolymer DescriptionPolypropylene PP 1632-01 is a polypropylene random copolymer produced utilizing unique catalyst and processing technology. It was designed for injection molding and stretch blow molding .. |
|||
Tensile Strength at Break | 31.0 MPa | 4500 psi | at max load; ASTM D638 |
A. Schulman PP 1632-01 Polypropylene Random Copolymer DescriptionPolypropylene PP 1632-01 is a polypropylene random copolymer produced utilizing unique catalyst and processing technology. It was designed for injection molding and stretch blow molding .. |
|||
Tensile Strength at Break | 31.0 MPa | 4500 psi | ASTM D638 |
Toyobo PELPRENE™ P90B Polyester TPE Features: Polyester TPEInformation provided by Toyobo. |
|||
Tensile Strength at Break | 31.0 MPa | 4500 psi | at max load; ASTM D638 |
A. Schulman PP 1632-01 Polypropylene Random Copolymer DescriptionPolypropylene PP 1632-01 is a polypropylene random copolymer produced utilizing unique catalyst and processing technology. It was designed for injection molding and stretch blow molding .. |
|||
Tensile Strength at Break | 31.0 MPa | 4500 psi | at max load; ASTM D638 |
A. Schulman PP 1632-01 Polypropylene Random Copolymer DescriptionPolypropylene PP 1632-01 is a polypropylene random copolymer produced utilizing unique catalyst and processing technology. It was designed for injection molding and stretch blow molding .. |
|||
Tensile Strength at Break | 31.0 MPa | 4500 psi | ASTM D638 |
Eastman Tenite 572A1V95316 Cellulose Acetate Butyrate, Smoke, Trsp Applications:Molded partsProduct Description: Tenite cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm fee.. |
|||
Tensile Strength at Break | 31.0 - 34.6 MPa | 4500 - 5020 psi | ASTM D638M |
DSM Somos® NeXT Stereolithography (SLA) Prototyping Polymer Somos® NeXT combines stiffness and impact resistance which brings it close the performance of injection molded thermoplastics. It produces finished parts with tight tolerances and detailed features.. |
|||
Tensile Strength at Break | 31.0 MPa | 4500 psi | 50 mm/min; ISO 527 |
Chi Mei Polylac® PA-747 ABS High impact |
|||
Tensile Strength at Break | 31.0 MPa | 4500 psi | ASTM D638 |
Aclo Accutech Polypropylene Homopolymer HP0336M40CL Mica Reinforced Coupled |
|||
Tensile Strength at Break | 31.0 MPa | 4500 psi | ASTM D1457 |
Asahi Glass Fluon® CD076 PTFE Coagulated Dispersion Powder Fluon®PTFE coagulated dispersion powders (fine powders) are used for paste extrusion to make tapes, tubes, rods and wire coatings.Information provided by Asahi Glass Company, Inc. |
|||
Tensile Strength at Break | 31.0 - 48.0 MPa | 4500 - 6960 psi | ASTM D638 |
Arkema Group KYNAR® 460 Polyvinylidene Fluoride Homopolymer - Extrusion Characteristics: Natural resin - translucent, off-white hemispheres. Broad molecular weight distribution. High stability in harsh thermal, chemical and ultraviolet environments. High toughness a.. |
|||
Tensile Strength at Break | 31.0 MPa | 4500 psi | |
Plastcom SLOVALEN PH 73 T 20 PP, 20% mineral filling FeaturesModified homopolymer PP for injection moulding with the content of 20% mineral filling. Increased rigidity, strength and thermal use up to 130°C depending on the talc conte nt. Decreased sh.. |
|||
Tensile Strength at Break | 31.0 MPa | 4500 psi | 50 mm/min, 1A; ISO 527 |
SABIC Innovative Plastics SABIC PPCOMPOUND 15T1040 PP SABIC® PPcompound 15T1040 is a general purpose, talc filled, heat stabilized homopolymer polypropylene compound, suitable for injection molding applications. The IMDS ID is 16487994 |
|||
Tensile Strength at Break | 31.0 MPa | 4500 psi | ASTM D638 |
A. Schulman POLYFLAM™ E-15937B High Strength Impact Modified Polypropylene DescriptionPolyfort® E-15937B is a high strength impact modified polypropylene.Information provided by A. Schulman. |
|||
Tensile Strength at Break | 31.0 MPa | 4500 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON QD000I PA 6/10 (Asia Pacific) LNP STAT-KON* QD000I is a compound based on Nylon 6/10 resin containing Carbon Powder. Added features of this material include: Electrically Conductive. |