Polymer Property : Tensile Strength at Break = 18000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	124 MPa	18000 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP IFL36L PA6.12 LNP* LUBRICOMP* IFL36L is a compound based on Nylon 6/12 containing 30% Glass Fiber, 15% PTFE. Added features of this grade include: Low Extractable, Wear Resistant.
Tensile Strength at Break	124 MPa	18000 psi	ISO 527
SABIC Innovative Plastics LNP LUBRICOMP OFL36 PPS - Branched (Asia Pacific) LNP LUBRICOMP* OFL36 is a compound based on PPS - Branched resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Tensile Strength at Break	124 MPa	18000 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP OFL36 PPS - Linear LNP* LUBRICOMP* OFL36 is a compound based on PPS - Linear resin containing 30% Glass Fiber, 15% PTFE. Added features of this grade include: Wear Resistant.
Tensile Strength at Break	124 MPa	18000 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM CRS5711 PEI 15% Glass fiber filled, enhanced flow Polyetherimide copolymer (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics, and ketones. ECO conforming, UL94 V0 and 5VA listing.
Tensile Strength at Break	124 MPa	18000 psi	ISO 527-2
Solvay Specialty Polymers KetaSpireÂ® KT-820 GF15 Polyetheretherketone (PEEK), 15% Glass Fiber KetaSpireÂ® KT-820 GF15 is a low flow, 15% glass-fiber reinforced grade of polyetheretherketone (PEEK). This resin offers higher strength and stiffness properties relative to unreinforced KetaSpir..
Tensile Strength at Break	124 MPa	18000 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON RFD04 PA 66 LNP STAT-KON* RFD04 is a compound based on Nylon 66 resin containing 20% Glass Fiber. Added features of this material include: Electrically Conductive.
Tensile Strength at Break	124 MPa	18000 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP PF005S PA 6 LNP* THERMOCOMP* PF005S is a compound based on Nylon 6 resin containing 25% Glass Fiber. Added features of this material include: Heat Stabilized.
Tensile Strength at Break	124 MPa	18000 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP RF0059 PA 66 LNP THERMOCOMP* RF0059 is a compound based on Nylon 66 resin containing 25% Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant.
Tensile Strength at Break	124 MPa	18000 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP NF0061 PC+ABS (Europe-Africa-Middle East) LNP* THERMOCOMP* NF0061 is a compound based on PC+ABS resin containing Glass Fiber, Flame Retardant. Added features include : Flame Retardant.
Tensile Strength at Break	124 MPa	18000 psi	ASTM D638
Chase Plastics CP Pryme® NN113L (Dry) Nylon 66, 13% Glass Fiber Reinforced, Lubricated Features: Good chemical resistanceGrease resistantLubricatedOil resistantHigh rigiditySolvent resistantHigh tensile strengthForm: PelletsInformation provided by Chase Plastics.
Tensile Strength at Break	124 MPa	18000 psi	ASTM D 638
SABIC Innovative Plastics LNP Verton OV00A PPS LNP* Verton* OV00A is a compound based on Polyphenylene Sulfide resin containing Long Glass Fiber.This data was supplied by SABIC-IP for the Americas region.