SABIC Innovative Plastics NORYL WCD835 PPE-TPE (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL WCD835 PPE-TPE (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flexible, low odor, halogen free extrusion grade intended for evaluation in applications such as wire insulation and cable jacket. Flame performance capable of meeting UL VW1 requirements. 80C end use temperature rating and good heat deformation performance as defined by UL 1581. 83 Shore A hardness. Processing typically conducted on standard extrusion equipment. UL 1581 tests conducted on 2.0 mm wire with 0.12 mm x 20 stranded copper conductor.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Melt Flow | 6.0 g/10 min @Load 10.0 kg, Temperature 250 °C |
6.0 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 83 | 83 | 30S reading; ASTM D2240 |
| Tensile Strength at Break | 10.0 MPa | 1450 psi | Type I, 50 mm/min; ASTM D638 |
| 10.0 MPa | 1450 psi | 50 mm/min; ISO 527 | |
| 17.0 MPa | 2470 psi | UL 1581 | |
| 18.0 MPa | 2610 psi | after 7days @113°C; UL 1581 | |
| Elongation at Break | 225 % | 225 % | 50 mm/min; ISO 527 |
| 250 % | 250 % | Type I, 5 mm/min; ASTM D638 | |
| 250 % | 250 % | after 7days @113°C; UL 1581 | |
| 270 % | 270 % | UL 1581 | |
| Flexural Modulus | 0.0300 GPa | 4.35 ksi | 12.5 mm/min; ISO 178 |
| 0.0400 GPa | 5.80 ksi | 12.5 mm/min, 100 mm span; ASTM D790 | |
| Heat Distortion | 20 % @Load 0.250 kg, Temperature 100 °C |
20 % @Load 0.551 lb, Temperature 212 °F |
UL 1581 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | UL temperature rating; UL 1581 |
| Brittleness Temperature | <= -40.0 °C | <= -40.0 °F | ASTM D746 |
| Glow Wire Test | 750 °C | 1380 °F | IEC 60695-2-13 |
| 850 °C @Thickness 3.00 mm |
1560 °F @Thickness 0.118 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 9.00e+15 ohm-cm | 9.00e+15 ohm-cm | IEC 60093 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| VW-1 | Pass | UL 1581 |
Users viewing this material also viewed the following:
- Nye Lubricants 748 (RL) Synthetic Oil
- Hyosung Topilene HJ145 PP
- Solvay Chemicals NOCOLOK® Flux P2 Potassium Fluoroaluminate
- TIMET TIMETAL® 6-2-4-6 Titanium Alloy (Ti-6Al-2Sn-4Zr-6Mo), 10% Equiaxed Alpha + STA
- Covestro Bayblend® FR3210 TV PC/ABS Blend
- ExxonMobil LD 201.48 Extrusion Coating for Milk Carton Resin
- Arlon LW5015Rxx-P0 0.050" (1.27 mm) Self-Fusing Silicone Tape (Triangular, Unsupported) with Poly Interleave
- 3M Scotch-Weld™ RT300B Rubber-Toughened Instant Adhesive
- Resistalloy International Resistalloy 6015 Nickel Chromium Electrical Resistance Alloy
- Mitsui Arlen™ C215 15% Glass Fiber-Reinforced Modified Nylon 6T (DAM)
Copyright © lookpolymers.com All Rights Reserved