SABIC Innovative Plastics NORYL WCD835 PPE-TPE
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL WCD835 PPE-TPE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flexible, low odor, halogen free extrusion grade intended for evaluation in applications such as wire insulation and cable jacket. Flame performance capable of meeting UL VW1 requirements. 80C end use temperature rating and good heat deformation performance as defined by UL 1581. 83 Shore A hardness. Processing typically conducted on standard extrusion equipment. UL 1581 tests conducted on 2.0 mm wire with 0.12 mm x 20 stranded copper conductor.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Melt Flow | 6.0 g/10 min @Load 10.0 kg, Temperature 250 °C |
6.0 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 83 | 83 | 30S reading; ASTM D2240 |
| Tensile Strength at Break | 10.0 MPa | 1450 psi | Type I, 50 mm/min; ASTM D638 |
| 10.0 MPa | 1450 psi | 50 mm/min; ISO 527 | |
| 17.0 MPa | 2470 psi | UL 1581 | |
| 18.0 MPa | 2610 psi | after 7days @113°C; UL 1581 | |
| Elongation at Break | 225 % | 225 % | 50 mm/min; ISO 527 |
| 250 % | 250 % | Type I, 5 mm/min; ASTM D638 | |
| 250 % | 250 % | after 7days @113°C; UL 1581 | |
| 270 % | 270 % | UL 1581 | |
| Flexural Modulus | 0.0300 GPa | 4.35 ksi | 12.5 mm/min; ISO 178 |
| 0.0400 GPa | 5.80 ksi | 12.5 mm/min, 100 mm span; ASTM D790 | |
| Heat Distortion | 20 % @Load 0.250 kg, Temperature 100 °C |
20 % @Load 0.551 lb, Temperature 212 °F |
UL 1581 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | UL temperature rating; UL 1581 |
| Brittleness Temperature | <= -40.0 °C | <= -40.0 °F | ASTM D746 |
| Glow Wire Test | 750 °C | 1380 °F | IEC 60695-2-13 |
| 850 °C @Thickness 3.00 mm |
1560 °F @Thickness 0.118 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 9.00e+15 ohm-cm | 9.00e+15 ohm-cm | IEC 60093 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| VW-1 | Pass | UL 1581 |
Users viewing this material also viewed the following:
- Nilit FRIANYL A63 GV35 Nylon 6.6 for injection molding, 35% glass fiber reinforced
- Qualchem Danamid AFGF-50 Polyamide 66, 50% Glass Fiber
- NOVA Chemicals Novapol® PF-Y821-BP Butene LLDPE Film Resin
- Gouda Vuurvast CURON 13 SC Dense Refractory Castable
- LATI Laticonther 52/11 CP3/600 F3 PP Homopolymer
- ExxonMobil Vacmul O 3 D
- Dow Corning XIAMETER® PMCPPMX-200 200CS Silicone Fluid
- ExxonMobil 25 Mobil DTE 20 Series
Copyright © lookpolymers.com All Rights Reserved