SABIC Innovative Plastics LNP STAT-KON DEP32 PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DEP32 PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* DEP32 is a compound based on Polycarbonate containing 10% Carbon Fiber, 15% PTFE/Silicone. Added features of this material include: Electrically Conductive, Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.28 g/cc | 1.28 g/cc | ASTM D792 |
| Density | 1.28 g/cc | 0.0462 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.120 % | 0.120 % | 50% RH, 24 hrs; ASTM D570 |
| 0.180 % | 0.180 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 105 MPa | 15200 psi | 5 mm/min; ISO 527 |
| 108 MPa | 15700 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.6 % | 2.6 % | 5 mm/min; ISO 527 |
| 2.8 % | 2.8 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 7.77 GPa | 1130 ksi | 1 mm/min; ISO 527 |
| 7.79 GPa | 1130 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 161 MPa | 23400 psi | ISO 178 |
| 163 MPa | 23600 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 166 MPa | 24100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 6.95 GPa | 1010 ksi | 2 mm/min; ISO 178 |
| 6.97 GPa | 1010 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.14 J/cm | 2.14 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.68 J/cm | 8.77 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 32.0 kJ/m² | 15.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 24.0 J @Temperature 23.0 °C |
17.7 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 7.00 J | 5.16 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 17.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
9.44 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 60.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
33.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C | 297 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 148 °C @Thickness 3.20 mm |
298 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 144 °C | 291 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 145 °C @Thickness 3.20 mm |
293 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 ohm | 100 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Heatbath/Park Wire Annealing Quenching and Tempering Salt
- SABIC Innovative Plastics LNP STAT-KON IS000XXL PA6.12
- Styron INSPIREâ„¢ DTF8000 ES Compounded Polypropylene
- Techmer ES HiFill FR® HIPS FR
- Plenco 6582 Phenolic, Briquette, Transfer Molded
- DSM Akulon® F136 PA6
- EMS-Griltech Griltex® D 1309E Copolyester Hotmelt Adhesive (Apparel Interlinings)
- ExxonMobil Tetramer K Olefin
Copyright © lookpolymers.com All Rights Reserved