Polymer Property : Tensile Strength at Break = 15200 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	105 MPa	15200 psi	50 mm/min; ASTM D638
Mytex Polymers AN16L(W)-D56 Polypropylene, Talc filled, Compounded, Elastomer, Impact modified Description: AN16L-D56 is a compounded talc filled elastomer modified polypropylene with good impact and excellent material flow properties.Key Applications: Automotive exteriorInformation provided ..
Tensile Strength at Break	<= 105 MPa	<= 15200 psi	ISO/R527
Polykemi AB SCANMID 6 B12^ F20 NH6 Nylon 6, Glass Fiber Reinforced, Halogen Free, Flame Retardant Information provided by Polykemi AB
Tensile Strength at Break	105 MPa @Thickness 4.00 mm, Temperature 23.0 °C	15200 psi @Thickness 0.157 in, Temperature 73.4 °F	Injection Molded; ISO 527-2
PolyOne Bergadur™ PB40 G15 blue Polybutylene Terephthalate (PBT) Information provided by PolyOne
Tensile Strength at Break	105 MPa	15200 psi
Idemitsu Kosan XarecÂ® EA 513 SPS, 30% Glass Filled
Tensile Strength at Break	105 MPa	15200 psi	5 mm/min; ISO 527
SABIC Innovative Plastics NORYL SE1GFN3 PPE+HIPS (Europe-Africa-Middle East) Noryl* SE1GFN3 is a 30% glass reinforced, injection moldable modified polyphenylene ether resin. Designed for improved dimensional stability and good flow , this resin also uses non-chlorinated, non..
Tensile Strength at Break	105 MPa	15200 psi	Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Ultem 1010A PEI (Europe-Africa-Middle East) Transparent, high flow Polyetherimide (Tg 217C). ECO Conforming.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Tensile Strength at Break	105 MPa	15200 psi	Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Ultem 2412EPR PEI (Europe-Africa-Middle East) 40% Milled glass filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing.This data was supplied by SABIC-IP for the Eu..
Tensile Strength at Break	105 MPa	15200 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM 9011 PEI (Asia Pacific) Transparent, high flow Polyetherimide (Tg 217C). ECO Conforming. Improved processability for Fiber extrusion.
Tensile Strength at Break	105 MPa	15200 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM HU1010 PEI (Asia Pacific) Transparent, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI),..
Tensile Strength at Break	105 MPa	15200 psi	ASTM D638
SABIC Innovative Plastics LNP STAT-KON DX05474 PC (Asia Pacific) LNP* Stat-kon* DX05474 is a compound based on Polycarbonate resin containing Flame Retardant, Carbon Fiber. Added features of this material include: Electrically Conductive, Easy Molding, Flame Ret..
Tensile Strength at Break	105 MPa	15200 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ValoxÂ® IQ507 PBT+PC (Asia Pacific) Valox iQ507 resin: Environmentally responsible, sustainable, and low carbon footprint resin that is 30% glass fiber reinforced PBT+PC alloy. Valox iQ507 offers good mechanical and thermal characte..
Tensile Strength at Break	105 MPa	15200 psi	ISO 527
SABIC Innovative Plastics LNP Stat-kon ZE0039 MODIFIED POYPHENYLENE (Asia Pacific) LNP* Stat-kon* ZE0039 is a compound based on MODIFIED POYPHENYLENE resin containing Carbon Fiber.This data was supplied by SABIC-IP for the Asia Pacific region.
Tensile Strength at Break	105 MPa	15200 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP KFZ24XXP Acetal Copoly LNP* THERMOCOMP* KFZ24XXP is a compound based on Acetal Copolymer resin containing 20% Glass Fiber, 10% Milled Glass. Added features of this material include: Low Warpage, Chemically Coupled, Inter..
Tensile Strength at Break	105 MPa	15200 psi	5 mm/min; ISO 527
SABIC Innovative Plastics NORYL NH7114 PPE+HIPS (Europe-Africa-Middle East) Noryl* NH7114 resin is a 20% glass reinforced, modified PPE-PS blend. The material uses non-halogenated flame retardants to achieve UL94 flame ratings while offering an exceptional balance of streng..
Tensile Strength at Break	105 MPa	15200 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP STAT-KON DEP32 PC LNP* STAT-KON* DEP32 is a compound based on Polycarbonate containing 10% Carbon Fiber, 15% PTFE/Silicone. Added features of this material include: Electrically Conductive, Wear Resistant.
Tensile Strength at Break	105 MPa	15200 psi	5 mm/min; ISO 527
SABIC Innovative Plastics ValoxÂ® IQNH4550 PBT (Europe-Africa-Middle East) Valox* iQNH4550 resin is a non-brominated/non-chlorinated flame retardant product based on an environmentally sustainable Valox iQ* PBT resin. Post-consumer recycle (PCR) usage is 31% based on EPEAT..
Tensile Strength at Break	105 MPa	15200 psi	5 mm/min; ISO 527
SABIC Innovative Plastics Noryl GFN1420V PPE+PS (Europe-Africa-Middle East) Noryl* GFN1420V resin is a high flow blend of polyphenylene ether (PPE) and polystyrene (PS) resin that contains 20 % glass reinforcement. The resin is suitable for injection molding and is designe..
Tensile Strength at Break	105 MPa	15200 psi	ISO 527-93
Wellman Wellamid® GFT1628-BK 17% Glass Fiber Reinforced, Impact Modified Nylon 66 Description: Glass Fiber Reinforced, Impact Modified Nylon 66Information provided by Wellman.
Tensile Strength at Break	105 MPa	15200 psi	dry; ISO 527-1/-2
EMS-Grivory Grivory® BG-15 HM PA6-GF15 Product description: Grilon BG-15 HM is a heat stabilized, normal viscosity, and adhesion modified PA6 injection molding grade with 15% glass fibers. Grilon BG-15 HM has the following important prop..
Tensile Strength at Break	105 MPa	15200 psi	dry; ISO 527-1/-2
EMS-Grivory Grivory® BGM-30 X PA6-(GF+MD)30 Product description: Grilon BGM-30 X is a heat stabilized PA 6 injection molding grade with a 30 % reinforcement combination (mineral and glass fiber). Grilon BGM-30 X has the following important pr..
Tensile Strength at Break	105 MPa	15200 psi	5 mm/min; ISO 527
CP-Polymer-Technik Wellamid® 6600 GV 20 HWCP 20% Glass Fiber Nylon 66, Heat Stabilized, Conditioned Information provided by CP-Polymer-Technik GmbH & Co. KG
Tensile Strength at Break	105 MPa	15200 psi	conditioned; ISO 527-1/-2
EMS-Grivory Grivory® HTM-4H1 PA6T/6I-MD40 Product description: Grivory HTM-4H1 is a 40 % mineral reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Polymer designation acc. to ISO: PA ..
Tensile Strength at Break	105 MPa	15200 psi	conditioned; ISO 527-1/-2
EMS-Grivory Grivory® LV-30H FWA black 9225 PA12-GF30 Product description: Grilamid LV-30H FWA black 9225 is a 30 % glass fiber reinforced, heat stabilized polyamide12 injection molding grade with the following special features: Stiffness combined with..
Tensile Strength at Break	105 MPa @Temperature 140 - 150 °C, Time 1.80e+7 sec	15200 psi @Temperature 284 - 302 °F, Time 5000 hour	5 [mm/min], 50% Loss of Tensile Strength; ICE 216
Akro-Plastic Akroloy® PA GF 30 (2718) PA 6.6 & PA6I/6T Dry, 30% Glass Filled One of the most characteristic properties of polyamide (PA 6.6) is the absorption of moisture. This essentially leads to increased toughness and elongation at break, to name the most important param..
Tensile Strength at Break	105 MPa @Temperature 150 - 160 °C, Time 1.80e+7 sec	15200 psi @Temperature 302 - 320 °F, Time 5000 hour	5 [mm/min], 50% Loss of Tensile Strength; ICE 216
Akro-Plastic Akromid® T1 GF 30 9 (3498) PPA Dry, 30% Glass Filled The new AKROMID® T is characterized primarily by high heat resistance and the lowest moisture absorption of the three PA grades, making it particularly well-suited in the automotive sector for high..
Tensile Strength at Break	105 MPa	15200 psi	DIN 53 455
Albis Plastics Tedur® L 9523 PPS, 60% Glass Fiber/Mineral Extremely Rigid, Excellent Surface Finish, Metallization w/o Base Coating. Incandescent wire resistance (2 mm) is 960°C per VDE 0471 T1.2.Applications: Insulating Equipment, Reflectors and Fitting..
Tensile Strength at Break	105 MPa	15200 psi	ISO 527-1/-2
DSM Akulon® K224-HPG3 Impact Modified Nylon 6-15% Glass Reinforced (European Grade) (Dry) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier ..
Tensile Strength at Break	105 MPa	15200 psi	5 mm/min; ISO 527
SABIC Innovative Plastics Noryl GFN1420V PPE+PS Noryl* GFN1420V resin is a high flow blend of polyphenylene ether (PPE) and polystyrene (PS) resin that contains 20 % glass reinforcement. The resin is suitable for injection molding and is designe..
Tensile Strength at Break	105 MPa	15200 psi
Radici Radiflam® A RV300AE (cond.) Nylon 66-30GF PA66 flame retardant injection molding grade. 30% Glass fiber reinforced, for items with high stiffness. Natural colorInformation provided by Radici group.