SABIC Innovative Plastics LNP THERMOCOMP NF0061 PC+ABS (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Glass Fiber Filled , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP NF0061 PC+ABS (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* NF0061 is a compound based on PC+ABS resin containing Glass Fiber, Flame Retardant. Added features include : Flame Retardant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 |
| Water Absorption | 0.12 % @Time 86400 sec |
0.12 % @Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0015 cm/cm | 0.0015 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 124 MPa | 18000 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.9 % | 1.9 % | 5 mm/min; ISO 527 |
| 2.5 % | 2.5 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
| Tensile Modulus | 7.80 GPa | 1130 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 159 MPa | 23100 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 161 MPa | 23400 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 7.20 GPa | 1040 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 32.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
17.8 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 67.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
37.2 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 114 °C | 237 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- Polykemi AB POLYabs N30 ABS
- Radici Heraflex® E 7722 TPC-ET Thermoplastic Elastomer
- Materion BrushCAST® 20C High Strength Casting Alloy (Solution Annealed & Aged)
- H.C. Starck Amperit® 582.072 Chromium Carbide-Nickel Chromium 80-20 (Cr3C2-NiCr)
- SABIC Innovative Plastics NORYL SE100HX PPE+PS
- SABIC Innovative Plastics ULTEM 1100F PEI (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP STAT-LOY M3000 PP (Europe-Africa-Middle East)
- E-Polymers EFLEX® S5090 Extrusion
- Fainplast Compounds KLT 93 Flexible PVC, Insulation Transparent Cables Lead Free
- Saint-Gobain Korel® K30-20 Soft Micro-cellular Polyurethane Foam
Copyright © lookpolymers.com All Rights Reserved