Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 10.0 MPa | 1450 psi | ISO 527 |
Polimeri Europa Flexirene® MT 40 A Linear Low Density Polyethylene Flexirene MT 40 A is a linear low density polyethylene (LLDPE), with antioxidants, suitable for injection molding application.Flexirene MT 40 A is characterized by a good processability and impact r.. |
|||
Tensile Strength at Break | 10.0 MPa | 1450 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible MG23B Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 10.0 MPa | 1450 psi | ASTM D638 |
Braskem BI 818 LDPE Injection Molding Polyethylene
(discontinued **) Applications: Injection molding; masterbatches. Information provided by Braskem |
|||
Tensile Strength at Break | 10.0 MPa | 1450 psi | ASTM D 638 |
LyondellBasell Hifaxâ„¢ CA260GC Thermoplastic Polyolefin Elastomer Description: Hifaxâ„¢ CA260GC White fractional melt flow, 40 MPa flexural modulus, UV-stabilized, precolored thermoplastic elastomeric olefin (TEO) resin has an excellent balance of flexibility,.. |
|||
Tensile Strength at Break | 10.0 MPa | 1450 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL WCD835 PPE-TPE Flexible, low odor, halogen free extrusion grade intended for evaluation in applications such as wire insulation and cable jacket. Flame performance capable of meeting UL VW1 requirements. 80C end.. |
|||
Tensile Strength at Break | 10.0 MPa | 1450 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL WCP821 PPE-TPE (Asia Pacific) Flexible Noryl* injection molding grade. Low specific gravity with very good non-halogenated flame retardant performance. Developed for evaluation in over-molding applications such as plugs, strain .. |
|||
Tensile Strength at Break | 10.0 MPa | 1450 psi | |
Shin-Etsu Silicones SV-57000U High Strength Silicone Elastomer SV57000U is one of a series of silicone bases designed for applications requiring high strength.. Product Features: Excellent mechanical properties.Typical Applications: Molding and Extrusion applic.. |
|||
Tensile Strength at Break | 10.0 MPa | 1450 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL WCD835 PPE-TPE (Europe-Africa-Middle East) Flexible, low odor, halogen free extrusion grade intended for evaluation in applications such as wire insulation and cable jacket. Flame performance capable of meeting UL VW1 requirements. 80C end.. |
|||
Tensile Strength at Break | 10.0 MPa | 1450 psi | at max load; ASTM D638 |
A. Schulman CP775-01 Molding Grade, Low Density Polyethylene DescriptionCp 755-01 is a molding grade, low-density polyethylene. ApplicationCP 755-01 meets the specification contained in FDA Regulation 177.1520 for food contact applications.Information provid.. |
|||
Tensile Strength at Break | 10.0 MPa | 1450 psi | 500 mm/min; ASTM D638 - ISO 527-2 |
DuPont Elvaloy® 3717 AC Ethylene and 17% Butyl Acrylate Copolymer Elvaloy® 3717 AC can be used for coextrusion, compounding and injection molding. In coextrusion, it can be used to improve sealing; in compounding, to improve low temperature and impact properties.. |
|||
Tensile Strength at Break | 10.0 MPa | 1450 psi | 500mm/min; ASTM D638 Type IV Specimen |
Westlake EMAC® Plus SP1358 21.5% Ethylene-Methyl Acrylate Copolymer Westlake EMAC® Plus SP1358 is a 21.5% EMA copolymer containing slip and antiblock. This resin is designed for blown or cast film, tie-layers, and extrusions where flexibility, compatibility, or low.. |
|||
Tensile Strength at Break | 10.0 MPa | 1450 psi | ASTM D638 |
ELASTO UK Dryflex® 502750S SEBS Based Material, Unfilled Qualities, 75A Hardness, Black The 500-seriesis very favorable when transparency and good scratch resistance are required, as well as when there are high surface finish requirements. Unfilled grades have excellent flow and mecha.. |
|||
Tensile Strength at Break | >= 10.0 MPa | >= 1450 psi | ISO R 527 |
Fainplast Compounds CKL 80/E Flexible PVC, Sheathing Lead Free Under sheathing |
|||
Tensile Strength at Break | >= 10.0 MPa | >= 1450 psi | ISO R 527 |
Fainplast Compounds CL 63/K Flexible PVC, Sheathing General purpose, opaque surface |
|||
Tensile Strength at Break | 10.0 MPa | 1450 psi | ISO R 527 |
Fainplast Compounds GS 69/F Flexible PVC, Injection Molding for Footwear Sandals |
|||
Tensile Strength at Break | 10.0 MPa | 1450 psi | ISO R 527 |
Fainplast Compounds PG 55/A Flexible PVC, Extrusion Modified with Rubber Gaskets modified with rubber |
|||
Tensile Strength at Break | 10.0 MPa | 1450 psi | ISO R 527 |
Fainplast Compounds PH 60 Flexible PVC, Transparent Extrusion Transparent profiles |
|||
Tensile Strength at Break | 10.0 MPa | 1450 psi | ISO R 527 |
Fainplast Compounds PM 5540 Flexible PVC, Extrusion Gaskets for frames |
|||
Tensile Strength at Break | 10.0 MPa | 1450 psi | ASTM D638 |
Azdel SuperLite® SL550700-100 PP Resin Matrix / 55% Glass Fiber (3.5 mm Molded Thickness) AZDEL SuperLite® SL550700-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
Tensile Strength at Break | 10.0 MPa @Temperature 175 °C, Time 605000 sec |
1450 psi @Temperature 347 °F, Time 168 hour |
Accelerated Aging; MIL-I-23053/15A |
3M BBI-A Shrinkable Tubing for Bus Bar 3M Heat Shrinkable Tubing for Bus Bar BBI-A Series is designed for insulating rectangular, square and round bus bar rated from 5 kV through 35 kV. It will also cover and insulate inline bolted conne.. |
|||
Tensile Strength at Break | 10.0 MPa | 1450 psi | ASTM D638 |
Arkema Group EVATANE® 28-40 Copolymer Ethylene - Vinyl Acetate EVATANE® 28-40 is a random copolymer of Ethylene and Vinyl Acetate made by high-pressure radicalar polymerisation process. EVATANE® 28-40 is stabilized with antioxidants. The High Vinyl Acetate co.. |
|||
Tensile Strength at Break | 10.0 MPa | 1450 psi | ISO R 527 |
Fainplast Compounds PK 5510 Flexible PVC, Lead Free Profiles |
|||
Tensile Strength at Break | >= 10.0 MPa | >= 1450 psi | |
Beijing Evergrow Resources PTFE, 20% Glass Fiber, 5% Graphite Filled Filled PTFE article is manufactured by molding method with filled PTFE resin. Filled PTFE resin is manufactured by compounding PTFE granular resin with fillers of many different kinds. Broadly speak.. |