Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 18.0 MPa | 2610 psi | |
Plastcom SLOVALEN PC 63 T 15-1M PP, 15% mineral filling FeaturesModified PP copolymer for injection moulding with the content of 15 % mineral filler, uv stabilized, good scratch resistance, low odor and very good flowability with good dimensional stabili.. |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | ASTM D638 |
SABIC B4660/B4660AB High Density Polyethylene for Blow Molding Product Description: B4660 series grades are medium molecular weight High Density Polyethylene homopolymer for blow molding applications. They are primarily designed for imparting high rigidity, t.. |
|||
Tensile Strength at Break | <= 18.0 MPa | <= 2610 psi | ISO/R527 |
Polykemi AB POLYelast TPE HJ-75 UV1 Thermoplastic Elastomer, PP/Elastomer/Mineral, UV-Stabilized, Low CLTE Information provided by Polykemi AB |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | ISO 527 |
Polyplastic Armlen® PP MF 30-3IM Polypropylene, 30% Mineral Filled UV resistant, impact modified, heat stabilizedInformation provided by PolyPlastic Group. |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | ASTM D638 |
SABIC BM6246LS High Density Polyethylene for Blow Molding Product Description: BM6246LS grade is a medium molecular weight High Density Polyethylene homopolymer for blow molding applications. It is primarily designed for imparting high rigidity, toughnes.. |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | ASTM D 638 |
LyondellBasell Hostacomâ„¢ 63A6-4 Polypropylene Homopolymer Description: Hostacomâ„¢ 63A6-4 medium high melt flow, 2,200 MPa flexural modulus, 40% calcium carbonate-filled polypropylene homopolymer has an excellent combination of properties, chemical resi.. |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL WCA871A PPE (Europe-Africa-Middle East) Flame retardant performance and mechanical properties capable of meeting UL VW-1 requirement and 105C temperature rating as defined UL1581. UL1581 tests conducted on 1.0mmD wire with AWG28 conductor.. |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL WCD841U PPE-TPE (Europe-Africa-Middle East) Flexible, UV stabilized, halogen free extrusion grade for applications such as wire insulation and cable jacket. Good color stability after UV weathering per ASTM D4459. Light color capable. Flame r.. |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Thermocomp MH0200A PP (Europe-Africa-Middle East) LNP* Thermocomp* MH0200A is a compound based on Polypropylene resin containing High Specific Gravity Filler.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | ASTM D638 |
UBE B128 Polyethylene Description: UBE Polyethylene is polymerized at high pressure using a tubular reactor. Production conditions are strictly controlled ensuring the product's superior physical and mechanical prope.. |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | At 50 mm/min; ISO/DIS 6259 |
Borealis BorPEX™ HE2515 High Density Polyethylene Compound for Silane Crosslinked Pipes BorPEX HE2515 is a silane crosslinkable compound which is used together with a catalyst masterbatch (Cat-MB) to accelerate the moisture-induced crosslinking reaction. It is designed for flexible cr.. |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | ISO 527-2 |
Total PS CPDS 820 Flame Retardant Polystyrene POLYSTYRENE (PS) COMPOUND (CPDS) 820 is a high impact brominated flame retardant polystyrene. A combination of high flow and high heat stability gives excellent processability and reduced cycle tim.. |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | ISO 527-2/50 |
ExxonMobil Exxtral™ CMU 101D Performance Polyolefin Product Description: A specialty thermoplastic polyolefin resin designed for automotive interior trim in which good surface finish, high scratch resistance, minimum dust deposit and good UV resistan.. |
|||
Tensile Strength at Break | >= 18.0 MPa | >= 2610 psi | 50 mm/min; ISO 527 |
Fainplast Compounds Ethylplus 613 HPE Polyethylene Cable Compound Polyethelene, halogen-free cable compound with superior thermo-mechanical properties, outstanding heat resistance, and high electrical propertiesExpandable HDPE by gas injectionInformation provided .. |
|||
Tensile Strength at Break | >= 18.0 MPa | >= 2610 psi | ISO R 527 |
Fainplast Compounds FK 001/AL Flexible PVC, Insulation Lead Free General purposes suitable for food contact according to CEE 90/128 |
|||
Tensile Strength at Break | >= 18.0 MPa | >= 2610 psi | ISO R 527 |
Fainplast Compounds FR 85 Flexible PVC, Insulation Low temperatures |
|||
Tensile Strength at Break | >= 18.0 MPa | >= 2610 psi | ISO R 527 |
Fainplast Compounds GA 0179 Flexible PVC, Flame Retardant Sheathing Hydrocarbon resistant sheathing |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | 50 mm/min; ISO 527 |
Eurostar Starpylen MX05039 PP, Mineral Filled, Injection Molding Starpylen MX05039 is a Mineral Filled Polypropylene Injection Molding ResinInformation provided by Eurostar. |
|||
Tensile Strength at Break | >= 18.0 MPa | >= 2610 psi | ISO R 527 |
Fainplast Compounds FRT 82 Flexible PVC, Insulation Telephone cables |
|||
Tensile Strength at Break | >= 18.0 MPa | >= 2610 psi | ISO R 527 |
Fainplast Compounds KL 92/3 Flexible PVC, Insulation for High Temperatures Lead Free Operatine temperature 105°C |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | ISO R 527 |
Fainplast Compounds MPH 83/T Medical Flexible PVC, Extrusion Technical tubes no DOP |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | ISO R 527 |
Fainplast Compounds MPH 87 Medical Flexible PVC, Extrusion Tubolar apparatus |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | ASTM D882 |
Arkema Group OREVAC® 18319 Grafted Maleic Anhydride Polyethylene OREVAC 18319 is a maleic anhydride grafted polyethylene used in the manufacturing of multi-layer aluminium panels. OREVAC 18319 is mainly used in aluminium panels to have good adhesion performances .. |
|||
Tensile Strength at Break | >= 18.0 MPa | >= 2610 psi | ASTM D4894 |
Adamas Adalon® 203 PTFE, 15/5% Glass/Graphite Filled Information provided by Adamas, HPM |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | ASTM D638 |
Arkema Group OREVAC® 9309 EVA Terpolymer OREVAC® is a range of ethylene-vinyl acetate copolymers modified by adjunction of polar groups which, when molten, have excellent adhesive properties to various substrates. They are supplied as fre.. |
|||
Tensile Strength at Break | >= 18.0 MPa | >= 2610 psi | ISO R 527 |
Fainplast Compounds AP 93 Flexible PVC, Flame Retardant Insulation General purposes |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics SABIC PPCOMPOUND 15T1020 PP SABIC® PPcompound 15T1020. This grade is a general purpose, talc filled, heat stabilized polypropylene resin suitable for injection molded applications. The IMDS ID is 16486973. |
|||
Tensile Strength at Break | >= 18.0 MPa | >= 2610 psi | ISO R 527 |
Fainplast Compounds FKA 88/1 Flexible PVC, Flame Retardant Insulation Lead Free Insulation low temperatures |